Wear-resisting tile glaze

A technology for glazes and ceramic tiles, applied in the field of wear-resistant ceramic tile glazes, can solve the problems of affecting the use and appearance of ceramic tiles, shortening the service life of ceramic tiles, and leaving scratches on the surface of ceramic tiles, so as to improve wear resistance and practicability, improve Quality and grade, glaze fine and smooth effect

Inactive Publication Date: 2018-12-07
安徽省德邦瓷业有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of people's quality of life and the change of aesthetic point of view, the use of ceramic tiles is also increasing. However, ceramic tiles are used for laying the ground. Naturally, the surface of ceramic tiles is often worn during daily use and scrubbing. Scratches are left on the surface of the tiles, which affect the use and appearance of the tiles, and also cause the tiles to become more and more prone to corrosion and damage, which seriously shortens the service life of the tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A wear-resistant tile glaze, made of the following raw materials in parts by weight: silicon dioxide 41, dolomite 35, plagioclase 15, modified muscovite 11, olivine 10, magnesium oxide 6.3, lutetium oxide 5.6, titanium dioxide 4.2, zirconia 3.7, boron oxide 2.6.

[0020] For the modified muscovite, pulverize the muscovite to 80~mesh, then evenly add a sodium silicate solution with a mass percentage concentration of 40% of the muscovite weight and a concentration of 3%, and let it stand at -46°C for 10 hours. After taking it out, use Heating at a rate of 3°C / min to 970°C and holding for 30 minutes to obtain modified muscovite.

[0021] A preparation method of a wear-resistant tile glaze, comprising the following steps:

[0022] (1) Crush dolomite to 140 mesh, heat to 460°C at a speed of 2°C / min, keep warm for 10 minutes, cool down to 170°C naturally, add 3% salt solution by mass percentage, mix well, and heat at 4°C Heating at a speed of 1 / min to 620°C and holding for ...

Embodiment 2

[0030] A wear-resistant tile glaze, made of the following raw materials in parts by weight: silicon dioxide 42, dolomite 36, plagioclase 16, modified muscovite 12, olivine 11, magnesium oxide 6.4, lutetium oxide 5.7, titanium dioxide 4.3, zirconia 3.8, boron oxide 2.7.

[0031] For the modified muscovite, the muscovite was crushed to 90 mesh, and then evenly added a sodium silicate solution with a mass percentage concentration of 43% of the muscovite weight and a concentration of 3.5%. Heating at a speed of ℃ / min to 990 ℃, keeping it warm for 35 minutes, to obtain modified muscovite.

[0032] A preparation method of a wear-resistant tile glaze, comprising the following steps:

[0033] (1) Crush dolomite to 160 mesh, heat to 490°C at a speed of 2.5°C / min, keep warm for 13 minutes, cool down to 185°C naturally, add 4% salt solution by mass percentage, mix well, and heat at 4.5°C Heating at a speed of 1 / min to 640°C and holding for 35 minutes to obtain modified dolomite;

[00...

Embodiment 3

[0041] A wear-resistant tile glaze, made of the following raw materials in parts by weight: silicon dioxide 43, dolomite 37, plagioclase 17, modified muscovite 13, olivine 12, magnesium oxide 6.5, lutetium oxide 5.8, titanium dioxide 4.4, zirconia 3.9, boron oxide 2.8.

[0042] For the modified muscovite, pulverize the muscovite to 100 meshes, then evenly add a sodium silicate solution with a mass percent concentration of 4% of the weight of the muscovite, and let it stand at -48°C for 12 hours. The speed of ℃ / min is heated to 1020 ℃, and the temperature is kept for 40 minutes to obtain modified muscovite.

[0043] A preparation method of a wear-resistant tile glaze, comprising the following steps:

[0044] (1) Crush dolomite to 200 mesh, heat to 520°C at a speed of 3°C / min, keep warm for 15 minutes, cool down to 200°C naturally, add 5% salt solution by mass percentage, mix well, and heat at 5°C Heating to 660°C at a speed of 1 / min and holding for 40 minutes to obtain modifi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention mainly relates to the technical field of ceramic glaze processing and discloses a wear-resisting tile glaze. The wear-resisting tile glaze is prepared from the following raw materials: 41-43 parts of silicon dioxide, 35-37 parts of dolomite, 15-17 parts of anorthose, 11-13 parts of modified white mica, 10-12 parts of olivine, 6.3-6.5 parts of magnesium oxide, 5.6-5.8 parts of lutecia, 4.2-4.4 parts of titanium dioxide, 3.7-3.9 parts of zirconium oxide and 2.6-2.8 parts of boron oxide. The wear-resisting tile glaze provided by the invention is smooth and fine, is high in wearing resistance, is capable of keeping the tile surface bright and fine, is anti-corrosion and is capable of promoting the quality and grade of tiles. The dolomite is firstly smashed, heated and calcined and then is added into a salt solution and is heated and calcined again so as to modify the dolomite, promote the fineness and smoothness of the dolomite, guarantee the smooth flowing during the glazingprocess and keep the tile surface smooth and flawless.

Description

technical field [0001] The invention mainly relates to the technical field of ceramic glaze processing, in particular to a wear-resistant tile glaze. Background technique [0002] With the improvement of people's quality of life and the change of aesthetic point of view, the use of ceramic tiles is also increasing. However, ceramic tiles are used for laying the ground. Naturally, the surface of ceramic tiles is often worn during daily use and scrubbing. Scratches are left on the surface of the tiles, which will affect the use and appearance of the tiles, and will also cause the tiles to become more and more prone to corrosion and damage, seriously shortening the service life of the tiles. Contents of the invention [0003] In order to remedy the defects of the prior art, the object of the present invention is to provide a wear-resistant tile glaze. [0004] A wear-resistant ceramic tile glaze, made of the following raw materials in parts by weight: silicon dioxide 41-43, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C03C1/02
CPCC03C1/026C03C8/00
Inventor 姚永祥
Owner 安徽省德邦瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com