A kind of flexible pzt/pvdf composite piezoelectric gel material and preparation method thereof

Abstract

A flexible PZT / PVDF composite piezoelectric electrogel material and a preparation method thereof belong to the technical field of piezoelectric materials. In the present invention, PVDF sol and PZT sol are respectively prepared and compounded to form a gel, and the flexible PVDF nanosheet is obtained through drying treatment, and PZT nanoparticles are grown on the flexible PVDF nanosheet and aggregated to form a nanoporous network structure. Composite piezoelectric electrogel materials. The composite airgel of the present invention has extremely low density due to its special microstructure, and the density of the material can be adjusted by adjusting the porosity of the airgel. It shows the characteristics of high strength and good flexibility, and PVDF is an organic piezoelectric material, which has good piezoelectric properties when combined with PZT, which is conducive to promoting the application of piezoelectric electrogel materials in the field of underwater acoustic transducers.

Description

technical field [0001] The invention belongs to the technical field of piezoelectric materials, and in particular relates to a flexible PZT / PVDF composite piezoelectric electrogel material and a preparation method thereof. Background technique [0002] Lead zirconate titanate (PZT) is a typical trigonal-tetragonal perovskite ferroelectric ceramic with excellent piezoelectric and dielectric properties, which plays an important role in the modern electronics industry and is widely used as an acoustic transducer It is used in the field of underwater acoustic transducers and medical imaging diagnostic equipment. The hydrostatic figure of merit (HFOM) is a standard to measure whether a material is suitable for making acoustic transducers such as hydrophones, and the hydrostatic voltage coefficient (g h ) is often used to characterize the sensitivity of underwater acoustic transducers, while the hydrostatic pressure coefficient depends on the piezoelectric coefficient and dielect...

AI Technical Summary

Problems solved by technology

In this organic sol-gelation method, metal alkoxides are usually used as precursors, and metal alkoxides undergo rapid hydrolysis and polycondensation reactions when they meet water, which is very easy to generate precipitates and cannot exist in a sol state; at the same time, PZT is lead ( Pb), zirconium (Zr), titanium (T) ternary metal oxides, the hydrolysis and polycondensation conditions of each precursor are different, it is difficult to find out the conditions that satisfy the hydrolysis and polycondensation of the three precursors at the same time; the valence of Pb is divalent and the content More, it is difficult to form a firm three-dimensional network structure, which makes PZT airgel brittle

Therefore, so far, PZT airgel has rarely been reported, almost staying at the research level of the Peer team (Journal of Non-Crystalline Solids, 1995,186:59-63) in the 1990s

On the other hand, although the density of airgel can be considered to be the lowest among all solid materials, it is precisely because of its special microstructure that the skeleton structure is unstable, which makes the mechanical properties of airgel poor.

PZT airgel, like other aerogels, has poor strength, high brittleness, poor flexibility, poor agglomeration, and cannot maintain good interface integrity due to its high porosity. Due to these reasons, its intrinsic properties are also obvious. As a result, pure PZT airgel cannot be used in underwater acoustic transducers at all, which limits the development of PZT airgel materials in the field of underwater acoustic transducers to a large extent.