Heat generating agent for food heating and preparation method thereof

A technology of exothermic agent and food, applied in the direction of heat exchange materials, chemical instruments and methods, etc., can solve the problems of different package sizes of exothermic agents, slow burning speed of exothermic agents, unusable heating agents, etc., and achieve easy market transportation and The effect of promotion, low manufacturing cost and long-term preservation

Inactive Publication Date: 2019-10-25
上海和志实业有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the existing heating agents have slow burning speed, low heating efficiency, or high local temperature, high material cost, difficult storage, and poor portability. For food heating, non-toxic heating is required, and some heating agents cannot be used. , and the size of the existing heating agent packaging is different, it is not convenient to use quantitatively according to the weight of food

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment 1, according to the following mass proportion preparation exothermic agent:

[0017] Calcium Oxide 45%, Calcium Hydroxide 10%, Copper Oxide 5%, Zinc Oxide 5%, Aluminum 30%, Sodium Carbonate 1%, Sodium Bicarbonate 4%. After adding water, the heating package reaches 90% in about 3 minutes ° and above, the fever lasts for about 15 minutes.

[0018] A preparation method for a heating agent for food heating:

[0019] In the first step, calcium oxide, calcium hydroxide, copper oxide, zinc oxide, aluminum, sodium carbonate and sodium bicarbonate are respectively granulated, and the particle diameter is 0.1mm-0.3mm;

[0020] In the second step, calcium oxide, calcium hydroxide, copper oxide, zinc oxide, aluminum, sodium carbonate, and sodium bicarbonate are quantitatively weighed, and then mixed by a mixer;

[0021] In the third step, after stirring evenly, quantitatively put it into a non-woven bag for sealing;

[0022] In the fourth step, the outside of the non-...

Embodiment 2

[0023] Embodiment 2, formulate exothermic agent according to the following mass proportion:

[0024] Calcium Oxide 40%, Calcium Hydroxide 12%, Copper Oxide 5%, Zinc Oxide 5%, Aluminum 33%, Sodium Carbonate 1%, Sodium Bicarbonate 4%, the time of heating above 90 degrees Celsius after adding water is more than 20 minutes .

[0025] A preparation method for a heating agent for food heating:

[0026] In the first step, calcium oxide, calcium hydroxide, copper oxide, zinc oxide, aluminum, sodium carbonate and sodium bicarbonate are respectively granulated, and the particle size is 0.1mm-0.3mm;

[0027] In the second step, calcium oxide, calcium hydroxide, copper oxide, zinc oxide, aluminum, sodium carbonate and sodium bicarbonate are quantitatively weighed, and then mixed by a mixer;

[0028] In the third step, after stirring evenly, quantitatively put it into a non-woven bag for sealing;

[0029] In the fourth step, the outside of the non-woven bag is wrapped and sealed with pl...

Embodiment 3

[0030] Embodiment 3, formulate exothermic agent according to the following mass proportion:

[0031] Calcium Oxide 55%, Calcium Hydroxide 8%, Copper Oxide 5%, Zinc Oxide 5%, Aluminum 20%, Sodium Carbonate 3%, Sodium Bicarbonate 4%, the time of heating above 90 degrees Celsius after adding water is more than 20 minutes .

[0032] A preparation method for a heating agent for food heating:

[0033] In the first step, calcium oxide, calcium hydroxide, copper oxide, zinc oxide, aluminum, sodium carbonate and sodium bicarbonate are respectively granulated, and the particle size is 0.1mm-0.3mm;

[0034] In the second step, calcium oxide, calcium hydroxide, copper oxide, zinc oxide, aluminum, sodium carbonate and sodium bicarbonate are quantitatively weighed, and then mixed by a mixer;

[0035] In the third step, after stirring evenly, quantitatively put it into a non-woven bag for sealing;

[0036] In the fourth step, the outside of the non-woven bag is wrapped and sealed with pla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a heat generating agent for food heating and a preparation method thereof. The heat generating agent is prepared from calcium oxide, calcium hydroxide, copper oxide, zinc oxide, aluminum, sodium carbonate and sodium bicarbonate, wherein the heat generating agent is prepared from the following components in percentage by weight: 20%-45% of calcium oxide, 1%-10% of calcium hydroxide, 1%-10% of copper oxide, 1%-10% of zinc oxide, 30%-50% of aluminum, 0.1%-10% of sodium carbonate and 5%-19% of sodium bicarbonate. Compared with an existing heat generating agent, the heat generating agent is long in duration time of reaction, non-toxic and harmless, low in price of raw materials, less in dosage and low in manufacturing cost, carrying and quantitative cooking are convenient caused by non-woven bag packaging, and the needs of batch and automated production are further met; since the calcium oxide can easily absorb moisture in air and become the calcium hydroxide, the heat generating agent is not prone to being preserved, under the wrapping of plastic film, long-term preservation is facilitated, so that the heat generating agent is better in stability, and market transportation and popularization are easier; and the heat generating agent is suitable for a wide range of crowds and environment, cooking time is shortened, and cooking conditions are reduced.

Description

technical field [0001] The invention relates to a heating agent and a preparation method thereof, in particular to a heating agent for food heating and a preparation method thereof. Background technique [0002] Exothermic agents usually refer to exothermic agents that use the heat of dissolution or oxidation heat generated by chemical reactions as the heat source to achieve exothermic purposes; exothermic agents are mainly a mixture of aluminum, calcium oxide, copper oxide, and zinc oxide, and often contain Some other add-ons, such as binders and fillers, etc. The rapidity of combustion of the exothermic agent and the heat released during combustion have a decisive influence on its applicability. In addition, its thermal conductivity and melting temperature also affect its applicability; the heating bag (body) made of this heating agent does not require a hot water source compared with the commonly used hot water bag, and the temperature is stable, and you can choose a sui...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K5/18
CPCC09K5/18
Inventor 余弟昌
Owner 上海和志实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap