Compound tin-boron-oxygen-chlorine and tin-boron-oxygen-chlorine non-linear optical crystal as well as preparation method and application
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A nonlinear optics, compound technology, applied in chemical instruments and methods, optics, crystal growth, etc., can solve problems such as difficulty in growing large-sized crystals and low birefringence
Inactive Publication Date: 2019-04-26
XINJIANG TECHN INST OF PHYSICS & CHEM CHINESE ACAD OF SCI
View PDF9 Cites 7 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
As we all know, the currently practical short-wavelength nonlinear optical crystal is the KBe crystal invented by Chinese scientists. 2 BO 3 f 2 (KBBF) crystal, BaB 2 o 4 (BBO) and LiB 3 o 5 (LBO), however, these crystals have defects such as difficulty in growing large-sized crystals and small birefringence, which limit their applications to a certain extent.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0054] Preparation compound:
[0055] According to the reaction formula: 2SnCl 2 +3B 2 o 3 →Sn 2 B 5 o 9 Cl+BCl 3 , the compound Sn was synthesized by solid phase reaction method 2 B 5 o 9 Cl:
[0056] SnCl 2 , B 2 o 3 Mix evenly at a molar ratio of 2:3, put it into a platinum crucible, place it in a muffle furnace, raise the temperature to 450°C under vacuum or an inert atmosphere, and keep the temperature constant for 48 hours to obtain the compound Sn 2 B 5 o 9 Cl polycrystalline powder.
Embodiment 2
[0058] Preparation compound:
[0059] According to the reaction formula: 2SnCl 2 +5H 3 BO 3 →Sn 2 B 5 o 9 Cl+6H 2 O+3HCl, the compound Sn was synthesized by solid phase reaction 2 B 5 o 9 Cl:
[0060] SnCl 2 , H 3 BO 3 Mix evenly at a molar ratio of 2:5, put it into a platinum crucible, place it in a muffle furnace under vacuum or an inert atmosphere, raise the temperature to 450°C, and keep the temperature constant for 24 hours to obtain the compound Sn 2 B 5 o 9 Cl polycrystalline powder.
Embodiment 3
[0062] Preparation compound:
[0063] According to the reaction formula: SnO+SnCl 2 +2B 2 o 3 +H 3 BO 3 →Sn 2 B 5 o 9 Cl+HCl+H 2 O, the compound Sn was synthesized by solid phase reaction 2 B 5 o 9 Cl:
[0064] SnO, SnCl 2 , B 2 o 3 , H 3 BO 3 Mix evenly according to the proportion of the reaction formula in Example 3, put it into a platinum crucible, place it in a muffle furnace, raise the temperature to 450°C under vacuum or an inert atmosphere, and keep the temperature constant for 120 hours to obtain the compound Sn 2 B 5 o 9 Cl polycrystalline powder.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a compound tin-boron-oxygen-chlorine and a tin-boron-oxygen-chlorine non-linear optical crystal as well as a preparation method and application. The compound has a chemical formula Sn2B5O9Cl, has a molecular weight of 470.70, and is prepared by using a solid-phase synthesis method or a vacuum packaging method. The compound of the crystal has a chemical formula Sn2B5O9Cl, hasa molecular weight of 470.70, belongs to an orthorhombic crystal system, has a space group of Pnn2, has cell parameters that a=11.281(3) angstrom, b=11.331(3) angstrom, c=6.5573(19) angstrom, alpha=90 degrees, beta=90 degrees and gamma=90 degrees, and has a unit cell volume of 838.2(4) angstrom<3>; a frequency-doubled effect of the crystal is about 0.5 time of that of KH2PO4(KDP); an ultravioletcut-off edge of the crystal is less than 350nm. The crystal is grown by using a melting method, a high-temperature liquid melting method, a vacuum packaging method, a hydrothermal method or a room-temperature solution method, the crystal is good in chemical stability and can be applied to all-solid-state laser emitters as a short wavelength non-linear optical crystal.
Description
technical field [0001] The invention relates to a compound tin boron oxychloride Sn 2 B 5 o 9 Cl and tin boron oxychloride Sn 2 B 5 o 9 Cl nonlinear optical crystal, its preparation method and application. Background technique [0002] Short-wavelength nonlinear optical crystals can convert near-infrared and visible lasers into short-wavelength lasers by using their frequency conversion properties, and have important application values in medical, communication, scientific research and other fields. As we all know, the currently practical short-wavelength nonlinear optical crystal is the KBe crystal invented by Chinese scientists. 2 BO 3 f 2 (KBBF) crystal, BaB 2 o 4 (BBO) and LiB 3 o 5 (LBO), however, these crystals have defects such as difficulty in growing large-sized crystals and small birefringence, which limit their applications to a certain extent. Therefore, it is of great significance and practical value to prepare and synthesize new short-wavelength ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.