Alginate fiber non-woven fabric capable of being gelled in water and preparation method and application thereof

A technology of seaweed fiber and non-woven fabric, applied in non-woven fabric, fiber treatment, plant fiber and other directions, can solve the problems of serious adhesion of hydrogel mask, high viscosity of sodium alginate solution, inconvenient processing of non-woven fabric, etc. Achieving the effects of trace water, excellent water retention, and strong equipment versatility

Active Publication Date: 2019-08-09
绍兴蓝海纤维科技有限公司
View PDF10 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Popular facial masks on the market are usually based on spunlace nonwovens, and the publication number is the patent application of CN 108179546 A, a kind of seaweed fiber nonwoven fabric and its production process and application of high-pressure non-aqueous solvent liquid flow for fiber winding In conclusion, the machine used to process non-woven fabrics in this method is inconvenient to process other non-woven fabrics. Second, the ions in the non-aqueous solution will accelerate the oxidation of the surface of the machine, resulting in shortened machine life, and non-woven fabrics can only absorb high moisture. Does not produce gel like traditional face masks
The patent application with the publication number CN 109577003 A, seaweed fiber facial mask base fabric and its preparation method, is that carboxymethyl cellulose fiber and calcium alginate fiber are blended into nonwoven fabric and then put into sodium alginate solution for modification. The fiber can only maintain the fibrous shape in dilute solution, and the sodium alginate solution has a high viscosity, which is not conducive to the modification operation, and the hydrogel mask made by this method has serious adhesion and high brittleness, which is not conducive to mask packaging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) Raw material preparation

[0030] The raw materials of the hydrogel type seaweed fiber nonwoven fabric of the present invention are seaweed fiber of 38mm×1.8dtex, tencel fiber of 38mm×2.0dtex and modal fiber of 38mm×2.0dtex, and the mass ratio thereof is 30:40:30. The prepared fibers are opened, carded, laid, and hydroentangled to form 35g / m 2 of nonwovens.

[0031] (2) Dipping

[0032] The prepared non-woven fabric was immersed in a mixed solution of 5% sodium chloride solution and ethanol with a volume ratio of 50:50 for 30 minutes.

[0033] (3) Washing and drying

[0034] Wash the nonwoven fabric prepared in the previous process in 90% ethanol solution to remove impurities on the fiber surface, and then dry it at 90°C until the moisture content is below 15% to obtain the finished product.

[0035] The finished product is not only suitable for beauty base fabrics such as mask cloth, eye mask cloth, hand mask cloth, lip mask cloth, etc., but also suitable for m...

Embodiment 2

[0037] (1) Raw material preparation

[0038] The raw materials of the hydrogel type seaweed fiber nonwoven fabric of the present invention are seaweed fiber of 38mm×1.8dtex, tencel fiber of 38mm×2.0dtex and modal fiber of 38mm×2.0dtex, and the mass ratio thereof is 50:30:20. The prepared fibers are opened, carded, laid, and hydroentangled to form 35g / m 2 of nonwovens.

[0039] (2) Dipping

[0040] The prepared non-woven fabric was immersed in a mixed solution of 5% sodium chloride solution and ethanol with a volume ratio of 50:50 for 20 minutes.

[0041] (3) Washing and drying

[0042] Wash the nonwoven fabric prepared in the previous process in 90% ethanol solution to remove impurities on the surface of the fiber, and then dry it at 80°C until the moisture content is below 15% to obtain the finished product.

[0043] The finished product is not only suitable for beauty base fabrics such as mask cloth, eye mask cloth, hand mask cloth, lip mask cloth, etc., but also suitabl...

Embodiment 3

[0045] (1) Raw material preparation

[0046] The raw materials of the hydrogel type seaweed fiber nonwoven fabric of the present invention are seaweed fiber of 38mm×1.8dtex, tencel fiber of 38mm×2.0dtex and acetate fiber of 38mm×2.0dtex, and the mass ratio thereof is 30:40:30 . The prepared fibers are opened, carded, laid, and hydroentangled to form 35g / m 2 of nonwovens.

[0047] (2) Dipping

[0048] The prepared non-woven fabric was immersed in a mixed solution of 10% sodium chloride solution and ethanol with a volume ratio of 80:20 for 10 minutes.

[0049] (3) Washing and drying

[0050] Wash the nonwoven fabric prepared in the previous process in 90% ethanol solution to remove impurities on the surface of the fiber, and then dry it at a temperature of 70°C until the moisture content is below 15% to obtain a finished product.

[0051] The finished product is not only suitable for beauty base fabrics such as mask cloth, eye mask cloth, hand mask cloth, lip mask cloth, et...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
water contentaaaaaaaaaa
Login to view more

Abstract

The invention discloses an alginate fiber non-woven fabric capable of being gelled in water and a preparation method and application thereof, and belongs to the technical field of non-woven fabric production. The alginate fiber non-woven fabric is prepared from alginate fibers, skeleton fibers and a modified solvent, wherein the mass ratio of the alginate fibers to the skeleton fibers is (30-80):(20-70). The alginate fiber non-woven fabric capable of being gelled in water is soft in texture and is gelled in water, after the alginate fiber non-woven fabric is applied to the skin, the effects ofmoisturizing and whitening can be achieved. The non-woven fabric changes the situation that a traditional facial mask base cloth only can be used as a medium, and the alginate fiber non-woven fabricis convenient to carry and easy to preserve.

Description

technical field [0001] The invention discloses a hydrogel-type seaweed fiber nonwoven fabric, a preparation method and application thereof, and belongs to the technical field of nonwoven fabric production. Background technique [0002] As a new type of functional fiber, seaweed fiber is a fiber formed by extracting alginic acid from seaweed as a raw material, making a solution with a certain concentration, extruding through a spinneret and undergoing an ion exchange reaction with metal ions in a coagulation bath. Seaweed fiber has good water absorption, biocompatibility, gelation, far-infrared effect, heavy metal adsorption, etc. [0003] As people have higher and higher requirements for the quality of facial masks, the existing facial mask base cloth has a thick texture and poor air permeability due to the addition of a large amount of essence; it also causes waste of resources because it only acts as a medium. Therefore, people are looking for a mask base cloth that can...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D06B3/10D06M13/207D06M13/144D06M11/13D06M101/04D06M101/06D06M101/10
CPCD04H1/4382D06B3/10D06B15/00D06M11/13D06M13/144D06M13/207D06M2101/04D06M2101/06D06M2101/10
Inventor 魏晋陈晗飞盛建村
Owner 绍兴蓝海纤维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap