Production process of double-sided film-coated color steel plate for building

A technology of double-sided lamination and production process, which can be used in layered products, lamination devices, lamination auxiliary operations, etc., can solve the problems of paint residue, benzene pollution, affecting human health, etc. And the effect of improving the temperature difference resistance

Inactive Publication Date: 2019-11-22
SHANDONG JINGHONG INTELLIGENT TECH CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, coatings are mainly used in the double-sided composite materials used in the construction and decoration industries in the market, but the coatings do have the following defects. First, both sides of the product need to be coated with protective coatings before they can be used, and the roller coating process is harmful to the environment and humans. Both cause very serious benzene pollution; second, there are unavoidable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1

[0020] The invention proposes a production process of a double-sided film-coated color steel plate for construction, which comprises the following steps:

[0021] S1: Select the substrate roll material, and the weight of the substrate roll material is greater than 300kg, and carry out preliminary cleaning of the substrate roll material, and then synchronously and evenly roll-coat the weather-resistant and environmentally friendly transparent glue on the front and back sides of the substrate roll material. During the roll coating process, The production line speed is 30 m / min, and it enters the oven after roller coating;

[0022] S2: Then, the front and back surfaces of the substrate coil are heated in an oven, and the heating temperature is 204°C. After passing through the oven, an adhesive layer can be formed on the front and back surfaces of the substrate coil, and the adhesive The thickness of the layer is 4 μm;

[0023] S3: The substrate coil processed...

Example Embodiment

[0028] Example 2

[0029] The invention proposes a production process of a double-sided film-coated color steel plate for construction, which comprises the following steps:

[0030] S1: Select the substrate roll material, and the weight of the substrate roll material is greater than 300kg, and carry out preliminary cleaning of the substrate roll material, and then synchronously and evenly roll-coat the weather-resistant and environmentally friendly transparent glue on the front and back sides of the substrate roll material. During the roll coating process, The production line speed is 33 m / min, and it enters the oven after roller coating;

[0031] S2: Then, the front and back surfaces of the substrate roll are heated in an oven, and the heating temperature is 210° C. After passing through the oven, an adhesive layer can be formed on the front and back surfaces of the substrate roll, and the adhesive The thickness of the layer is 5 μm;

[0032] S3: The substrate coil processe...

Example Embodiment

[0037] Example 3

[0038] The invention proposes a production process of a double-sided film-coated color steel plate for construction, which comprises the following steps:

[0039] S1: Select the substrate roll material, and the weight of the substrate roll material is greater than 300kg, and carry out preliminary cleaning of the substrate roll material, and then synchronously and evenly roll-coat the weather-resistant and environmentally friendly transparent glue on the front and back sides of the substrate roll material. During the roll coating process, The production line speed is 38 m / min, and it enters the oven after roller coating;

[0040] S2: Then, the front and back surfaces of the substrate roll are heated in an oven, and the heating temperature is 220° C. After passing through the oven, an adhesive layer can be formed on the front and back surfaces of the substrate roll, and the adhesive The thickness of the layer is 7 μm;

[0041] S3: The substrate coil processe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production process of a double-sided film-coated color steel plate for a building. The method comprises the following steps: heating the front surface and the back surface ofa substrate coil material through a drying oven, with adhesive layers being formed on the front and back surfaces of the substrate coil material after the substrate coil material passes through the drying oven; coating the front surface of the treated substrate coil material with front film through an upper heat-conducting film-coating steel roller and coating the back surface of the substrate with PET film through a lower film-coating rubber roller, with the upper heat-conducting film-coating steel roller being provided with an oil path heating system inside to allow the surface temperatureof the steel roller to be 90-100 DEG C; and after the double-sided film coating, immediately spraying cold water for a cooling purpose; after spraying, performing extrusion to remove water with a wringing roller, and drying water points on the front surface and the back surface through hot air blowing, with the temperature of the cooled substrate being 25-40 DEG C, and therefore, color film layersoutside the substrate are formed, and PE protective film is attached to the color film layers at room temperature. The aging resistance, damp-heat resistance, acid resistance, alkali resistance and temperature difference resistance of the steel plate provided by the invention are obviously improved.

Description

technical field [0001] The invention relates to the technical field of steel plate preparation, in particular to a production process of a double-sided film-coated color steel plate for construction. Background technique [0002] At present, coatings are mainly used in the double-sided composite materials used in the construction and decoration industries in the market, but the coatings do have the following defects. First, both sides of the product need to be coated with protective coatings before they can be used, and the roller coating process is harmful to the environment and humans. Both cause very serious benzene pollution; the second is that some coatings have unavoidable trace residues, which affect human health. The 3rd, production process is complicated, and energy waste is serious in the production process. Therefore, the double-sided lamination technology is mainly developed in the market to meet the growing demand of the construction and decoration industries, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B37/06B32B37/12B32B37/10B32B37/08B32B38/00B32B38/16
CPCB32B37/06B32B37/08B32B37/10B32B37/1284B32B38/00B32B38/162
Inventor 周国庆时佩涛李雪涛吕伟
Owner SHANDONG JINGHONG INTELLIGENT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap