Ultraviolet-curable laminating adhesive and preparation method thereof
A technology of ultraviolet light and film-coated adhesive, which is applied in the field of film-coated glue, can solve the problems of film-coated glue that it is difficult to take into account the transparency, gloss and adhesiveness at the same time, the drying speed is slow, and the development and application of high-gloss packaging are restricted, so as to achieve excellent high-gloss Packaging effect, quality improvement, excellent transparency effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0049] The present invention also provides a method for preparing any one of the above-mentioned ultraviolet light-curable film-coated adhesives, including the following steps:
[0050] Adding the urethane acrylate oligomer to the mixture of the first ultraviolet light curing monomer and the second ultraviolet light curing body, and stirring to obtain an intermediate;
[0051] The photoinitiator is heated and melted, and then the photoinitiator is added to the intermediate product, stirred and filtered to obtain the UV-curable film-coated adhesive.
[0052] It can be understood that the raw material ratio of the UV-curable film coating adhesive in the above preparation method is the same as that described above.
[0053] At the beginning of preparation, it is necessary to stir and mix the first UV-curable monomer and the second UV-curable monomer to prepare a mixed system of UV-curable monomers, where the stirring speed can be controlled to be 300-500r / min, for example 400r / min. Sub...
Example Embodiment
[0059] Example 1
[0060] The ultraviolet curable film-coated adhesive of this embodiment includes the following raw materials in parts by mass:
[0061] Polyurethane acrylate oligomer (Guangzhou Songda SD867): 20 parts
[0062] The first UV curing monomer (Xingren ACMO): 20 parts
[0063] The second UV curing monomer (Meiyuan M164): 56 parts
[0064] 2,4,6-Trimethylbenzoyl-diphenylphosphorus oxide: 2 parts
[0065] 2-hydroxy-2-methyl-1-phenyl-1-acetone: 2 parts
[0066] Among them, the urethane acrylate oligomer is a bifunctional urethane acrylate oligomer, the viscosity (25°C) is 30000-50000mPa.s, the molecular weight is 3500, the solid content is ≥99%, and the pH is 6-7;
[0067] The glass transition temperature of the first UV curing monomer is 147°C, and the viscosity (25°C) is 5-15mPa.s;
[0068] The glass transition temperature of the second ultraviolet curing monomer is -20°C, and the viscosity (25°C) is 100-150 mPa·s.
[0069] The ultraviolet curable film-coated adhesive of this emb...
Example Embodiment
[0073] Example 2
[0074] The ultraviolet curable film-coated adhesive of this embodiment includes the following raw materials in parts by mass:
[0075] Urethane acrylate oligomer: 25 parts
[0076] The first UV curing monomer (Xingren ACMO): 25 parts
[0077] The second UV curing monomer (Meiyuan M164): 46 parts
[0078] 2,4,6-Trimethylbenzoyl-diphenylphosphorus oxide: 2 parts
[0079] 2-hydroxy-2-methyl-1-phenyl-1-acetone: 2 parts
[0080] The raw material types and preparation method of the UV-curable film-coated adhesive in this embodiment are the same as those in the first embodiment. The UV-curable film-coated adhesive of this embodiment is 2#.
PUM
Property | Measurement | Unit |
---|---|---|
Viscosity | aaaaa | aaaaa |
Glass transition temperature | aaaaa | aaaaa |
Viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap