Light cement-based porous material and preparation method thereof

A technology for porous materials and cement, applied in the field of lightweight cement-based porous materials and their preparation, can solve problems such as insufficient compressive strength, and achieve the effects of reducing cement consumption, enhancing crack resistance, and improving durability

Inactive Publication Date: 2019-01-04
SOUTHEAST UNIV
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the compressive strength of the existing cement-based porous materials cannot meet the requirements, on the one hand, the present inv

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] In order to solve the problem that the compressive strength of the existing cement-based porous materials cannot meet the requirements, the present invention provides a lightweight cement-based porous material. The lightweight cement-based porous material is calculated in parts by mass and consists of the following components composition:

[0023] 185~280 parts of cement, 20~70 parts of fly ash, 5~14 parts of silica fume, 8.3~16.8 parts of chemical foaming agent, 1~2 parts of water reducing agent, 0.3~0.45 parts of foam stabilizer, fiber 1.85~8.40 Parts, 0.5 to 2.0 parts of water repellent, 102 to 168 parts of water.

[0024] Preferably, the cement in the present invention is P.II 52.5 Portland cement.

[0025] Preferably, the fly ash in the present invention has a CaO content of less than 10% and a surface area of ​​350-360m 2 / kg of low calcium ash.

[0026] Preferably, the average particle size of the silica fume in the present invention is 0.1 um, and the...

Example Embodiment

[0033] Example 2

[0034] This embodiment provides a preparation method of the lightweight cement-based porous material of the present invention, and the preparation method includes:

[0035] Step 1. In terms of parts by mass, 185~280 parts of cement, 20~70 parts of fly ash, 5~14 parts of silica fume, 8.3~16.8 parts of chemical foaming agent, 1~2 parts of water reducing agent, foam stabilizer Weigh 0.3~0.45 parts of agent, 1.85~8.40 parts of fiber, 0.5~2.0 parts of water repellent, 102~168 parts of water, and the temperature of water is 30~350℃;

[0036] Step 2. Mix the cement, fly ash, silica fume, water reducing agent, foam stabilizer, fiber and water repellent weighed in step 1 and mix and stir evenly, then add the water weighed in step 1 and stir evenly , Get the slurry;

[0037] Step 3. Add the chemical foaming agent weighed in step 1 to the slurry obtained in step 2, stir evenly, pour into the mold, and foam after standing to form a test block with a height of 35-40 mm. The tes...

Example Embodiment

[0038] Example 3

[0039] This embodiment provides a lightweight cement-based porous material. The lightweight cement-based porous material consists of the following components in parts by mass:

[0040] 185 parts of cement, 20 parts of fly ash, 5 parts of silica fume, 8.3 parts of chemical foaming agent, 1 part of water reducing agent, 0.3 part of foam stabilizer, 1.85 parts of fiber, 0.5 part of water repellent, 102 parts of water.

[0041] Preparation Process:

[0042] Step 1. In terms of parts by mass, 185 parts of cement, 20 parts of fly ash, 5 parts of silica fume, 8.3 parts of chemical foaming agent, 1 part of water reducing agent, 0.3 part of foam stabilizer, 1.85 parts of fiber, water-repellent Weigh 0.5 parts of reagent and 102 parts of water, the temperature of the water is 30℃;

[0043] Step 2. Mix the cement, fly ash, silica fume, water reducing agent, foam stabilizer, fiber and water repellent weighed in step 1 and mix and stir evenly, then add the water weighed in step 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a light cement-based porous material and a preparation method thereof, and belongs to the technical field of building materials. The light cement-based porous material comprises, by weight, 185-280 parts of cement, 20-70 parts of coal ash, 5-14 parts of silica fume, 8.3-16.8 parts of chemical foaming agents, 1-2 parts of water reducing agents, 0.3-0.45 part of foam stabilizers, 1.85-8.40 parts of fibers, 0.5-2.0 parts of water repellents and 102-168 parts of water. The compressive strength of the light cement-based porous material formed by matching is higher than or equal to 0.40MPa, the tensile strength of the light cement-based porous material is higher than or equal to 0.13MPa, by adding the coal ash and the silica fume, cement content can be decreased, cracksgenerated by stress of the light cement-based porous material can be eliminated, the later strength of the light cement-based porous material can be improved, the fibers are added into slurry to enhance the crack resistance of the light cement-based porous material, pores and filling capillary channels in the light cement-based porous material can be decreased by the water repellents, the water absorptivity or the water permeability of the light cement-based porous material under hydrostatic pressure are reduced, permeability resistance is improved, and durability is enhanced.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a lightweight cement-based porous material and a preparation method thereof. Background technique [0002] Thermal insulation materials refer to materials that can prevent heat loss inside a building or isolate external heat from entering. In the field of construction, thermal insulation materials are mainly responsible for the ability of the enclosure structure to maintain an appropriate indoor temperature in winter; thermal insulation materials are mainly responsible for the ability of the enclosure structure to isolate the impact of heat radiation and outdoor high temperature in summer, so as to keep the indoor temperature at an appropriate temperature. [0003] There are many types of thermal insulation materials, and there are many different classification methods. According to the material of thermal insulation materials, they can be divided into organic thermal ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B38/02C04B111/40
CPCC04B28/04C04B2111/40C04B2201/50C04B18/08C04B18/146C04B22/068C04B2103/302C04B24/20C04B22/085C04B16/0633C04B22/124C04B22/06C04B38/02
Inventor 佘伟张云升杨永敢郭盼盼
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap