High-strength 1J22 strip and manufacturing method thereof

A 1J22, production method technology, applied in the direction of magnetic materials, electrical components, circuits, etc., can solve the problems of low product life, poor mechanical performance and strength, and achieve the effect of improving mechanical performance, improving mechanical performance and avoiding oxidation

Inactive Publication Date: 2019-05-28
陕西新精特钢研精密合金有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the deficiencies of the prior art, the object of the present invention is to provide a high-strength 1J22 strip and its manufacturing method. The high-strength 1J22 strip adds Nb and Cr to the original composition, and through a special treatment process, it can significantly improve The mechanical properties of the 1J22 strip are improved, so that the high-strength 1J22 alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A high-strength 1J22 strip, specifically made through the following steps:

[0039] (1) Vacuum smelting: put 1J22 raw materials into a vacuum induction furnace for vacuum smelting, add Nb and Cr to the molten steel in vacuum smelting 8 minutes before tapping, so that the molten steel after vacuum smelting contains 47 parts by weight of Co, 1.5 parts by weight of V, 0.03 parts by weight of Nb, 0.01 parts by weight of Cr, and 47.2 parts by weight of Fe;

[0040] Among them, the raw materials of 1J22 are smelted into molten steel in a vacuum induction furnace, and Nb and Cr are added to the molten steel 8 minutes before tapping. It should be noted that the impurities of the 1J22 strip, such as the lower the content of C, Si, Mn, P, S, Ni and Cu, the better, the content of C is less than 0.02 parts by weight, the content of Si is less than 0.02 parts by weight, and the content of Mn is less than 0.02 parts by weight. The content of P is less than 0.02 parts by weight, the ...

Embodiment 2

[0056] A high-strength 1J22 strip, specifically made through the following steps:

[0057] (1) Vacuum smelting: put 1J22 raw materials into a vacuum induction furnace for vacuum smelting, add Nb and Cr to the molten steel in vacuum smelting 15 minutes before tapping, so that the molten steel after vacuum smelting contains 51 parts by weight of Co, 2.5 parts by weight of V, 0.5 parts by weight of Nb, 0.2 parts by weight of Cr, and 50.8 parts by weight of Fe;

[0058] Specifically, the impurities of the 1J22 strip, such as the lower the content of C, Si, Mn, P, S, Ni and Cu, the better, the content of C is less than 0.02 parts by weight, the content of Si is less than 0.02 parts by weight, and the content of Mn is less than 0.02 parts by weight. 0.02 parts by weight, the content of P is less than 0.015 parts by weight, the content of S is less than 0.015 parts by weight, the content of Ni is less than 0.015 parts by weight, and the content of Cu is less than 0.015 parts by weigh...

Embodiment 3

[0074] A high-strength 1J22 strip, specifically made through the following steps:

[0075] (1) Vacuum smelting: put 1J22 raw materials into a vacuum induction furnace for vacuum smelting, add Nb and Cr to the molten steel in vacuum smelting 10 minutes before tapping, so that the molten steel after vacuum smelting contains 50 parts by weight of Co, 2 parts by weight of V, 0.25 parts by weight of Nb, 0.015 parts by weight of Cr, and 48 parts by weight of Fe;

[0076] Specifically, the impurities of the 1J22 strip, such as the lower the content of C, Si, Mn, P, S, Ni and Cu, the better, the content of C is less than 0.02 parts by weight, the content of Si is less than 0.02 parts by weight, and the content of Mn is less than 0.02 parts by weight. 0.02 parts by weight, the content of P is less than 0.015 parts by weight, the content of S is less than 0.015 parts by weight, the content of Ni is less than 0.015 parts by weight, and the content of Cu is less than 0.015 parts by weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Coercive forceaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-strength 1J22 strip and a manufacturing method thereof and belongs to the field of alloy material machining and processing. According to the high-strength 1J22 strip, Nband Cr are added to original components, mechanical properties of the 1J22 strip are promoted significantly with a special processing technology, thus the high-strength 1J22 alloy can meet the requirements that coercive force Hc is smaller than or equal to 110 A/m, tensile strength Rm is larger than 590 MPa, and the yield strength ReL is larger than 360 MPa. The manufacturing method of the 1J22 strip relates to fast cooling, brine ice quenching and other technical points, and the technical problems that after heat treatment is conducted on an existing ferrocobalt 1J22 strip, the material is high in magnetic performance, but mechanical property strength is poor, and product life is short are solved.

Description

technical field [0001] The invention belongs to the field of alloy material processing, and in particular relates to a high-strength 1J22 strip and a manufacturing method thereof. Background technique [0002] Soft magnetic alloy is an important metal soft magnetic material, which has good magnetic properties, its Curie temperature is as high as 980 °C, the saturation magnetic induction at room temperature is as high as 2.4T, and it has high magnetic permeability and low coercive force. Soft magnetic alloys are mainly used in transformers and motors, as well as in the production of diaphragms for telephones, high-speed printers and receiver coils. At the same time, compared with other materials, this alloy can significantly reduce the weight and volume, and has an irreplaceable application status in the fields of aviation and aerospace. The most important application is to make the core component of the aero-generator - the rotor and stator. [0003] However, the mechanica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C19/07C22C38/30C22C38/24C22C38/26C22C38/02C22C38/04C22C38/20C22C38/52C22C38/46C22C38/48C22C38/42C21D8/12C21D1/18C21D1/74C22F1/10C22F1/02C22C30/00C22C30/02H01F1/147
Inventor 王凯
Owner 陕西新精特钢研精密合金有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap