Recycled self-compacting concrete and preparation method thereof

A technology of self-compacting concrete and recycled materials, applied in the field of concrete, can solve the problems of environmental secondary pollution, occupation of land resources, waste of natural resources, etc., and achieve the effects of protecting the living environment, solving environmental impacts, and reducing friction

Active Publication Date: 2019-10-22
西安新意达建筑制品有限公司
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional treatment method of waste concrete is mainly to transport it to the suburbs for stacking or landfill, which not only costs a lot of freight, causes secondary pollution to the environment, but also takes up a lot of valuable land resources, and simply discarding it is also extremely harmful to natural resources. big waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Recycled self-compacting concrete and preparation method thereof
  • Recycled self-compacting concrete and preparation method thereof
  • Recycled self-compacting concrete and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1-3

[0042] In the following preparation example, the polypropylene fiber is selected from the polypropylene fiber whose article number is JBX04 sold by Hebei Shenpeng Chemical Co., Ltd., and the epoxy resin is selected from the E-20 epoxy resin sold by Shenzhen Yoshida Chemical Co., Ltd., and the polyacrylamide is selected from Renqiu Shuoda Chemical Co., Ltd. sells polyacrylamide model SD-1200.

preparation example 1

[0043] Preparation Example 1: Heat 5kg of epoxy resin to 140°C, add 10kg of construction waste and 10kg of steel slag powder, mix thoroughly, place in an environment of 40°C for drying, and pulverize into powder, mix the powder with 20kg of iron tailings, 10kg of hollow Mix glass microspheres and 2kg polypropylene fiber evenly, add to 10kg polyacrylamide emulsion, stir evenly, and dry at 45°C; the particle size of iron tailings is 5mm, and the bulk density is 1500kg / m 3 , the apparent density is 2500kg / m 3 , the steel slag powder has an apparent density of 450m after iron removal, crushing, ball milling, and screening 2 / kg steel slag powder, polyacrylamide emulsion is made by mixing polyacrylamide and water with a mass ratio of 1:30, the particle size of hollow glass microspheres is 15μm, and the density is 0.1g / cm 3 , The average particle size of construction waste ≤ 2mm.

[0044] The raw material ratio of recycled material in table 1 preparation example 1-3

[0045]

preparation example 2

[0046] Preparation Example 2: According to the ratio in Table 1, heat 8kg of epoxy resin to 145°C, add 15kg of construction waste and 13kg of steel slag powder, mix thoroughly, place in an environment of 5°C for drying, and pulverize into powder, and mix the powder with 30kg of iron tailings, 13kg of hollow glass microspheres, and 4kg of polypropylene fibers were mixed evenly, added to 13kg of polyacrylamide emulsion, stirred evenly, and dried at 48°C; the particle size of the iron tailings was 8mm, and the bulk density was 1650kg / m 3 , the apparent density is 2800kg / m 3 , the steel slag powder has an apparent density of 500m after iron removal, crushing, ball milling, and screening 2 / kg steel slag powder, polyacrylamide emulsion is made by mixing polyacrylamide and water with a mass ratio of 1:40, the particle size of hollow glass microspheres is 23μm, and the density is 0.1g / cm 3 , The average particle size of construction waste ≤ 2mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses recycled self-compacting concrete and a preparation method thereof. The recycled self-compacting concrete comprises the following components in parts by weight: 220 to 260 parts of cement, 160 to 190 parts of water, 780 to 800 parts of broken stone, 150 to 158 parts of a recycled material, 80 to 85 parts of mineral powder, 10 to 14 parts of an expanding agent, 720 to 750 parts of sand, 3 to 7 parts of a water reducer, 2 to 10 parts of a viscosity modifier and 110 to 117 parts of coal ash; and the recycled material comprises the following components in parts by weight: 20 to 40 parts of iron tailings, 10 to 20 parts of building waste and 20 to 30 parts of steel slag powder. The recycled self-compacting concrete disclosed by the invention has the advantages of high flowing property, filling property and segregation resistance, and the wastes of steel slag and iron tailings are utilized sufficiently.

Description

technical field [0001] The invention relates to the technical field of concrete, more specifically, it relates to a recycled self-compacting concrete and a preparation method thereof. Background technique [0002] Self-compacting concrete (Self-Consolidating Concrete referred to as SCC) refers to the concrete that can flow and compact under its own gravity, even if there are dense steel bars, it can completely fill the formwork, obtain good homogeneity, and do not require additional vibration. The preparation of self-compacting concrete is generally through the selection and matching of admixtures, cementing materials, coarse and fine aggregates, and a reasonable mix ratio design, so that the yield stress of the concrete is reduced enough to be overcome by the shear stress due to its own weight, and the fluidity of the concrete is increased. At the same time, it has enough plastic viscosity to suspend the aggregate in the cement slurry without segregation and bleeding proble...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/02
CPCC04B18/022C04B28/04C04B18/12C04B18/142C04B18/16C04B14/22C04B16/0633C04B24/2652C04B14/02C04B14/06C04B18/08C04B2103/302C04B14/202C04B14/022C04B2103/0068C04B22/066
Inventor 豆伟党国鹏胡咪咪郜园
Owner 西安新意达建筑制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap