High-toughness wear-resistant cloth

A high-toughness, anti-abrasion technology, applied in textiles and papermaking, etc., can solve the problems of poor toughness, hand feeling, and poor anti-abrasion performance of fabrics, and achieve the effect of improved wear resistance, toughness, and good hand feeling

Inactive Publication Date: 2020-01-10
NANTONG LVBAJIAO TEXTILE PROD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional fabrics have poor abrasion resistance, and some fabrics with good abrasion resistance have poor toughness and hand feeling. Therefore, an improved technology is urgently needed to solve this problem in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] A kind of high-toughness wear-resistant cloth, its preparation method comprises the following steps:

[0024] Step 1: the composite fiber twisted with polyester fiber and half of cotton fiber is used as warp yarn, the composite fiber twisted with polyamide fiber and remaining cotton fiber is used as weft yarn, and the warp yarn and weft yarn are blended and woven to obtain the base fabric;

[0025] Step 2: Mix water-based polyurethane, polyvinyl ester, calcium carbonate, potassium carbonate, ethylene, fatty alcohol polyoxyethylene ether, nano-titanium dioxide, crosslinking agent, and plasticizer in proportion to obtain a wear-resistant coating solution;

[0026] Step 3: Put the base cloth into the wear-resistant coating solution for soaking, and at the same time carry out the suction treatment for 0.5~1h;

[0027] Step 4: Put the base fabric after the suction treatment into a dryer for drying to obtain a high-toughness anti-abrasion fabric.

Embodiment 1

[0029] A high-toughness wear-resistant cloth, including a base cloth and a wear-resistant coating;

[0030] The base fabric is made of 40% polyester fiber, 40% polyamide fiber and 20% cotton fiber;

[0031] The wear-resistant coating is prepared from the following raw materials in parts by mass: 20 parts of water-based polyurethane, 6 parts of polyvinyl ester, 4 parts of calcium carbonate, 2 parts of potassium carbonate, 1 part of ethylene, 3 parts of fatty alcohol polyoxyethylene ether, nano-titanium dioxide 2 parts, 4 parts of crosslinking agent, 2 parts of plasticizer.

[0032] The preparation method of the present embodiment comprises the following steps:

[0033] Step 1: the composite fiber twisted with polyester fiber and half of cotton fiber is used as warp yarn, the composite fiber twisted with polyamide fiber and remaining cotton fiber is used as weft yarn, and the warp yarn and weft yarn are blended and woven to obtain the base fabric;

[0034] Step 2: Mix water-ba...

Embodiment 2

[0039] A high-toughness wear-resistant cloth, including a base cloth and a wear-resistant coating;

[0040] The base fabric is made of 40% polyester fiber, 40% polyamide fiber and 20% cotton fiber;

[0041] The wear-resistant coating is prepared from the following raw materials in parts by mass: 23 parts of water-based polyurethane, 8 parts of polyvinyl ester, 6 parts of calcium carbonate, 3 parts of potassium carbonate, 1 part of ethylene, 4 parts of fatty alcohol polyoxyethylene ether, nano-titanium dioxide 3 parts, 5 parts of crosslinking agent, 3 parts of plasticizer.

[0042] The preparation method of the present embodiment comprises the following steps:

[0043] Step 1: the composite fiber twisted with polyester fiber and half of cotton fiber is used as warp yarn, the composite fiber twisted with polyamide fiber and remaining cotton fiber is used as weft yarn, and the warp yarn and weft yarn are blended and woven to obtain the base fabric;

[0044] Step 2: Mix water-ba...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-toughness wear-resistant cloth, which comprises base cloth and a wear-resistant coating; the base fabric is formed by blending and weaving 35-45% of polyester fibers, 35-45% of polyamide fibers and 10-30% of cotton fibers; the wear-resistant coating is prepared from waterborne polyurethane, polyvinyl ester, calcium carbonate, potassium carbonate, ethylene, fatty alcohol-polyoxyethylene ether, nano titanium dioxide, a crosslinking agent, and a plasticizer; the base fabric is formed by twisting, blending and weaving polyester fibers, polyamide fibers and cotton fibers, soaking with a special wear-resistant coating solution, rolling and sucking, and drying, so that the wear resistance and the toughness are greatly improved as compared with those of traditional fabric, and the base fabric also has good hand feeling.

Description

technical field [0001] The invention relates to the technical field of wear-resistant cloth, in particular to a high-toughness wear-resistant cloth. Background technique [0002] Cloth can be divided into two categories from the weaving method: woven fabric and knitted fabric. From the processing technology, it can be divided into: gray cloth, bleached cloth, dyed cloth, printed cloth, yarn-dyed cloth, mixed process cloth (such as printing on yarn-dyed cloth, composite cloth, flocking cloth, imitation fur cloth) and so on. It can also be divided by raw materials: cotton cloth, chemical fiber cloth, linen, woolen cloth, silk, and blended fabrics, etc. [0003] Traditional fabrics have poor abrasion resistance, and some fabrics with good abrasion resistance have poor toughness and hand feeling. Therefore, an improved technology is urgently needed to solve this problem in the prior art. Contents of the invention [0004] The purpose of the present invention is to provide a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)