A ceramic inkjet, black technology, applied in the field of ceramic decoration, can solve problems such as wear and blockage of printer nozzles, and achieve the effects of high ruthenium content, narrow particle size distribution and high yield

Inactive Publication Date: 2019-01-15
SUN YAT SEN UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of the stability and dispersibility of ceramic inks and the clogging and wear of printer nozzles caused by ceramic inks due to the large particle size of the coloring material, and to provide a controllable concentration, high yield, no need for secondary treatment, Black penetrating ink for ceramic inkjet printing with small particle size and narrow distribution, easy to popularize and apply, and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] React sodium isooctanoate and ruthenium trichloride at a molar ratio of 3:1. Before the reaction, mix sodium isooctanoate solution with alkane solvent evenly, add ruthenium trichloride, add 1‰ complexing agent, heat and stir at 110°C for 3 hours Prepare ruthenium isooctanoate, the percentages by weight of ruthenium isooctanoate and alkane solvent are 20% and 80% respectively, filter, wash and separate to obtain black ink.

Embodiment 2

[0018] React sodium isooctanoate and ruthenium trichloride at a molar ratio of 2:1. Before the reaction, mix sodium isooctanoate solution with alkane solvent evenly, add ruthenium trichloride, add 5‰ complexing agent, heat and stir at 110°C for 3 hours Prepare ruthenium isooctanoate, the weight percentages of ruthenium isooctanoate and alkane solvent are respectively 10% and 90%, filter, wash and separate liquid to obtain black ink.

Embodiment 3

[0020] React sodium isooctanoate with ruthenium acetylacetonate at a molar ratio of 3:1. Before the reaction, mix sodium isooctanoate solution with alkane solvent evenly, add ruthenium acetylacetonate, add 1‰ complexing agent, and heat and stir at 110°C for 3 hours. Ruthenium isooctanoate, the weight percentages of ruthenium isooctanoate and alkane solvent are respectively 30% and 70%, filter, wash and separate to obtain black ink.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
penetration depthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a black stain-bleeding ink for ceramic inkjet printing, wherein the black stain-bleeding ink is composed of the following components by the weight percentage: 10%-30% of a ruthenium metal complex, and 70%-90% of an organic solvent. The prepared black stain-bleeding ink has the advantages of high yield, high ruthenium content, homogenous phase of theink, no secondary treatment, narrow particle size distribution, no sedimentation, no clogging of printer nozzles, pure black after being printed and colored on a ceramic surface, and distinct patterns.

Description

Technical field: [0001] The invention relates to the technical field of ceramic decoration, in particular to a preparation technology of black bleeding ink for inkjet printing of ceramics. Background technique: [0002] Italy Meigao Company has been developing bleed ink since 2003. After more than ten years of technical reserves, it has become the leader in the field of bleed ink in the world. Ceramic inkjet bleed technology was introduced to China from Italy in 2013, and bleed ink was introduced in 2015. The research of the company has made a breakthrough in domestic color glaze enterprises and reached the stage of mass production. In the first half of 2015, leading enterprises in the industry such as Nobel, Dongpeng, and Mona Lisa successively released porcelain seepage tiles and produced them in batches, but the materials and technologies used came from abroad, and the output was not large. [0003] The research on domestic bleed ink is more than ten years later than tha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/30C09D11/36
CPCC09D11/30C09D11/36
Inventor 肖敏黄鹏飞孟跃中王拴紧韩东梅任山张风玲
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap