TA23 alloy plate with high impact toughness and high plasticity and preparation and application
A technology of alloy sheet and high plasticity, which is applied in the field of TA23 alloy sheet and its preparation and application, to achieve the effects of structure refinement, high safety, and novel process route
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0035] Example 1
[0036] (1) Ingot smelting: zero-grade titanium sponge, zirconium sponge, aluminum beans and pure iron are selected for ingredients and pressed into electrode blocks. After three vacuum consumable arc furnace smelting, TA23 alloy ingots are obtained, and the phase transition point is measured by metallographic method. 945℃;
[0037] (2) Slab forging: forging the TA23 alloy ingot obtained in step (1), wherein the forging temperature of the first-fire billet is 1050° C. (T β +105℃), after two piers and two pulls, the total deformation amount is 70%, and the final forging temperature is 865℃. Temperature 920℃(T β -25°C), also upsetting twice, the total deformation is 73%, the final forging temperature is 812°C, and then after shaping and milling, a square slab with a specification of 150mm for rolling is obtained, and the slab structure is equiaxed α +Intergranular beta, the slab meets the GB / T5193-2007 ultrasonic flaw detection grade A standard;
[0038] (3...
Example Embodiment
[0045] Example 2
[0046] (1) Ingot smelting: zero-grade titanium sponge, zirconium sponge, aluminum beans and pure iron are selected for ingredients and pressed into electrode blocks. After three vacuum consumable arc furnace smelting, TA23 alloy ingots are obtained, and the phase transition point is measured by metallographic method. 950℃;
[0047] (2) Slab forging: forging the TA23 alloy ingot obtained in step (1), wherein, the forging temperature of one-fire billeting is 1080°C (T β +130°C), after two piers and two pulls, the total deformation is 78%, the final forging temperature is 852°C, and the coarse as-cast structure is fully broken after forging in one fire; Temperature 930℃(T β -20°C), also upsetting twice, the total deformation is 75%, the final forging temperature is 803°C, and then after shaping and milling, a square slab with a specification of 120mm for rolling is obtained, and the slab structure is equiaxed α +Intergranular beta, the slab meets the GB / T5193-...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap