High-temperature high-pressure well cementation additive
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-temperature, high-pressure, additive technology, applied in the direction of drilling compositions, chemical instruments and methods, etc., can solve the problems of fast thickening of cement slurry and affect the normal construction of cementing operations, etc., to reduce the density difference between the upper and lower and prolong the thickening Time, the effect of improving dispersion
Inactive Publication Date: 2019-04-12
BEIJING DADE GUANGYUAN PETROLEUM TECH SERVICE
View PDF4 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
At present, with oil and gas exploration and development gradually extending to the depth of the formation, the corresponding formation temperature gradually increases, and the focus of oil and gas field development gradually shifts to deep wells, ultra-deep wells and other large temperature difference cementing. However, with the increase of temperature in high temperature cementing, the cement Slurry thickens quickly, which seriously affects the normal construction of cementing operations
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] High temperature and high pressure cementing additives, including component A and component B, component A includes the following raw materials in parts by weight: 20 parts of water reducer, 5 parts of hydroxyethylidene diphosphonic acid, 1 part of zeolite powder, and 30 parts of water ;Component B includes the following raw materials in parts by weight: 5 parts of coconut shell powder, 0.5 part of sugarcane powder, 3 parts of sodium carboxymethylcellulose, 2 parts of zinc acrylate, 5 parts of polyvinylpyrrolidone, and 200 parts of water;
[0026] Wherein, the preparation method of coconut shell powder is: pulverize coconut shell, sieve, obtain pulverized material, add the 4M sulfuric acid aqueous solution of its total mass 10 times amount to pulverized material, soak 2h, filter to obtain coconut shell slag, coconut shell slag is obtained. The shell slag is dried in a vacuum drying oven at 120°C to obtain pretreated coconut shell slag, and 10 times the total mass of etha...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle size (mesh)
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
quality score
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a high-temperature high-pressure well cementation additive. The high-temperature high-pressure well cementation additive comprises a component A and a component B, the component A comprises, by weight, 20 parts of a water reducing agent, 5 parts of hydroxyethyl bisphosphonic acid, 1 part of zeolite powder and 30 parts of water, and the component B comprises, by weight, 5 parts of coconut shell powder, 0.5 part of sugarcane powder, 3 parts of sodium carboxymethylcellulose, 2 parts of zinc acrylate, 5 parts of polyvinylpyrrolidone and 200 parts of water. A method for preparing the coconut shell powder comprises the steps that a 4 M sulphuric acid aqueous solution 10 times of the total mass of smashed materials is added to the smashed materials, soaking is carried outfor 2 h, the smashed materials are placed in a vacuum drying box of 120 DEG C to be dried, and pre-treated coconut shell residues are obtained; ethyl alcohol, a titanate coupling agent and potassium hydroxide are added to the pre-treated coconut shell powder, the materials are mixed, recirculation is carried out for 6 h, the materials are placed in the vacuum drying box of 120 DEG C to be dried, smashing is carried out, and the coconut shell powder is obtained. According to the high-temperature high-pressure well cementation additive, by means of the joint action of the component A and the component B, the thickening time of the cement mud is effectively prolonged.
Description
technical field [0001] The invention relates to the technical field of petroleum exploitation. More specifically, the present invention relates to a high temperature and high pressure well cementing additive. Background technique [0002] Cementing engineering is an important link in the drilling and completion process of oil and gas wells. Cement slurry cementing technology refers to injecting cement into the annular space between the well wall and casing, and achieving the sealing effect through cement. The quality of cementing determines the productivity of oil and gas layers and the life of oil and gas wells. At present, with oil and gas exploration and development gradually extending to the depth of the formation, the corresponding formation temperature gradually increases, and the focus of oil and gas field development gradually shifts to deep wells, ultra-deep wells and other large temperature difference cementing. However, with the increase of temperature in high te...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K8/487
CPCC09K8/487
Inventor 孟虎刘亚东孙晓东王良超
Owner BEIJING DADE GUANGYUAN PETROLEUM TECH SERVICE