Method for judging surface chromium metal content of chromium-plated plate

A surface metal and determination method technology, which is applied in the direction of measuring devices, material analysis through electromagnetic means, instruments, etc., can solve the problems of not being able to measure the level of chrome plating on the surface, polluting the environment, and cumbersome operations, etc., to achieve Measuring the effect of convenience and quickness

Active Publication Date: 2018-12-18
武汉钢铁有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method can obtain the content of chromium plating on the surface of the chrome-plated plate, the operation is cumbersome and time-consuming. The method involves hexavalent chromium, which will pollute the environment, and both sides of the steel plate participate in the electrolytic reaction. The final test result is the amount of chromium plating on both sides of the sample. The average value of chromium plating cannot be used to measure the level of chromium plating in different areas on the same sample surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for judging surface chromium metal content of chromium-plated plate
  • Method for judging surface chromium metal content of chromium-plated plate
  • Method for judging surface chromium metal content of chromium-plated plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Judgment of the amount of chrome plating on the front and back of the chrome-plated plate

[0046] Cut the chrome-plated plate into 12cm-long and 5cm-wide chrome-plated plate samples, soak the chrome-plated plate sample in 100mL 90℃ 300g / L NaOH solution for 20min, take out the chrome-plated plate sample, rinse it three times, dry it, and remove the chrome-plated plate Chromium oxide layer on the surface of the sample.

[0047] The two sides of the chrome-plated plate sample are respectively recorded as a-side and b-side, and the jump potential ΔE of the chrome-plated plate in the range of 5cm×5cm is measured on both sides. Surface a starts from the bottom of the chrome-plated plate sample, and takes the range of 5cm in length and 5cm in width as the area to be measured. The surface of the chrome-plated plate sample is coated with silicone rubber within the range of length greater than 5cm and less than 10cm from the bottom, and sealed. Among them, there is a distance o...

Embodiment 2

[0052] The determination of the amount of chrome plating in different areas on the same surface of the chrome-plated plate.

[0053] Cut the chrome-plated plate into 7cm×5cm chrome-plated plate samples, soak the chrome-plated plate sample in 100mL 90℃300g / LNaOH solution for 20min, take out the chrome-plated plate sample, rinse it three times and dry it, then remove the chrome-plated plate sample Surface chromium oxide layer.

[0054] In the 2cm area from the top of the chrome-plated plate sample, no silicone rubber is used for conductivity. Take an area of ​​1cm×1cm from the top, middle and bottom of the board for testing, and seal other parts with silicone rubber, see image 3 , where 1, 2, and 3 are the areas of the sample to be tested, and 4 is the connection between the electrolytic clamp and the sample. The electrolysis reaction proceeds sequentially from the bottom to the top. Specifically:

[0055] 1) Soak the area to be tested at the bottom of the chrome-plated pla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for judging the surface chromium metal content of a chromium-plated plate. The method comprises the following steps that: firstly, selecting a chromium-plated plate specimen; removing a chromium oxidation layer on the surface of the chromium-plated plate specimen; then, taking the chromium-plated plate specimen as an anode and a platinum wire as a cathode, carryingout constant current electrolysis in electrolyte sodium carbonate solution, recording a voltage value, marking voltage at the beginning as E1, along with electrolysis reaction, raising the voltage, subsequently, sharply increasing the voltage, when the voltage hardly changes, finishing electrolysis, finishing electrolyzing all surface metal chromium layers of the chromium-plated plate specimen, and recording voltage E2; and finally, calculating a voltage difference [Delta]E=E2-E1 before and after electrolysis to realize the semi-quantitative analysis of a chromium-plated amount of the surfaceof the chromium-plated plate. By use of the device, the measurement of the surface chromium-plated amount can be carried out on any position of the surface of the chromium-plated plate, and the distribution evenness of the surface metal chromium of the chromium-plated plate can be accurately judged.

Description

technical field [0001] The invention relates to a judging method, in particular to a judging method for the level of metal chromium content on the surface of a chrome-plated plate. Background technique [0002] Chromium-plated steel, also known as tin-free steel, is a new type of can-making material developed under the condition of reduced metal tin resources. It is a kind of electrolytic chromate treatment on the surface of the steel plate to deposit a layer of metallic chromium and chromium hydrated oxide on the surface of the steel plate. Compared with tinplate, its processing formability and mechanical strength are roughly the same as those of tinplate, while chrome plate products have the characteristics of low cost, strong adhesion, good high temperature resistance, strong sulfur resistance, etc., and are widely used in Crown caps, four-spin caps, etc. [0003] The existing chrome-plated surface coating mainly contains metal chromium layer (50~100mg / m 2 ) and chromi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): G01N27/416
CPCG01N27/4161
Inventor 李江文郎丰军黄先球程鹏彭浩庞涛黄菲马颖宋建红
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com