Building fireproof heat-insulating inorganic mineral coating and preparation method thereof

A technology of inorganic minerals and coatings, which is applied in the direction of fire-resistant coatings, anti-fouling/underwater coatings, coatings, etc. It can solve the problems of single thermal insulation-related performance thermal insulation coatings and the inability to guarantee the fire protection level of materials, etc., and achieve excellent thermal insulation effects , the thermal insulation effect is remarkable, the effect of reducing the bulk density

Pending Publication Date: 2020-01-21
湖南蓝天豚住工科技有限公司
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, domestic patents such as CN200910061883.6 and CN201010230484.0 are thermal insulation coatings with a single thermal insulation performance, and they all use pure acrylic resin as the film-forming substance, which cannot guarantee the fire protection level of the material to be A-level and non-combustible.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Building fireproof heat-insulating inorganic mineral coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Embodiment 1 of the present invention provides a fire-proof and heat-insulating inorganic mineral coating, which includes deionized water, defoamer, cellulose, multifunctional additives, dispersant, wetting agent, antiseptic and bactericide, propylene glycol, Nano-silica airgel, glass hollow microspheres, ceramic vacuum microspheres, silica sol, silicone acrylic resin and thickener, the weight fraction of each component is, deionized water 275, defoamer 1.5, cellulose 2, more Functional additive 1.5, dispersant 5, wetting agent 2, antiseptic bactericide 2, propylene glycol 20, nano silicon airgel 150, glass hollow microsphere 100, ceramic vacuum microsphere 110, silica sol 300, silicone acrylic resin 25, thickener6.

[0040] Its preparation method is as follows:

[0041] The first step is to add deionized water and stir;

[0042] The second step adds defoamer, cellulose, multifunctional auxiliary agent, dispersant, wetting agent, antiseptic and bactericide and propyle...

Embodiment 2

[0058] Embodiment 2 of the present invention provides a fire-proof and heat-insulating inorganic mineral coating, which includes deionized water, defoamer, cellulose, multifunctional additives, dispersant, wetting agent, antiseptic and bactericide, propylene glycol, Nano-silica airgel, glass hollow microspheres, ceramic vacuum microspheres, silica sol, silicone acrylic resin and thickener, the composition of each component is deionized water 300, defoamer 2, cellulose 1.5, multifunctional additives 2. Dispersant 6, wetting agent 1.5, antiseptic bactericide 2, propylene glycol 14, nano silicon airgel 135, glass hollow microsphere 125, ceramic vacuum microsphere 100, silicone acrylic resin 100, silica sol 280, thickener 6.

[0059] Its preparation method is as follows:

[0060] The first step is to add deionized water and stir;

[0061] The second step adds defoamer, cellulose, multifunctional auxiliary agent, dispersant, wetting agent, antiseptic and bactericide and propylene...

Embodiment 3

[0077] Embodiment 3 of the present invention provides a fire-proof and heat-insulating inorganic mineral coating, the heat-insulating coating includes deionized water, defoamer, cellulose, multifunctional auxiliary agent, dispersant, wetting agent, antiseptic and bactericide, propylene glycol, Nano silica airgel, glass hollow microspheres, ceramic vacuum microspheres, silica sol, silicone acrylic resin and thickener, the weight fraction of each component is: deionized water 280, defoamer 1.5, cellulose 1.5, more Functional additive 1, dispersant 6, wetting agent 1.5, antiseptic bactericide 1, propylene glycol 15, nano silicon airgel 150, glass hollow microspheres 125, ceramic vacuum microspheres 110, silica sol 300, silicone acrylic resin 20, thickener4.

[0078] Its preparation method is as follows:

[0079] The first step is to add deionized water and stir;

[0080] The second step adds defoamer, cellulose, multifunctional auxiliary agent, dispersant, wetting agent, antise...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a fireproof heat-insulating inorganic mineral coating for buildings and a preparation method thereof. The coating is formed by compounding and processing aerogel, hollow microspheres, high-fire-resistance resin, an inorganic cementing material and other auxiliaries. The nano silicon aerogel is the best thermal insulation material at present; the glass hollow micro-beads andthe ceramic vacuum micro-beads also have excellent heat insulation effects, so that by matching the components with aerogel, the thermal insulation performance is improved; meanwhile, the volume weight of the coating is reduced as a filler, the thermal insulation effect is more remarkable, the void ratio of a coating system is guaranteed by blending silica sol and silicone acrylic resin; furthermore, the strength and the fireproof performance of a coating film are also guaranteed. The invention also provides a composite coating using the coating, the thermal insulation putty adopts an inorganic gelling system taking expanded and vitrified micro bubbles as light aggregate, has excellent thermal insulation performance, has superstrong thermal insulation capability, A-grade fireproof capability and high temperature resistance, and well controls the cost.

Description

technical field [0001] The invention relates to the technical field of building thermal insulation coatings, in particular to a building fireproof and thermal insulation inorganic mineral coating and a preparation method thereof. [0002] technical background [0003] In the trend of advocating energy conservation, emission reduction and ecological greenness in today's world, thermal insulation materials are changing from industrial thermal insulation to architectural thermal insulation. The country is vigorously advocating low-carbon energy-saving industries and energy-saving energy industries, so we pay more attention to the research, development, promotion and application of building thermal insulation coatings. [0004] Heat insulation coating is a coating that can play a heat insulation effect on the surface of a building. It can be divided into transparent heat insulation coatings and non-transparent heat insulation coatings according to different application occasions;...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/00C09D133/04C09D5/18C09D5/14C09D7/61C09D5/34
CPCC09D1/00C09D143/04C09D5/18C09D5/14C09D7/61C09D7/70C09D5/34
Inventor 童彬原
Owner 湖南蓝天豚住工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap