Thermal dye sublimation transfer paper coating, thermal dye sublimation transfer paper and preparation method thereof

A transfer paper and thermal sublimation technology, applied in the field of papermaking, can solve the problems that the drying speed, ink transfer rate and pattern clarity are difficult to meet the quality requirements of thermal sublimation transfer paper, so as to improve the ink transfer rate and printing clarity, The effect of accelerating the drying speed

Inactive Publication Date: 2019-11-22
GOLD HUASHENG PAPER SUZHOU IND PARK
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the development of sublimation transfer printing technology, the current sublimation transfer paper has been difficult to meet people's quality requirements for sublimation transfer paper in terms of ink drying speed, ink transfer rate and pattern clarity.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal dye sublimation transfer paper coating, thermal dye sublimation transfer paper and preparation method thereof
  • Thermal dye sublimation transfer paper coating, thermal dye sublimation transfer paper and preparation method thereof
  • Thermal dye sublimation transfer paper coating, thermal dye sublimation transfer paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] see figure 1 , figure 1 It is a schematic flow diagram of an embodiment of the preparation method of the sublimation transfer paper of the present application, and the preparation method includes:

[0032]Step S11: 100 parts by mass of sodium carboxymethylcellulose, 10-30 parts by mass of starch, 10-50 parts by mass of pigment, 1-3 parts by mass of cationic polymer, 0.01-0.05 parts by mass of defoamer, 0.01-2 parts by mass of Mix parts by mass of dispersant, 0.01-3 parts by mass of pH regulator and 0.01-2 parts by mass of bactericide, and disperse evenly to obtain top coating;

[0033] Wherein, starch is ungelatinized starch;

[0034] Step S12: coating a topcoat on the base paper to obtain thermal transfer sublimation paper.

[0035] Wherein, starch is added in the form of dispersion liquid of starch in cold water. It should be pointed out that the "cold water" here is not limited to water with a very low temperature, as long as the temperature can make the starch i...

Embodiment 1

[0041] 100 parts of sodium carboxymethylcellulose (degree of substitution 0.8), 20 parts of ungelatinized tapioca starch, 30 parts of heavy calcium carbonate, 1 part of cationic alkylketene dimer, 0.02 parts of polyethylene glycol, 0.1 part of sodium polyacrylate, 0.05 part of isothiazolinone, and 0.6 part of sodium hydroxide are mixed together according to the order of the formula in Table 1, and after high-speed dispersion, a uniformly dispersed coating is obtained;

[0042] The above coating is 42g / m in gram weight 2 The base paper is coated on one side, and the coating amount is 4g / m 2 ; After the coating is completed, drying treatment is carried out to obtain sublimation transfer paper.

Embodiment 2

[0044] 100 parts of sodium carboxymethylcellulose (degree of substitution 0.8), 20 parts of ungelatinized tapioca starch, 30 parts of heavy calcium carbonate, 2 parts of cationic alkylketene dimer, 0.02 parts of polyethylene glycol, 0.1 part of sodium polyacrylate, 0.05 part of isothiazolinone, and 0.6 part of sodium hydroxide are mixed together according to the order of the formula in Table 1, and after high-speed dispersion, a uniformly dispersed coating is obtained;

[0045] The above coating is 42g / m in gram weight 2 The base paper is coated on one side, and the coating amount is 4g / m 2 ; After the coating is completed, drying treatment is carried out to obtain sublimation transfer paper.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
degree of substitutionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a thermal dye sublimation transfer paper coating, thermal dye sublimation transfer paper and a preparation method thereof, wherein the thermal dye sublimation transfer paper coating comprises sodium carboxymethyl cellulose, starch, a pigment, a cationic polymer and an additive, wherein the starch is non-gelatinized starch. By means of the mode, the water absorption of the thermal dye sublimation transfer paper can be improved, the drying speed of the printing ink paper is increased, and the printing ink transfer rate and the printing definition can be improved.

Description

technical field [0001] The present application relates to the technical field of papermaking, in particular to a thermal sublimation transfer paper coating, a thermal sublimation transfer paper and a preparation method thereof. Background technique [0002] Dye-sublimation transfer printing is to use inkjet printing, offset printing, screen printing, gravure printing and other printing methods to print text, patterns and other graphics that need to be printed on a On the special paper, the paper printed with graphics and text is superimposed on the substrate, and the ink on the sublimation transfer paper becomes gaseous by means of heating and pressure, and combines with the substrate to transfer the graphics and text to the substrate. things. In this process, the paper used for transfer is called sublimation transfer paper. [0003] With the development of sublimation transfer printing technology, the current sublimation transfer paper has been difficult to meet people's ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D21H19/38D21H19/40D21H19/54D21H19/52D21H19/62D21H19/46D21H19/56D21H19/44D21H19/64D21H21/36D21H19/84D21H21/16B41M5/035B41M5/50B41M5/52
CPCB41M5/035B41M5/0355B41M5/502B41M5/5218B41M5/5236D21H19/385D21H19/40D21H19/44D21H19/46D21H19/52D21H19/54D21H19/56D21H19/62D21H19/64D21H19/84D21H21/16D21H21/36D21H27/00
Inventor 丁强李娟周晶
Owner GOLD HUASHENG PAPER SUZHOU IND PARK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com