Low-water-absorption foamed cement

A technology of foamed cement and low water absorption, applied in the field of cement, can solve the problems affecting the service life of foamed cement, easy to absorb water, and limit the application of foamed cement, so as to shorten the setting speed and hardening speed, and the foam is fine and uniform, and keeps uniform The effect of sexuality and compactness

Inactive Publication Date: 2019-01-25
怀宁建国混凝土制品有限责任公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Foamed cement has a porous structure and is easy to absorb water, which w...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of low water absorption foaming cement, its raw material comprises by weight: 100 parts of cement, 1.9 parts of foaming agent, 0.7 part of foam stabilizer, 11 parts of waterproofing agent, 0.03 part of naphthalene-based water reducer, 0.5 part of reinforcing agent, water 47.5 parts, wherein, foaming agent is sodium lauryl sulfate and fatty alcohol polyoxyethylene ether sodium sulfate.

Embodiment 2

[0021] A kind of low water absorption foaming cement, its raw material comprises by weight: 100 parts of cement, 1.8 parts of foaming agent, 0.8 part of foam stabilizer, 10 parts of waterproofing agent, 0.04 part of naphthalene series water reducer, 0.4 part of strengthening agent, water 50 parts, wherein, whipping agent is sodium lauryl sulfate and fatty alcohol polyoxyethylene ether sodium sulfate;

[0022] The waterproofing agent is redispersible latex powder and triethanolamine phosphate;

[0023] The cement is high-strength sulfoaluminate cement and rapid hardening iron-aluminate cement;

[0024] The foam stabilizer is triethanolamine and fatty acid methanolamide;

[0025] The reinforcing agent is carboxymethyl cellulose and polyvinyl alcohol fiber.

Embodiment 3

[0027] A kind of low water absorption foaming cement, its raw material comprises by weight: 100 parts of cement, 2 parts of foaming agent, 0.6 part of foam stabilizer, 12 parts of waterproofing agent, 0.02 part of naphthalene series water reducer, 0.6 part of strengthening agent, water 45 parts, wherein, foaming agent is sodium lauryl sulfate and fatty alcohol polyoxyethylene ether sodium sulfate, and wherein, the weight ratio of sodium lauryl sulfate and fatty alcohol polyoxyethylene ether sodium sulfate is 5:1;

[0028] The waterproofing agent is redispersible latex powder and triethanolamine phosphate, wherein the weight ratio of redispersible latex powder and triethanolamine phosphate is 4:1;

[0029] The cement is high-strength sulfoaluminate cement and rapid-hardening iron-aluminate cement, wherein the weight ratio of high-strength sulfoaluminate cement and rapid-hardening iron-aluminate cement is 9:1;

[0030] The foam stabilizer is triethanolamine and fatty acid methan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses low-water-absorption foamed cement. The low-water-absorption foamed cement is prepared from the following raw materials in parts by weight: 100 parts of cement, 1.8 to 2 partsof a foaming agent, 0.6 to 0.8 part of a foam stabilizer, 10 to 12 parts of a waterproof agent, 0.02 to 0.04 part of a naphthalene water reducer, 0.4 to 0.6 part of a reinforcing agent, and 45 to 50 parts of water, wherein the foaming agent is lauryl sodium sulfate and fatty alcohol polyoxyethylene ether sodium sulfate. The low-water-absorption foamed cement is good in waterproof performance, lowin water absorption rate and good in strength.

Description

technical field [0001] The invention relates to the technical field of cement, in particular to a low-water-absorbing foamed cement. Background technique [0002] Foamed cement is to fully foam the foaming agent mechanically through the foaming system of the foaming machine, and evenly mix the foam with the cement slurry, and then go through the pumping system of the foaming machine for cast-in-place construction or mold molding. A new type of lightweight thermal insulation material with a large number of closed pores formed by natural conservation. [0003] Foamed cement has a porous structure and is easy to absorb water, which will affect the service life of foamed cement and limit the application of foamed cement. Contents of the invention [0004] Based on the technical problems in the background technology, the present invention proposes a low water absorption foamed cement, which has good water resistance, low water absorption and good strength. [0005] A kind of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/06C04B38/10
CPCC04B28/06C04B2201/50C04B24/16C04B24/166C04B24/122C04B24/124C04B2103/0057C04B2103/302C04B24/383C04B16/0641C04B38/10
Inventor 刘三宝
Owner 怀宁建国混凝土制品有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap