Fireproof paint

A technology of refractory coatings and raw materials, applied in the direction of fire-resistant coatings, lime coatings, coatings, etc., can solve the problems of reduced service life and low fire-resistant performance of refractory coatings, and achieve good compatibility, delayed decomposition, and good fire-resistant and flame-retardant properties Effect

Inactive Publication Date: 2019-03-26
ANHUI KAILIN ADVANCED MATERIAL CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the fire-resistant performance of the refractory coatings on the market is not high, which leads to a reduction in its service life and is difficult to meet the needs of the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of refractory coating, its raw material comprises by weight: 35 parts of diphenyl ether formaldehyde resin, 27 parts of modified expanded graphite, 12 parts of perlite powder, 12 parts of yttrium oxide powder, 5 parts of aluminum dihydrogen tripolyphosphate, cellulose acetate 6 parts of prime, 8 parts of o-xylene, 12 parts of film-forming agent, 3 parts of pentaerythritol, 1.5 parts of coupling agent, 1.5 parts of defoamer, 0.6 part of wetting agent, 1.5 parts of stabilizer, and 0.7 part of microgel.

Embodiment 2

[0021] A kind of refractory coating, its raw material comprises by weight: 50 parts of diphenyl ether formaldehyde resin, 16 parts of modified expanded graphite, 17 parts of perlite powder, 7 parts of yttrium oxide powder, 9 parts of aluminum dihydrogen tripolyphosphate, cellulose acetate 2 parts of prime, 15 parts of o-xylene, 5 parts of film-forming agent, 9 parts of pentaerythritol, 0.3 part of coupling agent, 4.5 parts of defoamer, 0.2 part of wetting agent, 2.5 parts of stabilizer, 0.2 part of microgel;

[0022] Wherein, the modified expanded graphite is prepared according to the following process: take ferrosilicon nitride powder and add deionized water, ultrasonically disperse to obtain ferrosilicon nitride dispersion; Graphite, supersonic treatment, then adding large particle size expanded graphite, mechanical stirring, filtering, drying, to obtain modified expanded graphite.

Embodiment 3

[0024] A kind of refractory coating, its raw material comprises by weight: 43 parts of diphenyl ether formaldehyde resin, 20 parts of modified expanded graphite, 15 parts of perlite powder, 10 parts of yttrium oxide powder, 7 parts of aluminum dihydrogen tripolyphosphate, cellulose acetate 4 parts of prime, 10 parts of o-xylene, 8 parts of film-forming agent, 5 parts of pentaerythritol, 1 part of coupling agent, 3 parts of defoamer, 0.4 part of wetting agent, 2 parts of stabilizer, 0.4 part of microgel;

[0025] Wherein, the modified expanded graphite is prepared according to the following process: take ferrosilicon nitride powder and add deionized water, ultrasonically disperse to obtain ferrosilicon nitride dispersion; Graphite, ultrasonic treatment, then adding large particle size expanded graphite, mechanical stirring, filtering, drying, to obtain modified expanded graphite;

[0026] In the operation of the ultrasonic dispersion, the ultrasonic power is 210W, and the ultra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of paint and in particular relates to fireproof paint. The fireproof paint comprises the following raw materials in parts by weight: 35-50 parts of diphenylether-formaldehyde resins, 16-27 parts of modified expanded graphite, 12-17 parts of perlite powder, 7-12 parts of yttria powder, 5-9 parts of aluminum dihydrogen tripolyphosphate, 2-6 parts of cellulose acetate, 8-15 parts of ortho-xylene, 5-12 parts of a film-forming agent, 3-9 parts of pentaerythritol, 0.3-1.5 parts of a coupling agent, 1.5-4.5 parts of an antifoaming agent, 0.2-0.6 part of awetting agent, 1.5-2.5 parts of a stabilizer and 0.2-0.7 part of microgel. The fireproof paint disclosed by the invention has excellent fire resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a refractory coating. Background technique [0002] Fire-resistant coating is a special coating used on the surface of flammable substrates, which can reduce the flammability of the surface of the coated material, retard the rapid spread of fire, and improve the fire resistance limit of the coated material. Applied on the surface of combustible substrates to change the combustion characteristics of the material surface and retard the rapid spread of fire; or applied to building components to improve the fire resistance limit of the components, called refractory coatings. [0003] However, the refractory coatings currently on the market have low refractory properties, resulting in reduced service life, which is difficult to meet market demand. Contents of the invention [0004] Based on the technical problems existing in the background technology, the present invention propose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/00C09D101/12C09D5/18C09D7/61C09D7/63C09D7/65
CPCC08K2003/221C08L2201/02C09D5/185C09D7/61C09D7/63C09D7/65C09D161/00C09D1/12C08K13/06C08K9/02C08K7/24C08K3/34C08K3/22
Inventor 李子荣王和山王厚国王和东殷东楼殷芳荣曹文强张万霞张萍
Owner ANHUI KAILIN ADVANCED MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com