Water-soluble industrial paint and preparation method thereof

An industrial paint, water-soluble technology, applied in the field of industrial paint, can solve problems such as paint toxicity and environmental hazards, and achieve the effect of strong paint film adhesion and good hardness

Inactive Publication Date: 2018-09-28
吉林省德嘉新型涂料(集团)有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of water-soluble industrial paint and preparation method thereof in order to solve the problem that existing traditional paint is poisonous, harmful to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-soluble industrial paint and preparation method thereof
  • Water-soluble industrial paint and preparation method thereof
  • Water-soluble industrial paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Step 1: Weigh 120g of deionized water, put it into the reaction kettle, then start the high-speed disperser, and control the speed at 350r / min;

[0033] Step 2: Weigh 4g of BYK-190 dispersant, 0.8g of Digo CN407 wetting agent, and 0.8g of BYK-024 defoamer, and put them into the reaction kettle in turn, and continue to stir at 350r / min for 15min. After stirring, successively Put in antirust pigments (1000 mesh zinc phosphate 3g and 1000 mesh barium sulfate 140g), mica powder (1000 mesh) 3g, Deqian Hemings FA179 anti-flash embroidery agent 0.5g, aluminum magnesium silicate gel solution 60g (concentration 12%), it is required to finish adding in 35 minutes, then the speed is increased to 750r / min, stirred and dispersed for 25 minutes, the speed is adjusted to 400r / min, the feed pump is started, and the slurry is driven into the next process;

[0034] Step 3: Start the feeding pump of the grinder. After the slurry overflows, start the grinder, control the speed and speed of...

Embodiment 2

[0039] Step 1: Weigh 140g of deionized water, put it into the reaction kettle, then start the high-speed disperser, and control the speed at 450r / min;

[0040] Step 2: Weigh 5g of BYK-190 dispersant, 1g of Digo CN407 wetting agent, 1g of BYK-024 defoamer, and put them into the reaction kettle in turn, and continue to stir at 450r / min for 25min. Rust pigment (1000 mesh zinc phosphate 5g and 1000 mesh barium sulfate 150g), mica powder (1000 mesh) 4g, Deqian Hemings FA179 anti-flash embroidery agent 0.6g, aluminum magnesium silicate gel solution 60g (concentration is 12 %), it is required to finish adding in 45 minutes, then the rotating speed is increased to 850r / min, stirred and dispersed for 35min, the rotating speed is adjusted to 500r / min, the feeding pump is started, and the slurry is driven into the next process;

[0041] Step 3: Start the feeding pump of the grinder. After the slurry overflows, start the grinder, control the speed and speed of 750r / min, and the main engin...

Embodiment 3

[0046] Step 1: Weigh 130g of deionized water, put it into the reaction kettle, then start the high-speed disperser, and control the speed at 400r / min;

[0047] Step 2: Weigh 4.5g of BYK-190 dispersant, 0.9g of Digo CN407 wetting agent, 0.9g of BYK-024 defoamer, put them into the reaction kettle in turn, and continue to stir at 400r / min for 20min. After stirring, Add anti-rust pigments (1000 mesh zinc phosphate 4g and 1000 mesh barium sulfate 1450g), mica powder (1000 mesh) 3.5g, Deqian Hemings FA179 anti-flicker agent 0.55g, aluminum magnesium silicate gel solution 60g (concentration is 12%), it is required to finish adding in 35-45min, then the speed is increased to 800r / min, stirred and dispersed for 30min, the speed is adjusted to 450r / min, the feed pump is started, and the slurry is driven into the next process;

[0048] Step 3: Start the feeding pump of the grinder. After the slurry overflows, start the grinder, control the speed and speed to 700r / min, and the main engine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention provides water-soluble industrial paint and a preparation method thereof, and belongs to the technical field of industrial paint. The water-soluble industrial paint uses alcohol acid modified styrene-acrylic resin as base materials; the base material is odorless and achieves an environmental-friendly effect; water level diluents are used; flash-rust inhibitors, anti-rust pigments, other coalescing agents and the like are used in a matched way; the obtained water soluble industrial paint has good hardness, anti-corrosion performance, high-temperature-resistant performance, water-resistant performance, anti-impact performance and the like; meanwhile, the industrial paint achieves the environmental-friendly effect, is odorless and harmless, and is safe for storage and transportation. Experiment results show that the hardness of the water-soluble industrial paint can reach 2H; the vulcanization resistant steam temperature can reach 150 DEG C; the paint film attaching force isstrong; under the condition of the skin temperature being 600 DEG C, the high-quality complete smearing coating can still be maintained; after being put into a baking oven with the temperature being300 DEG C for 15 hours, the paint film does not have an aging embrittlement phenomenon; the outdoor placement time can reach one year or more under the condition of not coating finishing paint; afterboiling for 15 hours in boiling water or after soaking for 14 months in tap water at room temperature, the coating does not generate bubbles and cannot fall off.

Description

technical field [0001] The invention belongs to the technical field of industrial paint, and in particular relates to a water-soluble industrial paint and a preparation method thereof. Background technique [0002] Due to the scientific design scheme, the water-soluble industrial paint has a unique formula and process that integrates the penetration type, conversion type and stable type. Scientifically take the osmotic transformation mechanism as the leading factor, use water as the dispersion medium, use multiple mechanisms such as physics and chemistry, and configure according to the chemical principles of scientific transformation, network and reflection, etc. It is a kind of green environmental protection and energy-saving material. Traditional oil-based paints are toxic, odorous, pollute the environment, and affect people's physical and mental health. Compared with traditional oil-based paints, the advantages of water-soluble industrial paints are: [0003] 1. Non-toxi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/02C09D5/08C09D7/20C09D7/61
CPCC08K2201/003C08L2201/08C09D5/024C09D5/028C09D5/084C09D5/18C09D7/20C09D125/14C08L75/04C08K13/02C08K3/28C08K3/32C08K3/30C08K3/34
Inventor 张洪力李红张云鹤孙立军
Owner 吉林省德嘉新型涂料(集团)有限公司