Aniline trimer modified sulfonate water-based epoxy curing agent and preparation method thereof

A technology of aniline trimer and water-based epoxy, which is applied in the field of polymer materials, can solve the problem that no aniline oligomer anti-corrosion filler or modified material has been developed

Active Publication Date: 2022-02-08
ANHUI UNIVERSITY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies in the prior art, provide a kind of aniline trimer modified sulfonate type water-based epoxy curing agent and preparation method thereof, to solve the problem of not developing aniline oligomer in the prior art as Technical issues with anti-corrosion fillers or modified materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aniline trimer modified sulfonate water-based epoxy curing agent and preparation method thereof
  • Aniline trimer modified sulfonate water-based epoxy curing agent and preparation method thereof
  • Aniline trimer modified sulfonate water-based epoxy curing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Prepare aniline trimer modified sulfonate water-based epoxy curing agent according to the following steps:

[0053] Add 1.73g of p-phenylenediamine sulfate dissolved in 100mL of hydrochloric acid solution (1.0mol / L) into a three-necked flask, cool down to -5°C, add 3.65g of ammonium persulfate and stir evenly, then quickly add 2.98g of aniline solution and keep The temperature of the system is between -5-0°C for 1 hour. After the reaction, the product is filtered and washed with 10% ammonia water and deionized water until the filtrate is neutral, and the solid product is dried to obtain aniline trimer (AT). Until the filtrate is neutral, it is finally placed in a vacuum oven at 50°C for 24 hours to prepare AT for use.

[0054] 94.5g tetraethylenepentamine (TEPA) is added in the there-necked flask, and 2.9g aniline trimer AT (AT accounts for TEPA and AT total mole fraction is 2%) is dissolved in the propylene glycol methyl ether and is added in the TEPA, control At a t...

Embodiment 2

[0066] Prepare aniline trimer modified sulfonate water-based epoxy curing agent according to the following steps:

[0067] Add 4.33g of p-phenylenediamine sulfate dissolved in 150mL of hydrochloric acid solution (1.0mol / L) into a three-necked flask, cool down to -5°C, add 11.52g of ammonium persulfate solution and stir evenly, then quickly add 7.44g of aniline solution, Keep the temperature of the system at -5-0°C and react for 1 hour. After the reaction is over, filter and wash the product with 10% ammonia water and deionized water until the filtrate is neutral, and dry the solid product to obtain aniline trimer body (AT). Until the filtrate is neutral, it is finally placed in a vacuum oven at 50°C for 24 hours to prepare AT for use.

[0068] Add 73.0g of triethylenetetramine (TETA) into the three-necked flask, and weigh 6g of aniline trimer AT (AT accounts for 4% of the total mole fraction of TETA and AT) and dissolve it in propylene glycol methyl ether and add it to TETA, ...

Embodiment 3

[0075] Prepare aniline trimer modified sulfonate water-based epoxy curing agent according to the following steps:

[0076] Add 8.65g of p-phenylenediamine sulfate dissolved in 200mL of hydrochloric acid solution (1.0mol / L) into a three-necked flask, cool down to -5°C, add 21.89g of ammonium persulfate solution and stir evenly, then quickly add 18.6g of aniline solution, Keep the temperature of the system at -5-0°C and react for 1 hour. After the reaction is over, filter and wash the product with 10% ammonia water and deionized water until the filtrate is neutral, and dry the solid product to obtain aniline trimer body (AT). Until the filtrate is neutral, it is finally placed in a vacuum oven at 50°C for 24 hours to prepare AT for use.

[0077] Add 51.5g of diethylenetriamine (DETA) into the three-necked flask, and weigh 12.5g of aniline trimer AT (AT accounts for 8% of the total molar fraction of TETA and AT) and dissolve it in propylene glycol methyl ether and add it to DETA...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
impact strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an aniline trimer-modified sulfonate-type water-based epoxy curing agent and a preparation method thereof, belonging to the field of macromolecular materials. A soluble aniline trimer is prepared by a chemical oxidation method, and then the aniline trimer is used , single epoxy end-capping agent, and fatty amine as raw materials to obtain a single-end mixed product of aniline trimer and aliphatic amine, and then mix the product with sulfamate and then further react with epoxy resin to synthesize aniline trimer. Sulfonate-type water-based epoxy curing agent. The epoxy curing agent is water dispersible and has a low viscosity, so it is storage stable without diluent. The invention has simple process and easy control of the reaction. The epoxy coating film obtained by curing the curing agent has high hardness, strong impact resistance, good gloss, adhesion reaches grade 0, pencil hardness is 2-3H, and is resistant to acid and alkali corrosion. sex is good.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to an aniline trimer modified sulfonate water-based epoxy curing agent and a preparation method thereof. Background technique [0002] Epoxy resin, as a class of thermosetting materials with excellent physical and mechanical properties, electrical insulation, chemical corrosion resistance, and heat resistance, has been widely used in various fields such as construction, chemical industry, transportation, and electronics. Among them, water-based epoxy curing agent, as the key to the actual production and application of water-based epoxy resin, is a research hotspot in recent years. At present, the preparation methods of water-based epoxy curing agents can be divided into cationic and non-ionic. Among them, cationic water-based epoxy curing agents are usually prepared by neutralizing organic acids to form salts, but the presence of excessive organic acids will reduce the film-forming ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G81/00C08G59/64
CPCC08G81/00C08G59/64
Inventor 杨建军曹忠富王思学吴庆云陈春俊周铭张建安吴明元刘久逸
Owner ANHUI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com