Method for reducing density of colored foam glass
A technology of foam glass and density, which is applied in glass molding, glass manufacturing equipment, manufacturing tools, etc., can solve the problems of reducing the density of colored foam glass, unsightly cost, etc., and achieves low raw material prices, light weight per unit volume, and wide application range wide effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0020] A method for reducing the density of colored foam glass comprising an essential component and at least one coloring component: the essential component comprising: 74 mol % SiO 2 ; 5 mol% CaO; 18 mol% Al 2 o 3 ; 1 mol% Na 2 O; the at least one coloring component comprises: 1 mol % of MnO 2 , 0.5 mol% Cu 2 O, 0.5 mol% Cr 2 o 3 .
[0021] Described reduction colored cellular glass density obtains as follows:
[0022] 1) Preparation of premix: 100 parts of aluminosilicate glass powder with a particle size of 500 mesh or more, 10 parts of calcium carbonate, alkali metal oxide Na 2 O 2 parts, colorant (MnO 2 , Cu 2 O and Cr 2 o 3 ) 2 parts were mixed, an appropriate amount of water was added, the ball-to-material ratio was 50:1, the rotating speed was 100-300rpm, and the ball milled for 30min, the said parts were parts by weight;
[0023] 2) Calculated on the basis of 100 parts of the prepared premix, add 15 parts of phenolic resin and mix evenly, place it in the ...
Embodiment 2
[0027] A method for reducing the density of colored foam glass comprising an essential component and at least one coloring component: the essential component comprising: 70 mol % SiO 2 ; 6 mol% CaO; 20 mol% Al 2 o 3 ; 2 mol% Na 2 O; the at least one coloring component comprises: 1 mol % of MnO 2 , 0.5 mol% Cu 2 O, 0.5 mol% CoO.
[0028] Described reduction colored cellular glass density obtains as follows:
[0029] 1) Preparation of premix: 100 parts of aluminosilicate glass powder with a particle size of 500 mesh or more, 8 parts of calcium carbonate, alkali metal oxide Na 2 O 4 parts, colorant (MnO 2 , Cu 2 O and CoO) are mixed in 2 parts, an appropriate amount of water is added, the ball-to-material ratio is 70:1, the rotation speed is 100-300rpm, and the ball mill is 30min, and the parts are parts by weight;
[0030] 2) Calculated on the basis of 100 parts of the prepared premix, add 25 parts of phenolic resin and mix evenly, place it in the mold for pre-pressuriza...
Embodiment 3
[0034] A method for reducing the density of colored foam glass comprising an essential component and at least one coloring component: the essential component comprising: 70 mol % SiO 2 ; 6 mol% CaO; 20 mol% Al 2 o 3 ; 2 mol% Na 2 O; the at least one coloring component comprises: 1 mol % of MnO 2 , 1 mol% CoO.
[0035] Described reduction colored cellular glass density obtains as follows:
[0036] 1) Preparation of premix: 100 parts of aluminosilicate glass powder with a particle size of 500 mesh or more, 8 parts of calcium carbonate, alkali metal oxide Na 2 O4 parts, colorant (MnO 2 Mix with 2 parts of CoO), add an appropriate amount of water, the ball-to-material ratio is 70:1, the rotation speed is 100-300rpm, and the ball mill is 30min, and the parts are parts by weight;
[0037] 2) Calculated on the basis of 100 parts of the prepared premix, add 15 parts of phenolic resin and mix evenly, place it in the mold for pre-pressurization to form a preform, and the pressuriz...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com