HRB400E-F coiled reinforced bar fine grain rolling technology method

A HRB400E-F, process method technology, applied in metal rolling, manufacturing tools, metal rolling and other directions, can solve the problems of increased production costs, price increases, and VN alloy demand growth, etc., to achieve strength and toughness improvement and customer satisfaction. The effect of increasing the degree of

Inactive Publication Date: 2019-08-16
盐城市联鑫钢铁有限公司
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Since the implementation of the new national standard GB/T1499.2-2018 in November 2018, HRB400Φ8 coiled snails are strictly prohibited from the production of water-penetrating steel bars, and are produced by VN microalloying process. The demand for VN alloys has increased significantly, the price has i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • HRB400E-F coiled reinforced bar fine grain rolling technology method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] A HRB400E-F disc screw fine-grain rolling process, which includes the following steps:

[0024] The first step is to control the heating temperature of the billet in the heating furnace by means of segmental heating, so that the tapping temperature of the billet is controlled at 1050±20°C, and the temperature difference between the end face and the head and tail is ≤30°C;

[0025] The second step is to increase the water tank after the pre-finishing and finishing mills, control the temperature of the steel billet entering the finish rolling to 900°C, the temperature before entering the laying frame to 810°C, and the temperature of the laying block to 860°C;

[0026] The third step is to increase the phase change cooling rate through air cooling;

[0027] In the fourth step, the speed of the conveying roller table is controlled in sections, the conveying speed of the roller table is gradually increased, and the overlapping position of the wire rod is gradually opened to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of steel rolling, in particular to an HRB400E-F coiled reinforced bar fine grain rolling technology method. The HRB400E-F coiled reinforced bar fine grainrolling technology method comprises the following steps that step 1, the heating temperature of a billet in a heating furnace is controlled by means of sectional heating, so that the tapping temperature of the billet is controlled at 1050+/-20 DEG C, and the temperature difference between the end face and the head and tail is equal to or smaller than 30 DEG C; step 2, water dipping tanks behind passing through pre-finishing rolling and finishing rolling mills are increased to control the temperature of the billet entering into the finishing rolling to 900 DEG C, the temperature before enteringa wire-drawing machine is 810 DEG C, and the temperature of the wire-drawing machine is 860 DEG C; step 3, the phase change cooling rate is increased through air cooling; and step 4, the speed of a conveying roll gang is controlled in sections, the conveying speed of the roll gang is increased gradually, the overlap positions of steel wire rods are pulled out gradually, the stacking density of wire coils is reduced, so that the cooling speed is balanced. According to the HRB400E-F coiled reinforced bar fine grain rolling technology method, the cost is greatly reduced under the premise of meeting the quality.

Description

technical field [0001] The invention relates to the technical field of steel rolling, in particular to a HRB400E-F disc screw fine-grain rolling process. Background technique [0002] Since the implementation of the new national standard GB / T1499.2-2018 in November 2018, HRB400Φ8 coiled snails are strictly prohibited from the production of water-penetrating steel bars, and are produced by VN microalloying process. The demand for VN alloys has increased significantly, the price has increased rapidly, and the production cost has increased significantly. Increase, vanadium nitrogen in steel is controlled at 0.02%-0.03%, 0.35 kg of vanadium nitrogen alloy is added on average per ton of steel, vanadium nitrogen alloy is 500,000 yuan / ton, and the cost of ton steel increases by 175 yuan. Therefore, there is an urgent need to reduce or cancel the use of VN alloys while ensuring quality and meeting the requirements of the new national standard to reduce production costs. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21B1/16B21B37/74B21B37/00B21B45/02
CPCB21B1/16B21B37/00B21B37/74B21B45/0224B21B2201/06
Inventor 谢锦官曾锦刁承民谢碧松赵根社王康
Owner 盐城市联鑫钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap