Production Technology of Diamond Wire Busbar Drawing Die

A wire drawing die and production process technology, applied in metal wire drawing, metal drawing forming tools, metal processing equipment, etc., can solve the problems of insufficient thermal conductivity of the sintered body 13, slow heat dissipation of the polycrystalline diamond 12, brittleness of the sintered body, etc. , to achieve the effect of improving thermal conductivity, improving filling efficiency, and reducing pressing pressure

Active Publication Date: 2019-11-12
ZHEJIANG JINPING WIRE DRAWING DIE CO LTD
View PDF16 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] It has been found through practical application that when the sintered body 13 prepared by using the sintered powder formula provided in the cited document is used in a diamond wire bus wire drawing die, the sintered body 13 has too high hardness and insufficient toughness, and the sintered body is brittle. hidden dangers, due to the insufficient thermal conductivity of the sintered body 13, there is a problem of slow heat dissipation of the polycrystalline diamond 12; therefore, a new solution needs to be proposed to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production Technology of Diamond Wire Busbar Drawing Die
  • Production Technology of Diamond Wire Busbar Drawing Die
  • Production Technology of Diamond Wire Busbar Drawing Die

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The present invention will be described in further detail below in conjunction with the accompanying drawings.

[0026] The production process of the diamond wire bus wire drawing die includes the following steps:

[0027] Step S1 (refer to figure 1 ), forming a mold cover 11 that meets the assembly requirements through CNC lathe processing, and opening a central hole groove 14 in the center of the end face of the mold cover 11 through a laser drilling machine to obtain the mold cover 11; technical effect: manufacturing the mold cover 11 according to the actual assembly requirements , so as to improve the adaptability of the diamond wire bus wire drawing die, so that it can meet various models and different manufacturers of wire drawing machines.

[0028] S2 (reference figure 2 , image 3), mix 30% copper powder, 20% nickel powder, 10% silver powder, 3% zinc powder, 6% tungsten powder, 8% manganese powder, 21% tin powder in proportion and grind them thoroughly , t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production process of a diamond wire busbar wire drawing die, relates to the technical field of wire drawing dies, and aims at the problems that sintered bodies is too high in hardness and insufficient in toughness, and polycrystalline diamond is low in radiating speed. According to the technical scheme, the production process is characterized in that the production process of the diamond wire busbar wire drawing die comprises the following steps that S2, 30% of copper powder, 20% of nickel powder, 10% of silver powder, 3% of zinc powder, 6% of tungsten powder, 8% ofmanganese powder and 21% of tin powder are uniformly mixed and fully ground, and sintered powder is obtained; and S4, a plurality of die sleeve fillers are clamped in a sintering press, the sinteringbodies are sintered and formed through the sintering press, the pressing pressure is 0.3-0.4 MPa, the temperature is raised to 610-630 DEG C at the rate of 11-14 DEG C / s and maintained for 14-15min, and then the sintering bodies are cooled to 200 DEG C or below with a furnace, and a die sleeve diamond composite is obtained. Through the production process of the diamond wire busbar wire drawing die, the hidden trouble of brittle cracks of the sintered bodies is reduced, the heat conduction performance of the sintered bodies is improved, and the heat dissipation capability of polycrystalline diamond is improved.

Description

technical field [0001] The invention relates to the technical field of wire drawing dies, more specifically, it relates to a production process of a diamond wire bus wire drawing die. Background technique [0002] Diamond wire is the abbreviation of diamond cutting wire, also known as diamond cutting wire or diamond wire. Generally, it is a diamond cutting wire made by inlaying tiny diamond particles on the busbar; the diamond wire busbar drawing die is used On the wire drawing machine, it is specially used for wire drawing to produce diamond wire busbar dies. [0003] Diamond wire bus wire drawing die such as Figure 5 As shown, it includes a mold base 1, a mold cover 11 clamped and fixed with the mold base 1, a polycrystalline diamond 12 arranged on the mold cover 11, and a sintered body 13 filled between the polycrystalline diamond 12 and the mold cover 11; The role of the body 13 is to protect the polycrystalline diamond 12 and reduce the hidden danger of its brittlenes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21C3/18
CPCB21C3/18
Inventor 张安朱琰琛
Owner ZHEJIANG JINPING WIRE DRAWING DIE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products