Insulating coating for storage battery of battery car

A heat-insulating coating and storage battery technology, which is applied in the direction of anti-corrosion coatings, fire-proof coatings, polyester coatings, etc., can solve the problem of affecting the working stability of storage battery products, the service life of operation safety, the inability to meet the heat dissipation requirements of high-power battery products, and battery zero. Unstable component power supply and other issues, to achieve the effect of low cost, simple and easy to use process, and fast heat dissipation

Inactive Publication Date: 2018-10-12
邵雷
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the development of the field of battery vehicles, battery products are developing towards miniaturization, light weight, compactness and high efficiency. Therefore, high-power battery products are developing rapidly, and the resulting large amount of heat will be directly Affect the working stability, operation safety and service life of battery products. Conventional cooling methods can no longer meet the heat dissipation requirements of high-power battery products. Due to temperature changes during work, the power supply of battery components will also be unstable, causing certain hazards. Therefore, it is necessary to increase the heat dissipation rate of battery products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A thermal insulation paint for storage battery of battery car, which consists of the following components in parts by weight: 50 parts of modified salicylic acid resin, 30 parts of basic epoxy resin, 20 parts of water glass, 10 parts of nano-carbon fiber, and 8 parts of silica airgel , 5 parts of ceramic fiber, 8 parts of corundum, 7 parts of curing agent, 8 parts of acrylic emulsion, 4 parts of silane compound, 7 parts of natural filling stone powder, 8 parts of additives, 10 parts of kaolin, 4 parts of nano-zinc oxide and anhydrous sulfuric acid Magnesium 3 parts.

Embodiment 2

[0014] A thermal insulation coating for storage battery of battery car, which consists of the following components in parts by weight: 70 parts of modified salicylic acid resin, 55 parts of basic epoxy resin, 30 parts of water glass, 15 parts of nano-carbon fiber, and 12 parts of silica airgel , 12 parts of ceramic fiber, 13 parts of corundum, 11 parts of curing agent, 12 parts of acrylic emulsion, 10 parts of silane compound, 10 parts of natural filling stone powder, 15 parts of additives, 20 parts of kaolin, 10 parts of nano zinc oxide and anhydrous sulfuric acid Magnesium 8 parts.

Embodiment 3

[0016] A thermal insulation paint for storage battery of battery car, which consists of the following components in parts by weight: 62 parts of modified salicylic acid resin, 44 parts of basic epoxy resin, 26 parts of water glass, 13 parts of nano-carbon fiber, and 9 parts of silicon dioxide airgel , 7 parts of ceramic fiber, 10 parts of corundum, 10 parts of curing agent, 9 parts of acrylic emulsion, 6 parts of silane compound, 8 parts of natural filling stone powder, 11 parts of additives, 17 parts of kaolin, 6 parts of nano-zinc oxide and anhydrous sulfuric acid Magnesium 5 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an insulating coating for a storage battery of a battery car. The insulating coating is prepared from, by weight, 50-70 parts of modified salicylic acid resin, 30-55 parts of basic epoxy resin, 20-30 parts of water glass, 10-15 parts of nanometer carbon fibers, 8-12 parts of silicon dioxide aerosol, 5-12 parts of ceramic fibers, 8-13 parts of carborundum, 7-11 parts of curing agent, 8-12 parts of acrylic emulsion, 4-10 parts of silane compound, 7-10 parts of natural filling stone powder, 8-15 parts of auxiliary agent, 10-20 parts of kaolin, 4-10 parts of nanometer zincoxide and 3-8 parts of anhydrous magnesium sulfate. By means of the insulating coating, heat with the increased internal temperature of the storage battery due to work of the storage battery can be effectively guided to a shell, and the insulating coating is high in cooling speed, poisonless and innocuous; all performance indexes meet the requirement for environmental protection, and the insulating coating is easy to use in the using process, is cured at the normal temperature, further has the performance like high temperature resistance, low temperature resistance and chemical corrosion resistance, and has a wide application field and low cost.

Description

technical field [0001] The invention relates to the field of development and utilization of battery cars, in particular to a heat-insulating coating for batteries of battery cars. Background technique [0002] In the development of the field of battery vehicles, battery products are developing towards miniaturization, light weight, compactness and high efficiency. Therefore, high-power battery products are developing rapidly, and the resulting large amount of heat will be directly Affect the working stability, operation safety and service life of battery products. Conventional cooling methods can no longer meet the heat dissipation requirements of high-power battery products. Due to temperature changes during work, the power supply of battery components will also be unstable, causing certain hazards. Therefore, it is necessary to increase the heat dissipation rate of battery products. Therefore, there is a need for a thermal insulation coating with reliable performance, hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/04C09D163/00C09D133/00C09D7/61C09D5/08
CPCC09D167/04C08K2003/2296C08K2003/3063C08K2201/011C08L2201/08C08L2205/03C09D5/08C09D5/18C09D7/61C09D7/70C08L63/00C08L33/00C08K13/04C08K3/046C08K3/36C08K7/04C08K3/346C08K3/22C08K3/30
Inventor 邵雷
Owner 邵雷
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products