Manufacturing process of writable touch film

A manufacturing process and touch film technology, applied in the field of writable touch film manufacturing process, can solve the problems of large volume shrinkage affecting adhesion and affecting the overall performance of light-cured materials, and achieve improved crosslinking rate and high printing accuracy , Improve the effect of product yield

Active Publication Date: 2021-09-03
合肥元顿传感科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the photopolymerization system is cured in the air, the oxygen in the air will make the photo-cured surface not completely cured and sticky, which seriously affects the overall performance of the photo-cured material, especially the volume shrinkage after curing affects adhesion, hardness, etc. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1~4

[0019] Embodiments 1-4: A manufacturing process of a writable touch film, the writable touch film includes a transparent base material, a sensing layer and a writing layer, the sensing layer is arranged between the writing layer and the transparent base material, The writing layer further includes a substrate and a UV printing layer, and the sensing layer is bonded to the substrate of the writing layer;

[0020] The UV printing layer is obtained by UV printing material under ultraviolet light irradiation, and this UV printing material is composed of the following components by weight, as shown in Table 1:

[0021] Table 1

[0022] components Example 1 Example 2 Example 3 Example 4 Aliphatic polyurethane triacrylate 25 copies 40 copies 36 copies 38 copies 1,6 hexanediol diacrylate 50 copies 40 copies 45 copies 38 copies Ethylene glycol diglycidyl ether 12 copies 14 copies 11 copies 12 copies 4-acryloylmorpholine 0.9...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a manufacturing process of a writable touch film, and its UV printing material is obtained through the following steps: step 1, the aliphatic polyurethane triacrylate, 1,6 hexanediol diacrylate, Ethylene glycol diglycidyl ether, castor oil polyglycidyl ether and alkyl modified organosiloxane are mixed in a stirring disperser to obtain material 1; step 2, adding the weight part of Butyloxycresyl, organic thermosetting polymethylurea resin, 4‑acryloylmorpholine, 2‑hydroxy‑2‑methyl‑1‑phenyl‑1‑acetone, sulfonyloxyketone and coloring pigment, continue to mix, Obtain material 2; step 3, send the material 2 obtained in step 2 to a bead mill and grind to a particle size of 300-400nm to obtain a UV printing material. According to the manufacturing process of the writable touch film of the present invention, the prepared UV printing layer has high printing precision, high curing hardness and scratch resistance.

Description

technical field [0001] The invention relates to a touch film, in particular to a manufacturing process of a writable touch film. Background technique [0002] UV light curing technology has the advantages of fast curing speed, high production efficiency, good mechanical and physical properties, less pollution, energy saving, etc., and is known as a green technology. With the increasing emphasis on environmental protection and the development of science and technology, the UV curing market is developing rapidly and is widely used in coatings, adhesives, inks, electronic packaging, glass, dental restoration, photolithographic imaging, and biomedicine. Although UV curing technology has made a lot of progress, there are still some problems in application, such as serious oxygen inhibition phenomenon in the existing UV curing system, low curing hardness, high viscosity and poor stability. [0003] Oxygen inhibition refers to the phenomenon that in the free radical photopolymeriz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G06F3/041C09D4/06C09D4/02C09D7/63
CPCC08F283/008C08F289/00C08K5/5415C08K5/07C08K5/13B32B33/00B32B9/00B32B9/04B32B27/06B32B27/308C08J2351/08C08J2451/00C08J5/18C08F222/102
Inventor 刘泽江
Owner 合肥元顿传感科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products