Cork polyurethane sole material and preparation method thereof

A shoe sole material, polyurethane technology, applied in the field of shoe sole materials, can solve problems such as poor wear resistance, sole cracking, and resistance to hydrolysis, etc., and achieve the effects of reducing production costs, improving compatibility, and low cost

Inactive Publication Date: 2019-07-16
泉州邦尼生物科技有限公司
View PDF20 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for soft polyurethane soles, they have poor wear resistance and are not resistant to hydrolysis, which can easily lead to cracks and breakages on the soles, resulting in certain limitations in the application range of polyurethane soles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of cork polyurethane sole material, comprises each raw material of following weight part:

[0028] Azodicarbonamide 3, sawdust 30, polycarbonate diol 80, isophorone diisocyanate 60, initiator 1, catalyst a0.5, color paste 0.1, trimethylamine 2, elastic dispersion 20.

[0029] Described initiator is dicumyl peroxide.

[0030] Described catalyst a is stannous octoate.

[0031] Described elastic dispersion liquid is made up of the raw material of following parts by weight:

[0032] Waste rubber powder 30, glycidol 3, methyl methacrylate 10, catalyst b0.01, 2-mercaptobenzimidazole 0.7, calcium stearate 2.

[0033] The catalyst b is lithium methylate.

[0034] The preparation method of described elastic dispersion liquid, comprises the following steps:

[0035] (1) Mix 2-mercaptobenzimidazole and calcium stearate, add it to toluene which is 10-18 times the weight of the mixture, and stir evenly to obtain a toluene solution;

[0036] (2) Take waste rubber powder, ...

Embodiment 2

[0045] A kind of cork polyurethane sole material, comprises each raw material of following weight part:

[0046] Azodicarbonamide 4, sawdust 35, polycarbonate diol 100, isophorone diisocyanate 70, initiator 2, catalyst a1, color paste 0.2, trimethylamine 4, elastic dispersion 30.

[0047] Described initiator is dicumyl peroxide.

[0048] Described catalyst a is stannous octoate.

[0049] Described elastic dispersion liquid is made up of the raw material of following parts by weight:

[0050] Waste rubber powder 40, glycidol 5, methyl methacrylate 12, catalyst b0.02, 2-mercaptobenzimidazole 1, calcium stearate 3.

[0051] The catalyst b is lithium methylate.

[0052] The preparation method of described elastic dispersion liquid, comprises the following steps:

[0053] (1) Take 2-mercaptobenzimidazole and calcium stearate and mix them, add them to toluene which is 18 times the weight of the mixture, and stir evenly to obtain a toluene solution;

[0054] (2) Take waste rubbe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cork polyurethane sole material. The sole material comprises the following raw materials in parts by weight: 3-4 parts of azodicarbonamide, 30-35 parts of saw dust, 80-100 parts of polycarbonate diol, 60-70 parts of isophorone diisocyanate, 1-2 parts of an initiator, 0.5-1 part of a catalyst a, 0.1-0.2 part of color paste, 2-4 parts of trimethylamine and 20-30 parts of anelastic dispersion liquid. The sole material disclosed by the invention has very strong impact strength and elongation at break, and is soft in texture, good in wear resistance, low in cost and highin quality.

Description

technical field [0001] The invention belongs to the field of shoe sole materials, and in particular relates to a cork polyurethane shoe sole material and a preparation method thereof. Background technique [0002] Polyurethane is the abbreviation of polyurethane. It is a polymer compound containing many repeated amino groups on the polymer main chain. It is formed by chemical reaction between isocyanate and polyol compound. It is light, comfortable, cold-resistant, and processed Fast and many other advantages, and its physical and mechanical performance indicators can be changed within a certain range through the selection of raw materials and the adjustment of formula, so as to meet the different requirements of users for product performance; [0003] Because of many advantages such as low production cost of polyurethane, it is widely used in the making of shoe soles. However, the soft polyurethane sole has poor wear resistance and is not resistant to hydrolysis, which eas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L97/02C08L51/04C08K5/23C08G18/44C08G18/75C08F289/00C08F220/14C08C19/06A43B13/04
CPCA43B13/04C08C19/06C08F289/00C08G18/44C08G18/755C08L75/04C08L2205/03C08F220/14C08L97/02C08L51/04C08K5/23
Inventor 吕正军王连波秦壮利李宁
Owner 泉州邦尼生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap