A kind of bamboo wood fiber wallboard and preparation method thereof

A bamboo and wood fiber and wallboard technology, applied in the field of wallboard, can solve problems such as inconvenience, and achieve the effects of facilitating wetting, improving mechanical properties, and fast curing

Active Publication Date: 2022-04-26
浙江中财管道科技股份有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the coating has high requirements on the environment. The operating environment of the coating must meet certain humidity and temperature conditions, which is conducive to the curing reaction of PUR glue and reaches the adhesive strength specified in the standard, which is inconvenient.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bamboo wood fiber wallboard and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The weight ratio is 75 parts of PVC resin, 75 parts of calcium carbonate powder, 8 parts of bamboo and wood fiber powder, 5 parts of calcium zinc stabilizer, 0.8 parts of AC foaming agent (azodicarbonamide), 5 parts of The foaming regulator, 0.4 parts of stearic acid and 0.6 parts of PE wax are added to the high-speed mixer and mixed with high temperature and heat to 110-130 ℃, and then low temperature and cold mixing to 35-55 ℃ for discharging. Then, the mixed ingredients discharged from the discharge are conveyed to the extruder to complete the extrusion of the base material of the bamboo and wood fiber wallboard. Finally, the extruded substrates were coated with PVC and the finished products were tested for peel strength and bending strength.

Embodiment 2

[0025] The weight ratio is 75 parts of PVC resin, 75 parts of calcium carbonate powder, 8 parts of bamboo fiber powder, 5 parts of calcium zinc stabilizer, 0.8 parts of AC foaming agent, 5 parts of foaming regulator, 0.4 Parts of stearic acid, 0.5 parts of PE wax, 0.5 parts of PEG with a molecular weight of 6000 and 3 parts of AIM resin are added to a high-speed mixer and mixed with high temperature and heat to 110-130°C, and then mixed with low temperature and cold to 35-55°C. material. Then, the mixed ingredients discharged from the discharge are conveyed to the extruder to complete the extrusion of the base material of the bamboo and wood fiber wallboard. Finally, the extruded substrates were coated with PVC and the finished products were tested for peel strength and bending strength.

Embodiment 3

[0027] The weight ratio is 75 parts of PVC resin, 75 parts of calcium carbonate powder, 8 parts of bamboo fiber powder, 5 parts of calcium zinc stabilizer, 0.8 parts of AC foaming agent, 5 parts of foaming regulator, 0.4 Parts of stearic acid, 0.6 parts of PE wax, 0.3 parts of PVA fiber and 2 parts of MBS resin are added to the high-speed mixer to heat and mix at high temperature to 110-130°C, and then cold-mix at low temperature to 35-55°C for discharging. Then, the mixed ingredients discharged from the discharge are conveyed to the extruder to complete the extrusion of the base material of the bamboo and wood fiber wallboard. Finally, the extruded substrates were coated with PVC and the finished products were tested for peel strength and bending strength.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bamboo-wood fiber wallboard and a preparation method thereof. The base material of the bamboo-wood fiber wallboard comprises 75-100 parts by weight of PVC resin, 75-100 parts of calcium carbonate powder, 2-15 parts of Bamboo fiber powder, 5-7 parts of stabilizer, 0.8-1 part of foaming agent, 5-8 parts of foam regulator, 0.4-1 part of stearic acid, 0.5-1 part of PE wax, 0.3 ~1.1 parts of substrate surface hydrophilic modifier and 2~4 parts of acrylate impact modifier, a kind of preparation method of bamboo wood fiber wallboard comprises a) mixing, b) extruding and c) covering membrane. In the present invention, by adding a substrate surface hydrophilic modifier such as polyethylene glycol or polyvinyl alcohol and adding an acrylate impact modifier such as AIM resin or MBS resin, the wallboard substrate and PUR hot-melt adhesive can be improved. Increase the junction strength, broaden the width of processing conditions during lamination, and enhance the mechanical properties of wallboard substrates.

Description

【Technical field】 [0001] The invention relates to the technical field of wallboards, in particular to the technical field of a bamboo-wood fiber wallboard and a preparation method thereof. 【Background technique】 [0002] With the improvement of living standards, people's requirements for the quality of interior decoration materials have gradually increased, and interior decoration materials are constantly being updated. Bamboo and wood fiber integrated wallboard is made of PVC, calcium powder, bamboo and wood fiber and other raw materials after extrusion processing to form a wood-plastic substrate, and then the surface of the substrate is pasted with PUR hot melt adhesive and PVC film, PP film or wall covering. Composite decoration materials. Bamboo and wood fiber integrated wall panels are favored by the majority of owners once they are launched on the market due to their advantages of fast decoration and environmental protection. [0003] PUR (Polyurethane Reactive), Chi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L97/02C08L23/06C08L71/02C08L29/04C08K3/26C08K5/09C08J9/10
CPCC08J9/103C08J2327/06C08J2497/02C08J2471/02C08J2429/04C08J2203/04C08K2003/265C08K5/09
Inventor 丁良玉谢文杰阮超
Owner 浙江中财管道科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap