Preparation method of high-temperature-resistant easily-stripped printing water-emulsion type resin

An easy-to-peel, water-emulsion-type technology, used in coatings, paper coatings, textiles and papermaking, etc., can solve the problems of poor film-forming properties, unenvironmental protection, and poor high temperature resistance, so as to improve heat resistance and overcome heat resistance. The effect of poor performance and good transparency

Inactive Publication Date: 2019-01-22
XIAN TIANYI ADHESIVE MATERIAL CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome above-mentioned deficiencies in the prior art, provide a kind of preparation method of high temperature resistant easy-peeling printing water-emulsion type resin, overcome the printing adaptability and easy-peeling property, poor film-forming property of coating film in the prior art, Poor high temperature resistance, not environmentally friendly, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-temperature-resistant easily-stripped printing water-emulsion type resin
  • Preparation method of high-temperature-resistant easily-stripped printing water-emulsion type resin

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0026] It should be noted that the structures, proportions, sizes, etc. shown in the drawings attached to this specification are only used to match the content disclosed in the specification, for those who are familiar with this technology to understand and read, and are not used to limit the implementation of the present invention Any modification of the structure, change of the proportional relationship or adjustment of the size shall still fall within the scope of the technical content disclosed in the present invention without affecting the effect and purpose of the present invention. In the range.

[0027] At the same time, terms such as "upper", "lower", "left", "right", "middle" and "one" quoted in this specification are only for the convenience of description and are not used to limit this specification. The practicable scope of the invention and the change or adjustment of its relative relationship shall also be regarded as the practicable scope of the present inventi...

Embodiment 1

[0029] The invention discloses a preparation method of high-temperature-resistant and easy-peeling printing water-emulsion resin, which comprises the following steps:

[0030] Step 1) configuring an aqueous emulsion of a nonionic emulsifier and an anionic emulsifier;

[0031] Step 2) Adding a low-temperature initiator to the aqueous emulsion in step 1) under stirring conditions and feeding nitrogen gas, and adding the monomer with a high glass transition temperature to the aqueous emulsion at a uniform speed and slowly within 4h to 7h;

[0032] Step 3) preparing high glass transition temperature resin seed emulsion;

[0033] Step 4) Use a pump to pump the medium-high glass transition temperature resin seed emulsion in step 3) into the pre-emulsified nano-oxide dispersion, and react to obtain a high-temperature resistant and easy-to-peel printing water-emulsion resin.

Embodiment 2

[0035] The invention discloses a preparation method of high-temperature-resistant and easy-peeling printing water-emulsion resin, which comprises the following steps:

[0036] Step 1) configuring an aqueous emulsion of a nonionic emulsifier and an anionic emulsifier;

[0037] Step 2) Adding a low-temperature initiator to the aqueous emulsion in step 1) under stirring conditions and feeding nitrogen gas, and adding the monomer with a high glass transition temperature to the aqueous emulsion at a uniform speed and slowly within 4h to 7h;

[0038] Step 3) preparing high glass transition temperature resin seed emulsion;

[0039] Step 4) Use a pump to pump the medium-high glass transition temperature resin seed emulsion in step 3) into the pre-emulsified nano-oxide dispersion, and react to obtain a high-temperature resistant and easy-to-peel printing water-emulsion resin.

[0040] Preferably, a method for preparing a high-temperature-resistant and easy-to-peel printing water-emuls...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of high-temperature-resistant easily-stripped printing water emulsion type resin, and the preparation method comprises the following steps: step 1) preparing a water-based emulsion of a nonionic emulsifier and an anionic emulsifier; step 2) under a stirring condition, after introducing nitrogen, adding a low-temperature initiator into the water-based emulsion of the step 1), and slowly dropwise adding a high glass transition temperature monomer into the water-based emulsion at a constant speed within 4-7 hours; step 3) preparing a high glass transition temperature resin seed emulsion; and step 4) and using a pump for pumping the high glass transition temperature resin seed emulsion obtained in the step 3) into a pre-emulsified nano oxide dispersion liquid for reaction to obtain the high-temperature-resistant easily-stripped printing water-emulsion type resin.

Description

technical field [0001] The invention belongs to the technical field of resin materials, and in particular relates to a preparation method of high-temperature-resistant and easy-to-peel printing water-emulsion resin. Background technique [0002] The water-based transfer protective coating is to coat a layer of paint on the surface of the paper-plastic film. After leveling and drying, a thin and uniform transparent bright layer is formed on the surface of the paper-plastic film. This layer not only makes the surface of the paper bright and smooth, but also plays a role Moisture-proof, anti-fouling, wear-resistant and other functions. The most important thing is that the water-based transfer protective coating can solve the problems of poor heat resistance, difficult peeling, difficulty in thermal transfer printing and printing adaptability of paper-plastic coating materials. It is truly green packaging and is being rapidly promoted and applied to advertising, Book covers, la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F292/00C08F220/06C08F230/08C08F220/14C08F212/08C09D151/10C09D5/20D21H19/20
CPCC08F292/00C09D5/18C09D5/20C09D151/10D21H19/20C08F220/06C08F230/08C08F220/14C08F212/08
Inventor 王伊尹常杰
Owner XIAN TIANYI ADHESIVE MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap