A kind of cobalt-based bulk amorphous alloy and preparation method thereof

An amorphous alloy, cobalt-based technology, applied in the field of cobalt-based bulk amorphous alloy and its preparation, can solve the problem of increasing raw material and preparation costs, hindering the large-scale application and development of Co-based bulk amorphous alloy, and unfavorable research and development. Develop ultra-high-strength metal materials and other issues to achieve high thermal stability

Active Publication Date: 2020-10-09
SOUTHWEST UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In summary, it can be found that the currently reported Co-based bulk amorphous alloys often contain noble metals such as Ta and Nb and rare earth elements, which greatly increases the cost of raw materials and preparation, which seriously hinders the scale-up of Co-based bulk amorphous alloys. Application and Development
At the same time, most Co-based bulk amorphous alloys contain a variety of components, which makes the preparation process and process of amorphous alloys too complicated, and is not conducive to the research and development of ultra-high-strength metal materials as a model system.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cobalt-based bulk amorphous alloy and preparation method thereof
  • A kind of cobalt-based bulk amorphous alloy and preparation method thereof
  • A kind of cobalt-based bulk amorphous alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0051] The present application also provides a method for preparing the cobalt-based bulk amorphous alloy, comprising the following steps:

[0052] A) batching is carried out according to the atomic percentage of each element of the cobalt-based bulk amorphous alloy shown in formula (I);

[0053] B) melting the raw materials obtained in step A) to obtain a master alloy ingot;

[0054] C) performing water-cooled copper mold suction casting on the master alloy ingot, rapid solidification and cooling to obtain a cobalt-based bulk amorphous alloy;

[0055] co a W b B c (I);

[0056] Wherein, a, b and c are the atomic percentages of corresponding elements;

[0057] a=54-70; b=15-30; c=12-19; ​​a+b+c=100.

[0058] In the process of preparing the cobalt-based bulk amorphous alloy, batching is carried out first, and the batching process is carried out in a manner well known to those skilled in the art, and there is no special limitation here. In a specific embodiment, the mass...

Embodiment 1 3

[0064] Example 1 Ternary Co 63 W 21 B 16 Preparation of bulk amorphous alloys

[0065] Step 1: Ingredients

[0066] According to Co a W b B c The target composition of the ternary bulk amorphous alloy takes three kinds of raw materials Co, W and B, and the metal raw materials need to polish the surface oxide skin, and the mass percentage purity of each raw material needs to be higher than 99.9%; the Co a W b B c Among them, Co is metal cobalt Co, W is metal tungsten W, B is elemental boron B, a, b, and c are atomic percentages, a=63, b=21, c=16, and a+b+c=100;

[0067] Step 2: Melting into alloy ingots and preparing Co in a vacuum electric arc furnace 63 W 21 B 16 bulk amorphous alloy

[0068] Put the prepared raw materials into the vacuum electric arc furnace, and then evacuate to 4×10 -3 Below Pa, fill in 0.05MPa argon again, and continue vacuuming to 4×10 -3 Below Pa, refill with 0.2MPa argon; under the protection of an argon atmosphere with a mass percentage ...

Embodiment 2

[0074] Example 2Co 59 W 26 B 15 Preparation of bulk amorphous alloys

[0075] Step 1: Ingredients

[0076] According to Co a W b B c The target composition of the ternary bulk amorphous alloy takes three kinds of raw materials Co, W and B, and the metal raw materials need to polish the surface oxide skin, and the mass percentage purity of each raw material needs to be higher than 99.9%; the Co a W b B c Among them, Co is metal cobalt Co, W is metal tungsten W, B is elemental boron B, a, b, and c are atomic percentages, where a=59, b=26, c=15, and a+b+c= 100;

[0077] Step 2: Melting alloy ingots and Co in a vacuum electric arc furnace 59 W 26 B 15 Bulk amorphous alloy Put the prepared raw materials into the vacuum electric arc furnace, and then vacuumize to 4×10 -3 Below Pa, fill in 0.05MPa argon again, and continue vacuuming to 4×10 - 3 Below Pa, refill with 0.2MPa argon; under the protection of an argon atmosphere with a mass percentage of high purity of 99.99...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
breaking strengthaaaaaaaaaa
breaking strengthaaaaaaaaaa
Login to View More

Abstract

The present invention provides a kind of such as formula Co a W b B c The cobalt-based bulk amorphous alloy shown, wherein a, b and c are the atomic percentages of the corresponding elements; a=54-70; b=15-30; c=12-19; ​​a+b+c=100 . The cobalt-based bulk amorphous alloy provided by this application has ultra-high strength, ultra-high hardness, extremely high thermal stability, strong amorphous forming ability, good corrosion resistance and soft magnetic properties; the experimental results show that this The strength of the cobalt-based bulk amorphous alloy provided by the application is 5500MPa-6300MPa, the glass transition temperature Tg is 844K-960K, and the corrosion current density in 3.5wt / % NaCl solution is as low as 8μA / cm 2 .

Description

technical field [0001] The invention relates to the technical field of amorphous alloys, in particular to a cobalt-based bulk amorphous alloy and a preparation method thereof. Background technique [0002] Bulk amorphous alloys are amorphous alloys whose three-dimensional dimensions are greater than 1 mm. Bulk amorphous alloy has a unique structure of long-range disorder and short-range order due to its atomic arrangement, so it has extremely high strength and hardness, excellent corrosion resistance and wear resistance, etc. , information and other fields show good application prospects. [0003] Among the many systems of bulk amorphous alloys, the mechanical properties of cobalt-based bulk amorphous alloys are particularly outstanding. In 2003, Inoue and others from Tohoku University in Japan developed a Co-Fe-Ta-B bulk amorphous alloy with a fracture strength of 5.2GPa, creating the world's highest strength record for metal bulk materials at that time (Inoue A, Shen B L...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C45/04
CPCC22C45/04C22C1/11
Inventor 郭胜锋赖利民丁凯露
Owner SOUTHWEST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com