Water-based sunlight-resistant red pigment and preparation method thereof
A light-fast red and pigment technology, applied in the field of chemical pigments, can solve the problems of poor printing performance, poor emulsification of offset printing ink, water pollution, etc., and achieve the effect of improving water resistance and increasing emulsification.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] (1) Preparation of rosin liquid: start stirring, add 2 parts of potassium hydroxide to water, add 15 parts of rosin, stir and dissolve for 30 minutes, check that it is completely transparent, and obtain rosin liquid;
[0022] (2) Preparation of diazo solution: start stirring and adjust the motor speed to 35HZ, add 35 parts of RC base and 10 parts of G red base, heat up to 40 degrees, add ammonia water, PH=8.5, check the dissolution and transparency, add ice to cool down To 25 degrees, adjust the motor; speed 50HZ, quickly add hydrochloric acid and continue to add ice to 0 degrees; stir for 20 minutes, add 15 parts of sodium nitrate, and when finished, check the end point of diazotization with PH test paper and KI test paper, requiring PH test paper to be redder. The KI test paper is blue, the temperature is 0 degrees, and the delay is 20 minutes. Check the diazotization end point. The KI test paper is slightly blue to slightly blue, and the diazonium solution is obtained...
Embodiment 2
[0026] (1) Preparation of rosin liquid: start stirring, add 4 parts of potassium hydroxide to water, add 20 parts of rosin, stir and dissolve for 35 minutes, check that it is completely transparent, and obtain rosin liquid;
[0027] (2) Preparation of diazo solution: start stirring and adjust the motor speed to 35HZ, add 40 parts of RC and 20 parts of RC, heat up to 40 degrees, add ammonia water, PH=8.6, check the dissolution and transparency, add ice to cool down To 25 degrees, adjust the motor; speed 50HZ, quickly add hydrochloric acid and continue to add ice to -1 degrees; stir for 20 minutes, add 30 parts of sodium nitrate, and when finished, check the end point of diazotization with PH test paper and KI test paper, and the PH test paper is required to be red , the KI test paper is blue, the temperature is 1 degree, and the delay is 20 minutes. Check the diazotization end point. The KI test paper is slightly blue to slightly blue, and the diazonium solution is obtained;
...
Embodiment 3
[0031] (1) Preparation of rosin liquid: start stirring, add 6 parts of potassium hydroxide to water, add 23 parts of rosin, stir and dissolve for 40 minutes, check that it is completely transparent, and obtain rosin liquid;
[0032] (2) Preparation of diazo solution: start stirring and adjust the motor speed to 35HZ, add 50 parts of RC and 25 parts of RC, heat up to 40 degrees, add ammonia water, PH=9.0, check the dissolution and transparency, add ice to cool down To 25 degrees, adjust the motor; speed 50HZ, quickly add hydrochloric acid and continue to add ice to -1 degrees; stir for 20 minutes, add 30 parts of sodium nitrate, and when finished, check the end point of diazotization with PH test paper and KI test paper, and the PH test paper is required to be red , the KI test paper is blue, the temperature is 1 degree, and the delay is 20 minutes. Check the diazotization end point. The KI test paper is slightly blue to slightly blue, and the diazonium solution is obtained;
...
PUM
![No PUM](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/noPUMSmall.5c5f49c7.png)
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka.patsnap.com/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap