Water-containing softly-embedded section specimen and manufacturing method thereof

A production method and cross-section technology, which is applied in the field of bioresin embedding cross-sections, can solve the problems of long specimen production cycle, long time, high cost, etc., and achieve the effect of complete shape and structure, easy preservation and use, and strong sense of reality

Active Publication Date: 2019-12-13
HENAN ZHONGBO BIO PLASTINATION TECHN CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, in the above-mentioned production method, acetone is used for dehydration and degreasing, which takes a long time, and the specimen production cycle is long and the cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The water treatment agent of the present embodiment comprises the following components in parts by mass:

[0032] 100 parts of resin, 0.2 part of initiator, 0.3 part of anti-yellowing agent.

[0033] The resin is a waterborne urethane acrylate variety.

[0034] The initiator is 2-methyl-1-[4-(methylthio)phenyl]-2-(4-morpholinyl)-1-propanone.

[0035] The anti-yellowing agent is epoxy resin anti-yellowing agent V76-PUv.

[0036] The soft embedding agent of the present embodiment comprises the following components in parts by mass:

[0037] 100 parts of UV curing resin with flexibility after UV curing, 0.6 parts of photoinitiator, and 0.3 parts of anti-yellowing agent.

[0038] The UV curable resin with flexibility after UV curing is water-based urethane acrylate.

[0039] Anti-yellowing agents include phosphites.

[0040] The hardness of the cured UV curable resin is Shore A60.

[0041] The preparation method of the moisture-containing soft-embedded section specime...

Embodiment 2

[0053] The water treatment agent of the present embodiment comprises the following components in parts by mass:

[0054] 100 parts of resin, 0.6 part of initiator, 0.1 part of anti-yellowing agent.

[0055] The resin is a waterborne epoxy acrylate.

[0056] The initiator is 2-methyl-1-(4-methylthiophenyl)-2-morpholinyl-1-propanone.

[0057] Anti-yellowing agent is ultraviolet absorber UV-196.

[0058] The soft embedding agent of the present embodiment comprises the following components in parts by mass:

[0059] 100 parts of UV curable resin with flexibility after UV curing, 0.5 parts of photoinitiator, and 0.2 parts of anti-yellowing agent.

[0060] The UV curable resin having flexibility after UV curing is polyurethane, and the polyurethane is polyurethane acrylate.

[0061] The anti-yellowing agent includes one or several kinds of phosphorothioate.

[0062] The hardness of the cured UV curable resin is Shore A60.

[0063] The preparation method of the moisture-contain...

Embodiment 3

[0075] The water treatment agent of the present embodiment comprises the following components in parts by mass:

[0076] 100 parts of resin, 0.8 part of initiator, 0.4 part of anti-yellowing agent.

[0077] The resin is one or several types of water-based polyester acrylate.

[0078] The initiator is 2-methyl-1-(4-methylthiophenyl)-2-morpholine-1-propanone (IHT-PI907).

[0079] The anti-yellowing agent is epoxy resin anti-yellowing agent V76-PUv.

[0080] The soft embedding agent of the present embodiment comprises the following components in parts by mass:

[0081] 100 parts of UV curing resin with flexibility after UV curing, 0.2 parts of photoinitiator, and 0.6 parts of anti-yellowing agent.

[0082] The UV curable resin that has flexibility after UV curing is polyester acrylate.

[0083] The anti-yellowing agent includes one or several kinds of phosphorothioate.

[0084] The hardness of the cured UV curable resin is Shore A60.

[0085] The preparation method of the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a water-containing softly-embedded section specimen and a manufacturing method thereof, and belongs to the technical field of biological resin embedded sections. The manufacturing method of the water-containing softly-embedded section specimen comprises the following steps: freezing a biological specimen, sawing the biological specimen to for sheet section specimens, and soaking the section specimens in a water treatment agent for moisture treatment to obtain pretreated section specimens after the soaking is finished; putting the pretreated section specimens to a mold,and pouring a soft embedding agent into the mold at a non-initiation temperature, wherein the soft embedding agent has flexibility after being cured; and performing curing at an initiation temperature after the pouring is finished to obtain the product. The section specimens are soaked in the water to completely lock the water in the section specimens, so the water cannot flow out to influence embedding. The water is locked in the section specimens, so that the original state of biological tissues can be retained, and the state of the biological tissues can be truly reproduced.

Description

technical field [0001] The invention belongs to the technical field of bioresin embedding section, and in particular relates to a water-containing soft embedding section specimen and a preparation method thereof. Background technique [0002] Embedded specimen technology has been applied to the field of bioanatomical specimens for nearly 30 years. Bioplasticized specimens produced by resin technology have the advantages of non-toxic, odorless, long-term storage, convenient use, and long-term storage in the air. [0003] When the existing biological specimens are embedded, they are generally embedded in hard resin, that is, the resin has high hardness and no elasticity after curing. There are also soft embedding techniques. Soft-embedded specimens are not easy to crack, can be stored for a long time and the specimens are relatively clear, and can be bent to multiple additions and directions. The invention patent with application publication number CN109523873A discloses a s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A01N1/00G09B23/36
CPCA01N1/00G09B23/36
Inventor 程明亮赵顺贠跃进吉晓磊王永超张帅斌
Owner HENAN ZHONGBO BIO PLASTINATION TECHN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap