Copolymer compatilizer and preparation method and application thereof

A technology of compatibilizer and copolymer, which is applied in the field of copolymer compatibilizer and its preparation, and can solve the problems of easy migration of compatibilizer

Active Publication Date: 2019-03-19
WANHUA CHEM GRP CO LTD
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this linear compatibilizer also faces the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Copolymer compatilizer and preparation method and application thereof
  • Copolymer compatilizer and preparation method and application thereof
  • Copolymer compatilizer and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0043] A certain amount of carboxyl-terminated liquid polybutadiene (Shandong Qilong Chemical Co., Ltd., the number of repeating units is 100) and an equimolar amount of glycidyl acrylate are added to the reactor, and then 3% of the total mass of the reactants The catalyst 4-dimethylaminopyridine and the solvent toluene with a mass ratio of 1:1 to the total reactants were added into the reaction kettle, mixed evenly, heated to 100°C under stirring, and reacted for 5 hours. Then discharge, remove the solvent and unreacted reactant and catalyst. The resulting product was dried at 120°C to constant weight to obtain Functionalized Liquid Polybutadiene Example 1.

preparation example 2

[0045]Add a certain amount of hydroxyl-terminated liquid polybutadiene (Shandong Qilong Chemical Co., Ltd., the number of repeating units is 50) and glycidyl methacrylate into the reactor, wherein the hydroxyl-terminated liquid polybutadiene and methacrylic acid The ratio of glycidyl ester is 1:1.2, then will account for the catalyst 4-dimethylaminopyridine of reactant gross mass 4% and be 3:2 solvent hexanaphthene with reactant gross mass ratio to join in the reactor, mix Evenly, the temperature was raised to 110°C under stirring, and the reaction was carried out for 4 hours. Then discharge, remove the solvent and unreacted reactant and catalyst. The resulting product was dried at 120°C to constant weight to obtain functionalized liquid polybutadiene Example 2.

preparation example 3

[0047] A certain amount of hydroxyl-terminated liquid polybutadiene (Shandong Qilong Chemical Co., Ltd., number of repeating units is 30) and maleic anhydride are added in the reactor, wherein the ratio of hydroxyl-terminated liquid polybutadiene and maleic anhydride is 1:1.1. Then, the catalyst pyridine accounting for 6% of the total mass of the reactants and the solvent cyclohexane with a ratio of 2:1 to the total mass of the reactants were added into the reactor, mixed evenly, and heated to 110° C. under stirring, and reacted for 4 hours. Then discharge, remove the solvent and unreacted reactant and catalyst. The resulting product was dried at 120°C to constant weight to obtain functionalized liquid polybutadiene Example 3.

[0048] Other functionalized liquid polybutadienes used in the following examples were prepared as described above except using different numbers of repeating units of hydroxyl terminated liquid polybutadienes, different anhydrides or acid esters.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Melt indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to a copolymer compatilizer. Copolymer comprises 50-80wt% of alkenyl monomer of with solubility parameter between 16.5-23(MPa)1/2, 0.1-10wt% of functional monomer and 10-40wt% offunctionalized liquid polybutadiene. Structure of the copolymer compatilizer is shown as follows, wherein R1 refers to -H or -COOH, R2 refers to -H or -CH3, X refers to -OH, -COOH or -NH2, and repeating unit number n is an integer between 10 and 200. The invention further provides a preparation method and application of the copolymer compatilizer. Compared with the prior art, the trielement copolymer has the advantages that the copolymer can be stably distributed on two-phase interfaces of polyester or polyamide and ABS, can improve phase morphology and improve mechanical performance of alloy, especially impact performance.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a copolymer compatibilizer and its preparation method and application, which can be used to improve compatibility and improve the performance of blended materials. Background technique [0002] Polymer alloy technology can improve the performance of polymer materials, reduce production conditions and realize the functionalization and high performance of polymer materials. It plays an irreplaceable role in the fields of polymer science and polymer material engineering. [0003] It is generally believed that in order to ensure an excellent blending effect, the components of the polymer alloy must have good compatibility, and the following principles should be considered when selecting the resin: the principle of polarity matching, the principle of similar surface tension, the principle of similar diffusion ability, The principle of equal viscosity and the principle of sim...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F279/02C08F220/14C08F212/08C08F220/18C08L69/00C08L55/02
CPCC08F279/02C08L69/00C08L2205/08C08L2205/03C08L55/02C08L51/04C08F220/1803C08F220/1802C08F220/1804
Inventor 张金龙周明黄岐善杨杰
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap