A kind of zinc oxide nanowire and its preparation method

A zinc oxide nanowire and zinc oxide technology, applied in the direction of zinc oxide/zinc hydroxide, etc., can solve the problems of cumbersome preparation process, complicated production equipment, and high personnel requirements

Active Publication Date: 2021-05-11
ARMY ENG UNIV OF PLA
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the technical problems that existing zinc oxide nanowires require special raw materials or reagents, cumbersome preparation process, complex production equipment and high requirements for personnel, the present invention provides a zinc oxide nanowire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of zinc oxide nanowire and its preparation method
  • A kind of zinc oxide nanowire and its preparation method
  • A kind of zinc oxide nanowire and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment provides a method for preparing zinc oxide nanowires, which specifically includes the following steps:

[0034] Weigh 28g of zinc oxide, 11.6g of aluminum powder, 30.7g of cuprous oxide, and 11.6g of tin oxide (the moles of zinc oxide, aluminum powder, cuprous oxide and tin The ratio is 16:20:10:4), after uniform mixing in the mixer for 2 hours, pour figure 1 The graphite crucible 4 in the shown reaction chamber 2 is placed in a combustion synthesis device, ignited with a tungsten wire to initiate a self-propagating high-temperature synthesis reaction, and the reaction ends within ten seconds. After natural cooling, the reaction chamber, A large number of gray zinc oxide nanowires were collected in graphite crucibles and gas-permeable covers.

Embodiment 2

[0036] This embodiment provides a method for preparing zinc oxide nanowires, which specifically includes the following steps:

[0037] Weigh 31.6g of zinc oxide, 11.6g of aluminum powder, 30.7g of cuprous oxide, and 5.8g of tin oxide (the content of zinc oxide, aluminum powder, cuprous oxide and tin The molar ratio is 18:20:10:2), after uniform mixing in the mixer for 2h, pour figure 1 The graphite crucible 4 in the shown reaction chamber 2 is placed in a combustion synthesis device, ignited with a tungsten wire to initiate a self-propagating high-temperature synthesis reaction, and the reaction ends within ten seconds. After natural cooling, the reaction chamber, A large number of gray zinc oxide nanowires were collected in graphite crucibles and gas-permeable covers.

Embodiment 3

[0039] This embodiment provides a method for preparing zinc oxide nanowires, which specifically includes the following steps:

[0040] Weigh 33.2g of zinc oxide, 11.6g of aluminum powder, 30.7g of cuprous oxide, and 2.9g of tin oxide (the content of zinc oxide, aluminum powder, cuprous oxide and tin The molar ratio is 19:20:10:1), after uniform mixing in the mixer for 2h, pour figure 1 The graphite crucible 4 in the shown reaction chamber 2 is placed in a combustion synthesis device, ignited with a tungsten wire to initiate a self-propagating high-temperature synthesis reaction, and the reaction ends within ten seconds. After natural cooling, the reaction chamber, A large number of gray zinc oxide nanowires were collected in graphite crucibles and gas-permeable covers.

[0041] result test

[0042] Phase analysis, microscopic morphology analysis and microwave absorption performance analysis were performed on the zinc oxide nanowires obtained in the examples.

[0043] 1. Pha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of nanomaterial preparation, in particular to a zinc oxide nanowire and a preparation method thereof. The zinc oxide nanowire is made by burning a combustion agent, a propellant, a zinc source agent and an additive. The preparation method of the invention does not need special raw materials and equipment, is simple to operate, requires low technical level requirements on equipment and production personnel, has large output, and is suitable for batch preparation.

Description

technical field [0001] The invention relates to the technical field of nanomaterial preparation, in particular to a zinc oxide nanowire and a preparation method thereof. Background technique [0002] Nano Zinc Oxide (ZnO) is a multifunctional new inorganic material with a particle size between 1-100nm. Due to the miniaturization of crystal grains, the surface electronic structure and crystal structure change, resulting in surface effects, volume effects, quantum size effects, macroscopic tunnel effects, and high dispersion that macroscopic objects do not have. Magnetism, mechanics and other aspects show many special functions, which make them have important application value in many fields such as ceramics, chemical industry, electronics, optics, biology, medicine, textile, coating, etc., and can be used as ultraviolet light shielding materials, antibacterial agents, fluorescent Materials, photocatalytic materials, etc., have advantages that ordinary zinc oxide does not hav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G9/03
CPCC01G9/03C01P2002/72C01P2004/01C01P2004/16
Inventor 唐香珺赵芳李俊寿张翼飞李青韩兰懿
Owner ARMY ENG UNIV OF PLA
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com