Catalyst carrier for heavy oil hydrogenation treatment and preparation thereof

A heavy oil hydrogenation and catalyst technology, which is applied in the direction of catalyst carrier, catalyst activation/preparation, physical/chemical process catalyst, etc., can solve the problems of low mechanical strength of catalyst and less concentrated pore distribution, and achieve good mechanical strength and pore distribution concentrated effect

Inactive Publication Date: 2003-01-15
CHINA PETROCHEMICAL CORP +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mechanical strength of the catalyst is still low, and the pore distribution is not too concentrated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 230g pseudo-boehmite (dry basis 70%) and 15g alumina powder are mixed with 12.1g carbon black, 1.55g phosphoric acid, 3.6g acetic acid, 7.2g squash powder, 211g clean water to become plastic, and then Extruded into 1.2mm four-leaf clover strips on an extruder, dried at 120°C for 4 hours, and calcined at 850°C for 2 hours to obtain carrier A, whose properties are listed in Table 1.

Embodiment 2

[0023] Mix and knead 230g pseudo-boehmite dry rubber powder and 28.4g alumina powder with 10.1g carbon black, 1.82g phosphoric acid, 4.0g formic acid, 7.6g starch, and 220g clean water to form a plastic body, and then extrude it on the extruder into 1.2mm four-leaf clover strips, dried at 120°C for 4 hours, and calcined at 950°C for 2 hours to obtain carrier B, whose properties are listed in Table 1.

Embodiment 3

[0025] In Example 1, the phosphoric acid was changed to boric acid, the acetic acid was changed to nitric acid, and the turnip powder was changed from 7.2 g to 11.8 g, which is the cost example, and the carrier C was obtained, and its properties are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a heavy oil hydrogenation treatment catalyst carrier and its preparation method. In the course of preparation the pseudo-thin empholite and aluminium oxide are mixed according to a certain proportion,then mixed with compound pore-expanding agent and kneaded to mouldable body, then strip-extruded and formed by means of strip-extruding machine, then dried and roasted at high temp. so as to obtain the required carrier.

Description

technical field [0001] The invention relates to a heavy oil hydrotreating catalyst carrier and a preparation method thereof, in particular to a residue oil hydrodemetallization and hydrodesulfurization catalyst carrier and a preparation method thereof. Background technique [0002] At present, industrial hydrotreating catalysts are usually supported by alumina or alumina containing a small amount of additives, and metal elements of group VIII and group VIB are used as active components. It is well known that the pore structure of the catalyst has an important influence on the performance of the catalyst. Catalysts for heavy oil hydrotreating, especially catalysts used for residual oil hydrotreating, generally need to have larger pore diameter and pore volume to facilitate the internal diffusion of macromolecular reactants in heavy oil and avoid or slow down the The deposition of the catalyst blocks the pores of the catalyst, resulting in a rapid decline in catalyst activity...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J21/04B01J32/00B01J37/04
Inventor 方维平孙素华王纲王永林丁莉
Owner CHINA PETROCHEMICAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap