Fine chemical sewage deodorant and preparation method thereof
A fine chemical and deodorant technology, applied in the field of fine chemical sewage deodorant and its preparation, can solve the problems of insufficient deodorization effect, low deodorization efficiency, poor deodorization effect, etc., and achieve excellent adsorption capacity , The effect of long removal time and high deodorization rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] In this example, the fine chemical sewage deodorant is made of the following raw materials in parts by weight: 50 parts of modified zeolite, 1 part of lactic acid bacteria, 1 part of microbial complex bacteria, 8 parts of spices, 10 parts of calcium persulfate, 10 parts of hydrogen peroxide 15 parts of mint extract, 15 parts of tea extract, 15 parts of wild Gastrodia elata extract, 3 parts of polyethylene glycol, 3 parts of hydroxymethyl cellulose, 4 parts of disinfectant;
[0028] Wherein, the modification method of the modified zeolite is: preparing a cetyltrimethylammonium bromide solution with a mass concentration of 1%, and mixing the natural zeolite and the prepared cetyltrimethylammonium bromide solution with 3g: 19mL mixed, at 27°C, shake reaction for 4h, centrifuge at 3500r / min for 10min, collect the precipitate, wash with distilled water, centrifuge and wash 4 times under the same conditions, until no detectable in the supernatant after washing Hexadecyltrimet...
Embodiment 2
[0035] In this example, the fine chemical sewage deodorant is made of the following raw materials in parts by weight: 80 parts of modified zeolite, 2 parts of lactic acid bacteria, 3 parts of microbial complex bacteria, 17 parts of spices, 18 parts of calcium persulfate, and 18 parts of hydrogen peroxide. 25 parts of mint extract, 25 parts of tea extract, 25 parts of wild gastrodia elata extract, 10 parts of polyethylene glycol, 7 parts of hydroxymethyl cellulose, 8 parts of disinfectant;
[0036]Wherein, the modification method of the modified zeolite is: preparing a cetyltrimethylammonium bromide solution with a mass concentration of 2%, mixing the natural zeolite with the prepared cetyltrimethylammonium bromide solution 3g: 19mL mixed, at 27°C, shaking reaction for 5.5h, then centrifuge at 6000r / min for 16min, collect the precipitate, rinse with distilled water, centrifuge and wash 6 times under the same conditions, until no detection is found in the supernatant after washin...
Embodiment 3
[0043] In this example, the fine chemical sewage deodorant is made of the following raw materials in parts by weight: 65 parts of modified zeolite, 1.5 parts of lactic acid bacteria, 2 parts of microbial composite bacteria, 12 parts of spices, 14 parts of calcium persulfate, 14 parts of hydrogen peroxide 20 parts of mint extract, 20 parts of tea extract, 20 parts of wild Gastrodia elata extract, 6.5 parts of polyethylene glycol, 5 parts of hydroxymethyl cellulose, 6 parts of disinfectant;
[0044] Wherein, the modification method of the modified zeolite is: preparing a cetyltrimethylammonium bromide solution with a mass concentration of 1.5%, mixing the natural zeolite and the prepared cetyltrimethylammonium bromide solution with 3g: 19mL mixed, at 27°C, after oscillating for 4.8h, centrifuge at 4700r / min for 13min, collect the precipitate, wash with distilled water, centrifuge and wash 5 times under the same conditions, until no detection is found in the supernatant after wash...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com