A kind of ice surface oil resistant anti-slip shoe material and preparation method thereof

An oil-resistant and anti-slip technology, which can be used in shoe soles, footwear, clothing, etc., and can solve problems such as poor mechanical properties

Active Publication Date: 2021-09-10
WENZHOU YIHE SHOE MATERIAL CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The above-mentioned technical scheme mainly adopts high-damping butyl rubber and nitrile rubber to improve the anti-slip effect of the sole, but butyl rubber is difficult to be compatible with other rubbers such as nitrile when it is not chlorinated or brominated. Resulting in poor overall mechanical properties, needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ice surface oil resistant anti-slip shoe material and preparation method thereof
  • A kind of ice surface oil resistant anti-slip shoe material and preparation method thereof
  • A kind of ice surface oil resistant anti-slip shoe material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A kind of oil-resistant anti-slip shoe material on ice, the raw material components are shown in Table 1 in parts by weight. The anti-aging agent adopts anti-aging agent RD, the accelerator A adopts accelerator DTDM, and the accelerator B adopts accelerator MBS. The preparation method of this oil-resistant non-slip shoe material comprises the following steps:

[0049] Step 1, mix the glass fiber and the solution prepared by silane coupling agent SI-69 evenly, dry at 100°C for 3 hours, and obtain the modified glass fiber for use;

[0050] Step 2, mix and stir laurane, anti-aging agent, vulcanization accelerator (that is, accelerator A+accelerator B), carbon disulfide and PEG-4000 evenly to obtain a compounding agent for use;

[0051] Step 3, mix butyl rubber, cis-butadiene rubber, nitrile rubber, solution polystyrene butadiene rubber and carbon nine resin into the banbury mixer, mix and banbury for 5 minutes, then add white smoke and continue to mix and banbury for 3 mi...

Embodiment 2

[0057] The difference from Example 1 is that, in parts by weight, the raw material components are as shown in Table 1. The preparation method of oil-resistant non-slip shoe material comprises the following steps:

[0058] Step 1, mix the glass fiber with the solution prepared by the silane coupling agent SI-69 evenly, and dry it at 120°C for 4 hours to obtain the modified glass fiber for use;

[0059] Step 2, mixing and stirring laurane, anti-aging agent, vulcanization accelerator, carbon disulfide and PEG-4000 evenly to obtain a compounding agent for later use;

[0060] Step 3, butyl rubber, butadiene rubber, nitrile rubber, solution polystyrene butadiene rubber and C9 resin are mixed and put into a banbury mixer for banburying, mixing and banburying for 10 minutes, then adding white smoke to continue mixing and banburying for 5 minutes, When the temperature reaches 125°C, the rubber masterbatch is obtained;

[0061] Step 4, uniformly mixing the rubber masterbatch, modified...

Embodiment 3

[0065] The difference from Example 1 is that, in parts by weight, the raw material components are as shown in Table 1. The preparation method of oil-resistant non-slip shoe material comprises the following steps:

[0066] Step 1. Mix the glass fiber with the solution prepared by silane coupling agent SI-69 evenly, and dry it at 110°C for 3.5 hours to obtain the modified glass fiber for use;

[0067] Step 2, mixing and stirring laurane, anti-aging agent, vulcanization accelerator, carbon disulfide and PEG-4000 evenly to obtain a compounding agent for later use;

[0068] Step 3, mix butyl rubber, cis-butadiene rubber, nitrile rubber, solution polystyrene butadiene rubber and carbon nine resin into the internal mixer for banburying, mix and banbury for 8 minutes, then add white smoke and continue to mix and banbury for 4 minutes, When the temperature reaches 120°C, the rubber masterbatch is obtained;

[0069] Step 4, uniformly mixing the rubber masterbatch, modified glass fiber...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ice-surface oil-resistant anti-skid shoe material and a preparation method thereof, and relates to the technical field of shoe materials. The raw materials include butyl rubber; butadiene rubber; nitrile rubber; dissolved polystyrene butadiene rubber; white smoke; zinc oxide ; Antiaging agent; Plasticizer; Silane coupling agent; Vulcanization accelerator. The shoe material prepared by this formula is integrated with the specific pattern of the outsole, or is pasted on the outsole. The obtained shoe sole has the advantages of oil resistance and anti-skid, good mechanical properties, and no return of fog. Excellent anti-skid performance, suitable for use on ice and snow.

Description

technical field [0001] The invention relates to the technical field of shoe materials, in particular to an oil-resistant and anti-slip shoe material on ice and a preparation method thereof. Background technique [0002] In an environment with thin ice, snow, ice water, and permafrost interfaces, when the soles are in contact with wet and smooth ground or ground with ice attached, ice water will adhere to the surface of the soles to form a water film, making pedestrians walk It is easy to cause slip and fall injuries. Therefore, the requirements for the anti-slip performance of the sole are higher in ice, wet and oily environments, and improving the anti-slip performance is also a key factor for ensuring safety and comfort. [0003] At present, the traditional shoe soles are mainly made of natural rubber and some synthetic rubber. Although they can achieve the basic wear-resistant and anti-skid effects of rubber outsoles, they cannot meet the anti-slip performance of special...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L9/02C08L23/22C08L9/00C08L9/06C08L57/02C08L71/02C08K13/06C08K9/06C08K7/14C08K3/22C08K5/378C08K5/47C08K5/3437A43B13/04
CPCA43B13/04C08K2003/2296C08L9/02C08L2201/08C08L2205/035C08L23/22C08L9/00C08L9/06C08L57/02C08L71/02C08K13/06C08K9/06C08K7/14C08K3/22C08K5/378C08K5/47C08K5/3437
Inventor 黄忠达刘晓清李树和郑元康梁云鸿
Owner WENZHOU YIHE SHOE MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com