Diatom ooze coating easy to clean and dry
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A diatom mud coating, easy-to-clean technology, applied in the field of decorative coatings, can solve problems such as shedding, easy staining of walls, and short service life
Inactive Publication Date: 2019-01-04
东莞市爱乐居环保科技有限公司
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The existing diatom mud paint has many raw materials, and the walls made of it are also easy to stain or even fall off, easy to powder, not resistant to scrubbing, and have a short service life
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0035] A kind of easy-to-clean and easy-to-dry diatom mud coating of the present embodiment comprises the following components in parts by weight: 25 parts of diatom mud, 5 parts of calciumhydroxide, 8 parts of white cement, the copolymer of ethylene / vinyl acetate 3 1 part, 1 part of nano titanium dioxide powder, 1 part of sodiumchloride, 5 parts of nitrocellulose, 10 parts of drier, 3 parts of bamboo charcoal, 6 parts of alkali lignin, 3 parts of modified polyesterfiber, and 25 parts of water.
[0036] Among them, the weight content of diatomite in diatom mud is 65%, the particle size of diatomite is 400 mesh, the particle size of nano-titanium dioxide powder is 2000 mesh, and the drier includes zirconium isooctanoate, manganese isooctanoate and isooctanoate Copper, its weight ratio is 1:0.1:0.6.
[0037] The preparation method of the diatom mud coating of the present embodiment may further comprise the steps:
[0038] 1) Weighing the components of the corresponding parts...
[0044] Among them, the weight content of diatomite in diatom mud is 85%, the particle size of diatomite is 700 mesh, the particle size of nano-titanium dioxide powder is 2600 mesh, and the drier includes zirconium isooctanoate, manganese isooctanoate and isooctanoate Copper, its weight ratio is 1:0.15:0.7.
[0045] The preparation method of the diatom ooze coating of the present embodiment is the same as embodiment 1.
Embodiment 3
[0047] An easy-to-clean and easy-to-dry diatom mud coating of the present embodiment comprises the following components in parts by weight: 35 parts of diatom mud, 5 parts of calcium hydroxide, 3 parts of white cement, ethylene / vinyl acetatecopolymer 1 3 parts, nano titanium dioxide powder 3 parts, sodium chloride 2 parts, nitrocellulose 5 parts, drier 5 parts, bamboo charcoal 3 parts, alkali lignin 8 parts, modified polyester fiber 5 parts, water 30 parts.
[0048] Among them, the weight content of diatomite in diatom mud is 70%, the particle size of diatomite is 800 mesh, the particle size of nano-titanium dioxide powder is 1000 mesh, and the drier includes zirconium isooctanoate, manganese isooctanoate and isooctanoate Copper, its weight ratio is 1:0.2:0.6.
[0049] The preparation method of the diatom ooze coating of the present embodiment is the same as embodiment 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle size (mesh)
aaaaa
aaaaa
particle size (mesh)
aaaaa
aaaaa
particle size (mesh)
aaaaa
aaaaa
Login to View More
Abstract
An embodiment of the invention discloses diatom ooze coating easy to clean and dry. The diatom ooze coating comprises, by weight, 25-35 parts of diatom ooze, 5-10 parts of calciumhydroxide, 3-8 partsof white cement, 1-3 parts of redispersible latex powder, 1-3 parts of nanometer titanium dioxide powder, 1-3 parts of sodiumchloride, 5-10 parts of cellulosenitrate, 5-10 parts of driers, 3-6 parts of formaldehyde absorbents, 4-8 parts of alkali lignin, 3-5 parts of modified polyester fibers and 25-35 parts of water. The diatom ooze coating in the embodiment of the invention has the advantagesthat extensive research is carried out on the driers, and composite driers with zirconium iso-octoate, manganese iso-octoate and copper iso-octoate which are compounded with one another at specific ratios can be obtained; synergistic effects can be realized by various components in the diatom ooze coating in the embodiment of the invention, only a few raw materials are used, energy can be saved,environments can be protected, and the obtained diatom ooze coating is short in surface drying time and hard drying time; the diatom ooze coating is good in antifouling property and easy to clean andis scrubbing-resistant when applied to diversified building surfaces, and excellent protection and decoration effects can be realized by the diatom ooze coating for walls.
Description
technical field [0001] The invention relates to the technical field of decorative coatings, in particular to an easy-to-clean and easy-to-dry diatom mud coating. Background technique [0002] At present, self-drying coatings are being vigorously developed at home and abroad, which requires the use of driers. Most of the driers are naphthenates, which can catalyze oxidation and promote polymerization, and accelerate the drying of paint films. The existing diatom mud paint has many raw materials, and the walls made of it are also easy to stain or even fall off, easy to drop powder, not resistant to scrubbing, and have a short service life. Contents of the invention [0003] In order to solve the problems in the prior art, the purpose of the embodiments of the present invention is to provide an easy-to-clean and easy-to-dry diatom mud coating. [0004] In order to achieve the above object, the technical solution of the embodiment of the present invention is: [0005] An eas...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More