Combination of inorganic nonmetal and plastic and preparation method thereof
An inorganic non-metal and combination technology, applied in the field of combination, can solve the problems of affecting the appearance of products, gaps in the joint, and low joint strength.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0051] In another aspect of this embodiment, a method for preparing a conjugate is also provided, which is applied to the above conjugate, see image 3 , the method includes the following steps:
[0052] S1. An inorganic non-metallic part is provided, the inorganic non-metallic part has a first surface;
[0053] Wherein, the material of the inorganic non-metal part is olivine, spinel, sapphire, glass or ceramics. Before the first surface treatment of the inorganic non-metallic part, it also includes: surface pretreatment, the surface pretreatment is used to remove the grease on the first surface. In the surface pretreatment process, the first surface of the ceramic substrate can be treated with a degreasing agent or a degreasing agent for a certain period of time, such as: 300s; finally put it into deionized water for cleaning and completely dry.
[0054] S2. Prepare a precursor layer on the first surface, and heat-treat the precursor layer to obtain a multi-element oxide la...
Embodiment 1
[0065] An inorganic non-metallic part is provided, the inorganic non-metallic part is a zirconia ceramic sheet, the zirconia ceramic sheet has a first surface, and the first surface is used for combining with plastic to form a combined body.
[0066] First, the first surface is pretreated with a degreaser or a degreasing agent to remove grease on the first surface.
[0067] In the surface pretreatment process, the first surface of the ceramic substrate can be treated with a degreasing agent or a degreasing agent for a certain period of time, such as: 300s; finally put it into deionized water for cleaning and completely dry.
[0068] Next, prepare the film-forming slurry.
[0069] Add 50 parts of n-butanol, 5 parts of diethanolamine, 50 parts of tetrabutyl titanate, and 200 parts of zirconium n-propoxide into the beaker, and mix them evenly by stirring; weigh 20 parts of nano-titanium dioxide Microspheres, 50 parts of nano-silica microspheres, put 2 parts of potassium hydroxid...
Embodiment 2
[0081] An inorganic non-metallic part is provided, the inorganic non-metallic part is a glass sheet, the glass sheet has a first surface, and the first surface is used for combining with plastic to form a combined body.
[0082] First, the first surface is pretreated with a degreaser or a degreasing agent to remove grease on the first surface.
[0083] In the surface pretreatment process, the first surface of the ceramic substrate can be treated with a degreasing agent or a degreasing agent for a certain period of time, such as: 300s; finally put it into deionized water for cleaning and completely dry.
[0084] Next, prepare the film-forming slurry.
[0085] Add 50 parts of n-butanol, 5 parts of diethanolamine, 50 parts of tetrabutyl titanate, and 200 parts of zirconium n-propoxide into the beaker, and mix them evenly by stirring; weigh 20 parts of nanometer two Silica microspheres, 50 parts of nano-silica microspheres, put into a ball mill jar, then add 50 parts of n-butanol...
PUM
| Property | Measurement | Unit |
|---|---|---|