Mahua stone imitated enamel decorative plate and preparation method thereof

A technology of twisted stone and decorative boards, which is applied in chemical instruments and methods, laminating devices, and other household appliances, etc., can solve the problems that product quality cannot meet the use requirements, and enamel decorative boards cannot meet application requirements, etc., so as to facilitate industrialization Production, easy to achieve, fine glazed effects

Active Publication Date: 2019-07-19
HANGZHOU FANTASY PORCELAIN PROD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the material and process reasons of the existing enamel decorative board preparation method, the method of decal paper or screen printing is generally used for patterns or patterns. This method is only suitable for planes, and is not suitable for shapes such as corners, inner corners, and grooves. Enamel decorative board, the quality of the prepared product cannot meet the requirements of use
For example, the enamel decorative materials in some application fields and occasions must meet the requirements of anti-collision, sound absorption and imitation stone appearance of enamel decorative panels. The enamel decorative panels obtained by the existing preparation process cannot meet the above application requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mahua stone imitated enamel decorative plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A preparation method of imitation twisted stone enamel decorative plate, comprising the following steps:

[0040] (1) CNC cutting, cutting and folding the special steel plate to be processed into the desired shape

[0041] (2) Carry out degreasing, derusting and secondary neutralization anti-rust treatment on the enamel special steel plate to be treated;

[0042] (3) The special steel plate for enamel after processing in the above-mentioned step (2) is sprayed with an electrostatic dry powder equipment for bottom glaze and top glaze;

[0043] (4) Sinter the enamel special-purpose steel plate sprayed in the above step (3) at 830° C. for 7 minutes. After sintering, the thickness of the bottom glaze and top glaze is 100 μ to obtain a white enamel steel plate substrate;

[0044] (5) The preparation process of the bottom color glaze of twisted stone is;

[0045] A: Take the following raw materials in parts by weight: 100 parts of titanium glaze, 5 parts of clay, 0.1 part o...

Embodiment 2

[0062] A preparation method of imitation twisted stone enamel decorative plate, comprising the following steps:

[0063] (1) CNC cutting, cutting and folding the special steel plate to be processed into the desired shape

[0064] (2) Carry out degreasing, derusting and secondary neutralization anti-rust treatment on the enamel special steel plate to be treated;

[0065] (3) The special steel plate for enamel after processing in the above-mentioned step (2) is sprayed with an electrostatic dry powder equipment for bottom glaze and top glaze;

[0066] (4) Sinter the enamel special steel plate sprayed in the above step (3) at 840° C. for 6 minutes. After sintering, the thickness of the bottom glaze and top glaze is 150 μ to obtain a white enamel steel plate substrate;

[0067] (5) The preparation process of the textured stone base color glaze is:

[0068] A: Take the following raw materials in parts by weight: 100 parts of titanium glaze, 7 parts of clay, 0.3 parts of bentonite...

Embodiment 3

[0085] A preparation method of imitation twisted stone enamel decorative plate, comprising the following steps:

[0086] (1) CNC cutting, cutting and folding the special steel plate to be processed into the desired shape

[0087] (2) Carry out degreasing, derusting and secondary neutralization anti-rust treatment on the enamel special steel plate to be treated;

[0088] (3) The special steel plate for enamel after processing in the above-mentioned step (2) is sprayed with an electrostatic dry powder equipment for bottom glaze and top glaze;

[0089] (4) Sinter the enamel special steel plate sprayed in the above step (3) at 850° C. for 5 minutes. After sintering, the thickness of the bottom glaze and top glaze is 180 μ to obtain a white enamel steel plate substrate;

[0090] (5) The preparation process of the textured stone base color glaze is:

[0091] A: Take the following raw materials in parts by weight: 100 parts of titanium glaze, 8 parts of clay, 0.5 part of bentonite,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a Mahua stone imitated enamel decorative plate. The method comprises the following steps: pre-treating a steel plate special for enamel, spraying groundglaze and surface glaze, conducting sintering, preparing Mahua stone ground color glaze, conducting spraying and sintering, preparing Mahua stone glaze, and conducting spraying and sintering to obtain the product. The Mahua stone ground color glaze and the Mahua stone glaze are sequentially sprayed on an enamel steel plate base plate, the glaze and the base plate are better fused through sintering, the technology is simplified, implementation is easy, and industrial production is facilitated. The invention further provides the Mahua stone imitated enamel decorative plate which is prepared bythe method. The Mahua stone imitated enamel decorative plate has the characteristics of smooth and attractive Mahua glaze layer, fine and smooth glaze surface, wear resistance, corrosion resistance, weather resistance and easiness in cleaning, and can be applied to subway stations, underground passages, tunnels, outer walls and the like as a decorative material.

Description

technical field [0001] The invention relates to the field of enamel building materials, in particular to an imitation twist stone enamel decorative plate and a preparation method thereof. Background technique [0002] The enamel-coated product is also called post-coated product, which is a product that imparts functions such as corrosion resistance, chemical resistance, and weathering resistance by forming an enamel layer on the surface of the substrate, and improves the life of the steel plate. Compared with pre-coated products, enamel-coated products have disadvantages such as high manufacturing cost, but they have excellent quality in terms of hardness, weather resistance, washability, heat resistance and non-combustibility; at the same time, enamel-coated products The product itself also has a high degree of pollution suppression and excellent chemical resistance that can be restored by washing. At present, enamel decorative panels have been widely used in building curt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/00B32B9/04B32B3/12B32B15/01B32B15/20B32B7/12B32B37/12B32B37/10C23D5/02C23D11/00C03C8/20C03C8/16
CPCB32B3/12B32B7/12B32B9/002B32B9/041B32B15/016B32B15/20B32B37/10B32B37/1284B32B2255/06B32B2255/20B32B2255/28B32B2307/554B32B2307/712B32B2307/714B32B2607/02C03C8/16C03C8/20C03C2207/04C23D5/02C23D11/00
Inventor 臧源恒谢向荣楼国龙
Owner HANGZHOU FANTASY PORCELAIN PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com