Polyolefin composition, polyolefin masterbatch, polyolefin film and surface decorative composite material and preparation method of surface decorative composite material

A polyolefin film and composite material technology, applied in the field of decorative materials, can solve the problems of high cost and increase the cost of raw materials, and achieve the effect of dense surface structure and inhibition of surface migration.

Active Publication Date: 2019-03-05
BYD CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Since thermoplastic polyolefin elastomer films are usually relatively expensive, the use of thermoplastic polyolefin elastomer films to make the skin layer of automotive interiors can provide a soft touch, while improving the grade of automotive interiors, it also virtually increases the cost of raw materials
At the same time, lightweight has become the development trend of the automotive industry, but the current interior skin materials have little consideration for lightweight development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyolefin composition, polyolefin masterbatch, polyolefin film and surface decorative composite material and preparation method of surface decorative composite material
  • Polyolefin composition, polyolefin masterbatch, polyolefin film and surface decorative composite material and preparation method of surface decorative composite material
  • Polyolefin composition, polyolefin masterbatch, polyolefin film and surface decorative composite material and preparation method of surface decorative composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] In the fifth aspect, the present invention also provides a method for preparing a surface decoration composite material, the preparation method comprising the following steps: S1, sequentially extruding, molding, and cooling the polyolefin masterbatch according to the present invention to obtain a polyolefin Film; S2. Heating one side surface of the polyolefin film to melt it to form a melting surface to be embossed, and then bonding the foam layer to the other side surface of the polyolefin film and performing lamination-pressing The flowers are processed to obtain composite materials.

[0039] According to the preparation method of the present invention, the steps of extruding and forming the polyolefin film masterbatch can be carried out in a three-roll calender. For specific operating conditions, reference can be made to conventional operating conditions in the art. Taking the steps of extruding and molding with a three-roll calender as an example, the operating pa...

Embodiment 1-6

[0049] Examples 1-6 and Comparative Documents 1-3

[0050] (1) The polyolefin film composition comprises:

[0051] Thermoplastic polyolefin (TPO): commercially available from Exxon Mobil's TPO CNN010, the melt flow index is 8g / 10min; the density is 0.90g / mL;

[0052] Linear low-density polyethylene (LLDPE): commercially available from Dow DuPont's linear low-density polyethylene 1648, the melt flow index is 3.5g / 10min; density is 0.92g / mL;

[0053] Random copolymer polypropylene (PP-R): commercially available from Yanshan Petrochemical Co., Ltd. random copolymer polypropylene C5908, melt flow index is 9g / 10min; density is 0.91g / mL;

[0054] Cross-linking agent: commercially available dicumyl peroxide from Sinopharm Group;

[0055] Crosslinking auxiliary agent 1: TAIC-70D commercially purchased from Shanghai Changyu Chemical Co., Ltd., wherein the content of triallyl isocyanurate is greater than 70% by weight;

[0056] Cross-linking aid 2: RICON 154DA commercially available ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polyolefin composition, a polyolefin masterbatch, a polyolefin film and a surface decorative composite material and a preparation method of the surface decorative composite material. The composition comprises, in parts by weight, 100 parts of a polyolefin system, 0.01-3 parts of a crosslinking agent, 0.01-3 parts of a crosslinking assistant and 0.1-10 parts of a microsphere expansion agent when the weight of the polyolefin system is counted as a standard, wherein the crosslinking agent is an organic peroxide crosslinking agent, and the cross-linking assistant is an acrylate crosslinking assistant and / or a polybutadiene-based crosslinking assistant. The microsphere expansion agent is added, and a mode of microsphere expansion is adopted to replace the mode of gas foaming, so that not only can the density of the formed polyolefin film be reduced, but also no formation of pinholes in the surface of the formed polyolefin film can be achieved, and the surface structure of the polyolefin film is dense, soft and comfortable.

Description

technical field [0001] The invention relates to the field of decorative materials, in particular to a polyolefin composition, a polyolefin masterbatch, a polyolefin film, a surface decoration composite material and a preparation method thereof. Background technique [0002] The scope of automotive interiors is mainly composed of instrument panels, door panels, roofs, seat cushions, wood grain finishes, sun visors, armrests, gear covers, etc. The material properties are very demanding, and they have high requirements for temperature resistance, weather resistance, odor, appearance, Wear resistance and other requirements are very strict. Among them, the structures of instrument panels, door panels, armrests, roofs, seat backs, etc. are basically the same. At present, the skin layers of these automotive interiors are increasingly using thermoplastic polyolefin elastomer films (TPO or TPV) . [0003] Since thermoplastic polyolefin elastomer films are usually relatively expensi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/00C08L23/08C08L23/14C08K13/02C08K5/14C08J9/32C08J3/24C08J3/22B32B27/06B32B27/32B32B5/18B32B7/10B29D7/01
CPCB29D7/01B32B5/18B32B7/10B32B27/065B32B27/32B32B2255/10B32B2255/26B32B2264/0257B32B2307/71C08J3/226C08J3/246C08J5/18C08J9/32C08J2203/22C08J2323/00C08J2323/14C08J2423/00C08J2423/08C08L23/00C08L23/14C08L2203/14C08L2203/16C08L2205/035C08L2207/04C08L23/0815C08K13/02C08K5/14
Inventor 黄少华徐学峰沈艳超
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com