Environmentally-friendly water-based gravure ink and preparation method thereof
A gravure ink, water-based technology, applied in the field of environmentally friendly water-based gravure ink and its preparation, to achieve the effects of convenient transportation and storage, easy popularization and application, and low preparation cost
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] The environment-friendly water-based gravure ink of the present embodiment comprises the following raw material components by weight percentage: 84.6% of main film-forming substances, 0.3% of pigments, 15% of fillers, and 0.1% of lubricants;
[0023] The main film-forming substance is an acrylic acid prepolymer;
[0024] The pigment is light-fast blue powder and light-fast yellow powder mixed in a ratio of 2:1 by weight;
[0025] Described filling material is that titanium dioxide, colloidal calcium carbonate are mixed using in the ratio of 12:3 by weight percentage;
[0026] The lubricant is polyethylene wax.
[0027] The preparation method of the environmental protection water-based gravure printing ink described in the present embodiment, comprises the steps:
[0028] (1) Prepare a clean feeding cylinder, place it in the disperser and fix the cylinder body;
[0029] (2) Add 846g of acrylic acid prepolymer into the feeding tank, and add 1g of lubricant while stirri...
Embodiment 2
[0035] The environment-friendly water-based gravure ink of the present embodiment comprises the following raw material components by weight percentage: 85.0% of main film-forming substances, 0.6% of pigments, 14% of fillers, and 0.4% of lubricants;
[0036] The main film-forming substance is an acrylic acid prepolymer;
[0037] The pigment is light-fast blue powder and light-fast yellow powder mixed in a ratio of 1:1 by weight;
[0038] Described filler is that titanium dioxide, talcum powder are used in the ratio of 2:5 by weight percentage;
[0039] The lubricant is polyethylene wax.
[0040] The preparation method of the environmental protection water-based gravure printing ink described in the present embodiment, comprises the steps:
[0041] (1) Prepare a clean feeding cylinder, place it in the disperser and fix the cylinder body;
[0042] (2) Add 850g of acrylic acid prepolymer into the feeding tank, and add 4g of lubricant while stirring to make it fully mixed. The s...
Embodiment 3
[0048] The environment-friendly water-based gravure ink of the present embodiment comprises the following raw material components by weight percentage: 85.9% of main film-forming substances, 0.6% of pigments, 13% of fillers, and 0.5% of lubricants;
[0049] The main film-forming substance is an acrylic acid prepolymer;
[0050] The pigment is a light-fast blue powder and a light-fast yellow powder mixed in a ratio of 2:1 by weight;
[0051] Described filler is colloidal calcium carbonate;
[0052] The lubricant is polyethylene wax.
[0053] The preparation method of the environmental protection water-based gravure printing ink described in the present embodiment, comprises the steps:
[0054] (1) Prepare a clean feeding cylinder, place it in the disperser and fix the cylinder body;
[0055] (2) Add 859g of acrylic acid prepolymer into the feeding tank, and add 5g of lubricant while stirring to make it fully mixed. The stirring speed is 1000r / min, and the stirring time is 25...
PUM
Property | Measurement | Unit |
---|---|---|
friction coefficient | aaaaa | aaaaa |
friction coefficient | aaaaa | aaaaa |
gloss | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com