High-strength anti-cracking foam concrete and preparation method thereof

A foam concrete, high-strength technology, applied in the field of materials, can solve the problems that affect the promotion and application of foam concrete, low strength, water absorption, etc., achieve good crack resistance, reduce surface tension, and improve stability

Active Publication Date: 2019-08-09
CHINA FIRST METALLURGICAL GROUP
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still some defects in foam concrete, such as low strength, cracking, water absorption, etc. These defects affect the promotion and application of foam concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength anti-cracking foam concrete and preparation method thereof
  • High-strength anti-cracking foam concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention. Obviously, the described embodiments are only a part of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative work shall fall within the protection scope of the present invention.

[0022] It should be noted that the embodiments of the present invention and the features in the embodiments can be combined with each other if there is no conflict.

[0023] The present invention will be further described below in conjunction with specific embodiments, but it is not a limitation of the present invention.

[0024] The present invention provides a high-strength anti-cracking foamed concrete, and its preparation method includes the following steps:

[0025]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to high-strength anti-cracking foam concrete and a preparation method thereof. The high-strength anti-cracking foam concrete comprises, by weight, 200-240 parts of cement, 20-45parts of slag powder, 80-120 parts of water, 1-3 parts of a waterproof agent, 1-5 parts of foaming agents, 0.2-0.5 part of a foam stabilizer, 45-70 parts of lightweight aggregate and 0.3-0.8 part of wood fiber. A double foaming method using the physical foaming agent and the chemical foaming agent is utilized, and the wood fiber is also used so that a large quantity of stable closed air holes canbe formed in the foam concrete, convection and radiation effects in the air holes can be weakened, the water absorption rate of the material is reduced, and meanwhile, the heat conductivity coefficient of the high-strength anti-cracking foam concrete is lower. Due to the double foaming method, the properties of the materials such as the cement, the slag powder and the wood fiber can be fully achieved, and the high-strength anti-cracking foam concrete with the strength and crack resistance better than those of conventional foam concrete is obtained.

Description

Technical field [0001] The invention relates to the technical field of materials, in particular to a high-strength anti-cracking foamed concrete and a preparation method thereof. Background technique [0002] With the continuous development of the construction industry, low-carbon energy saving has become a new development direction for modern buildings. Foamed concrete, also known as foamed cement, lightweight concrete, etc., is a new type of building energy-saving material that is waste-friendly, environmentally friendly, energy-saving, low-cost and non-combustible. As a new type of energy-saving and environmentally-friendly building material, foam concrete has begun to be used in the roof insulation of non-load-bearing parts of buildings. Its main advantages are: low density, light weight, heat preservation, sound insulation, earthquake resistance, etc. However, foam concrete still has certain defects, such as low strength, cracking, water absorption, etc. These defects affec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B38/02C04B111/34
CPCC04B28/04C04B2111/343C04B2201/20C04B2201/32C04B2201/50C04B18/08C04B18/142C04B22/145C04B18/141C04B2103/65C04B2103/48C04B18/26C04B24/14C04B22/062C04B38/02C04B24/34C04B22/068
Inventor 滕飞方三陵黄文钢朱雄兵潘旭马翮飞袁凯
Owner CHINA FIRST METALLURGICAL GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap