Nano paint, preparation method of nano paint, floor coated with nana paint and preparation method

A nano-floor technology, applied in coatings, biocide-containing paints, anti-fouling/underwater coatings, etc., can solve the problems of increasing decoration costs, easy scratches and damages, and affecting the appearance of the floor, and achieve a guaranteed anti-skid level , prevent scratches, improve the effect of anti-skid level

Inactive Publication Date: 2018-10-02
王红杰
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of people's life, people have higher requirements for the floor, but when the traditional floor is used, it is easy to scratch and damage, which affects the beauty of the floor, and also increases people's decoration costs, which in turn affects people's mood. People's quality of life, and thus cannot meet people's living needs
[0003] At present, the anti-skid level of floors on the market is generally R9, and some manufacturers have produced floor anti-skid levels up to R11, but it is far from enough for an absolutely safe environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of nano paint, it is characterized in that: described a kind of mixed PVA nano paint is prepared according to following raw material mass percentage: 50 parts of water; 1 part of dispersant; 2 parts of defoaming agent; 5 parts of ethylene glycol; 1 part; 15 parts of porous powder quartz; 10 parts of ammonium polyphosphate; 80 parts of elastic acrylic emulsion; 15 parts of nano-zinc oxide; 12 parts of nano-titanium dioxide; 5 copies of PVA.

[0022] Further, the nano paint is prepared according to the following steps:

[0023] 1) Mix water, dispersant, ethylene glycol, elastic acrylic emulsion, nano-zinc oxide, and nano-titanium dioxide evenly, heat to 50°C-55°C, and keep for at least 50 minutes;

[0024] 2) Continue to add defoamer, porous powder quartz, and ammonium polyphosphate, heat up to 65°C-67°C, and keep warm for 30min;

[0025] 3) Heat up to 70°C, add hair mask auxiliaries, thickeners, fungicides, PVA, and keep warm for 60 minutes;

[0026] 4) Adding ...

Embodiment 2

[0034] A kind of nano paint, it is characterized in that: described a kind of mixed PVA nano paint is prepared according to following raw material mass percentage: 55 parts of water; 1 part of dispersant; 2 parts of defoaming agent; 6 parts of ethylene glycol; 1 part; 16 parts of porous powder quartz; 12 parts of ammonium polyphosphate; 90 parts of elastic acrylic emulsion; 16 parts of nano-zinc oxide; 13 parts of nano-titanium dioxide; 10 copies of PVA.

[0035] Further, the nano paint is prepared according to the following steps:

[0036] 1) Mix water, dispersant, ethylene glycol, elastic acrylic emulsion, nano-zinc oxide, and nano-titanium dioxide evenly, heat to 50°C-55°C, and keep for at least 50 minutes;

[0037] 2) Continue to add defoamer, porous powder quartz, and ammonium polyphosphate, heat up to 65°C-67°C, and keep warm for 30min;

[0038] 3) Heat up to 70°C, add hair mask auxiliaries, thickeners, fungicides, PVA, and keep warm for 60 minutes;

[0039] 4) Adding...

Embodiment 3

[0047] A kind of nano paint, it is characterized in that: described a kind of mixed PVA nano paint is prepared according to following raw material mass percentage: 65 parts of water; 1.5 parts of dispersant; 2.5 parts of defoaming agent; 6 parts of ethylene glycol; PH regulator 1 part; 17 parts of porous powder quartz; 13 parts of ammonium polyphosphate; 100 parts of elastic acrylic emulsion; 18 parts of nano-zinc oxide; 14 parts of nano-titanium dioxide; 12 copies of PVA.

[0048] Further, the nano paint is prepared according to the following steps:

[0049] 1) Mix water, dispersant, ethylene glycol, elastic acrylic emulsion, nano-zinc oxide, and nano-titanium dioxide evenly, heat to 50°C-55°C, and keep for at least 50 minutes;

[0050] 2) Continue to add defoamer, porous powder quartz, and ammonium polyphosphate, heat up to 65°C-67°C, and keep warm for 30min;

[0051] 3) Heat up to 70°C, add hair mask auxiliaries, thickeners, fungicides, PVA, and keep warm for 60 minutes; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses nano paint, a preparation method of the nano paint, a floor coated with the nano paint and a preparation method, in particular to a composition and manufacturing method of thenano paint and the preparation method of the anti-skid floor coated with the nano paint. According to the preparation method of the floor, the floor is coated with the nano paint for primary solidification, and is then coated with a layer of nano paint for secondary solidification, so that the quality of the floor is ensured, the situation can be prevented that the appearance of the floor is influenced when the floor is scratched, the anti-skid level of the floor is increased, and the floor is in a state with a high anti-skid level; in addition, the nano paint is stored in a chamber to be protected from heat and sunlight radiation, and the situation can be prevented that the service life of the nano paint is influenced when the nano paint changes during exposure to the sun, and the anti-skid level of the floor is ensured.

Description

technical field [0001] The invention relates to the technical field of floors, in particular to a floor coated with nano-varnish and a preparation method thereof. Background technique [0002] With the improvement of people's life, people have higher requirements for the floor, but when the traditional floor is used, it is easy to scratch and damage, which affects the beauty of the floor, and also increases people's decoration costs, which in turn affects people's mood. People's quality of life, and thus can not meet people's living needs. [0003] At present, the anti-skid level of floors on the market is generally R9, and some manufacturers have produced floor anti-skid levels up to R11, but it is far from enough for an absolutely safe environment. [0004] Therefore, this area needs a kind of antiskid floor that can improve floor antiskid level to R12. Contents of the invention [0005] The object of the present invention is to provide a kind of nano paint and its pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D5/14C09D7/61B05D7/00B05D7/24
CPCB05D7/24B05D7/586B05D2502/00B05D2503/00B05D2601/24C08K2201/011C09D5/14C09D133/00C08L29/04C08K13/04C08K7/26C08K2003/323C08K2003/2296C08K2003/2241B05D2420/01B05D2420/02B05D2420/03
Inventor 王红杰
Owner 王红杰