Production method of fibers for antibacterial and durable mattress fabric

A mattress and fabric technology, applied in fiber processing, plant fibers, flame-retardant fibers, etc., can solve problems such as poor softness and poor wear resistance, and achieve the effects of avoiding short service life, prolonging service life, and enhancing antibacterial properties.

Inactive Publication Date: 2019-10-22
阜阳皖春家俬有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Glass fiber is an inorganic non-metallic material with excellent performance. It is prepared as a mattress fabric, which has poor softness during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of fibers for antibacterial and durable mattress fabric
  • Production method of fibers for antibacterial and durable mattress fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of antibacterial, the preparation method of durable mattress fabric fiber, comprises the steps:

[0034] (1) Pretreatment of raw bamboo fiber:

[0035] a. drop the raw bamboo fiber into the pulverizer to pulverize, and cross 100 mesh sieves to get the raw bamboo fiber powder for subsequent use after pulverizing;

[0036] b. First put fulvic acid and fulvic acid into a sterile beaker filled with purified water in a weight ratio of 3:1, and keep stirring until the fulvic acid and fulvic acid are completely dissolved. Seal with plastic wrap and place at 0°C After being placed in an environment for 30 minutes, the original bamboo fiber powder obtained in operation a was immersed in the prepared solution in an environment of 0°C, and stirred continuously at a speed of 50 rpm, and ultrasonic treatment of a specific frequency was carried out while stirring, and the stirring treatment After 45 minutes, centrifuge, wash with ice ethanol for 3 times, and dry until the moi...

Embodiment 2

[0056] A kind of antibacterial, the preparation method of durable mattress fabric fiber, comprises the steps:

[0057] (1) Pretreatment of raw bamboo fiber:

[0058] a. drop the raw bamboo fiber into the pulverizer and pulverize, and cross 130 mesh sieves to get the raw bamboo fiber powder for subsequent use after pulverizing;

[0059] b. Put the fulvic acid and fulvic acid into a sterile beaker filled with purified water in sequence according to the weight ratio of 3.5:1.5, and keep stirring until the fulvic acid and fulvic acid are completely dissolved. Seal with plastic wrap and place at 2°C After being placed in an environment for 35 minutes, the raw bamboo fiber powder obtained in operation a was immersed in the prepared solution in an environment of 2°C, and stirred continuously at a speed of 60 rpm, and ultrasonic treatment of a specific frequency was carried out while stirring, and the stirring treatment After 50 minutes, centrifuge, wash with ice ethanol for 4 times,...

Embodiment 3

[0079] A kind of antibacterial, the preparation method of durable mattress fabric fiber, comprises the steps:

[0080] (1) Pretreatment of raw bamboo fiber:

[0081] a. the original bamboo fiber is dropped into the pulverizer and pulverized, and after the pulverization, 160 mesh sieves are used to obtain the original bamboo fiber powder for subsequent use;

[0082] b. First put fulvic acid and fulvic acid into a sterile beaker filled with purified water in a weight ratio of 4:2, and keep stirring until the fulvic acid and fulvic acid are completely dissolved, then seal with plastic wrap and place at 4°C After being placed in the environment for 40 minutes, the raw bamboo fiber powder obtained in operation a was immersed in the prepared solution in an environment of 4°C, and stirred continuously at a speed of 70 rpm, and ultrasonic treatment of a specific frequency was carried out while stirring, and the stirring treatment After 55 minutes, centrifuge, wash with ice ethanol fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method of fibers for antibacterial and durable mattress fabric. The production method includes the steps of firstly, preprocessing original bamboo fibers; secondly, performing ion injection; thirdly, modifying glass fibers; fourthly, blending; fifthly, spinning and setting. The production method has the advantages that the original bamboo fibers and the glass fibers are subjected to special treatment and then blended, the advantages of the two fibers are kept, the defects of the two fibers are overcome, the defects that the original bamboo fibers are shortin service life, and the glass fibers are brittle and poor in wear resistance are overcome, the bacterial resistance, breathability, flame retardance and strength of the fibers for the mattress fabricare enhanced evidently, and the service life of the final product is prolonged.

Description

technical field [0001] The invention belongs to the technical field of mattress processing, and in particular relates to a preparation method of fibers for antibacterial and durable mattress fabrics. Background technique [0002] Bamboo fiber mattresses are made of natural bamboo fibers (i.e. bamboo fibers) extracted from naturally growing bamboos, processed through high-tech, and produced according to the sleeping habits of the human body. Bamboo fiber mattress has antibacterial and deodorizing, anti-mite, anti-ultraviolet, coloring, rebound, drape and wear resistance functions superior to other fibers, fast moisture absorption and release, good air permeability, degradable, flame retardant effect Excellent. [0003] Plant fiber is an extremely abundant renewable resource, and its main components are cellulose, hemicellulose and lignin. In recent years, the use of plant fibers to prepare new functional composite materials has become a research hotspot. Bamboo is a natura...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/00D01F1/10D01F1/07C03B37/10C03C25/007D06M13/184D06M11/72D06M10/02D06M101/06
CPCC03B37/10C03C25/007D01F1/07D01F1/10D01F1/103D01F2/00D06M10/02D06M11/72D06M13/184D06M2101/06D06M2200/30
Inventor 唐金年
Owner 阜阳皖春家俬有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com