Sound insulation type A-grade fireproof polystyrene board and preparation method thereof

A technology of polystyrene board and polystyrene, which is applied in the direction of sustainable manufacturing/processing, chemical industry, climate sustainability, etc., can solve the problems of waste of resources, poor fireproof performance of polystyrene board, limited application range, etc., and achieve Enhanced compressive and tensile strength, good sound insulation effect, and broad market prospects

Inactive Publication Date: 2020-02-11
徐州飞云泡沫制品有限责任公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the poor fire performance of polystyrene board, it will produce deadly poisonous gas when it is burned. It has been banned by the relevant state departments, and glass rock wool is used instead of polystyrene board. Although glass rock wool has heat insulation function and A-level fire protection function , but belongs to high energy consumption, high emission, high pollution industries, waste resources, affect the environment, and can not effectively soundproof, not strong enough, harmful to human health at the same time, the safety factor is poor, the scope of application is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for preparing a sound-insulating type A-class fireproof polystyrene board, comprising the following synthesis steps:

[0026] S1. Raw material mixing: 38 parts of polystyrene raw materials, 38 parts of fumed silica, 1 part of nano-aerogel, 1 part of graphene, 1 part of white high-temperature ceramic glaze, and 5 parts of Eucommia gum, based on the mass fraction. 0.5 parts of antioxidant AW and 3 parts of modified sepiolite for material premixing;

[0027] S2, heating and stirring: put the premixed material obtained in step S1 in a stirring device with electric heating function and heat up to 50°C for stirring, and stir for 10 minutes to fully mix the materials;

[0028] S3. Baking and bonding: Put the evenly stirred mixture in step S into an oven and continue to heat up to 70°C and bake for 20 minutes to make polystyrene powder and Eucommia glue viscous. , white high-temperature ceramic glaze, Eucommia glue, anti-aging agent AW and modified sepiolite are bonde...

Embodiment 2

[0033] A method for preparing a sound-insulating type A-class fireproof polystyrene board, comprising the following synthesis steps:

[0034] S1. Raw material mixing: 50 parts of polystyrene raw materials, 50 parts of fumed silica, 2 parts of nano-aerogel, 2 parts of graphene, 6 parts of white high-temperature ceramic glaze, and 6 parts of Eucommia gum are mixed in proportion by mass fraction. 1 part, 1 part of antioxidant AW and 5 parts of modified sepiolite for material premixing;

[0035] S2, heating and stirring: the premix obtained in step S1 is placed in a stirring device with electric heating function, and the temperature is raised to 60° C. and stirred for 15 minutes, so that the materials are fully mixed;

[0036] S3. Baking and bonding: put the evenly stirred mixture in step S2 in an oven and continue to bake at 80°C for 30 minutes to make the polystyrene powder and Eucommia glue viscous. Fumed silica, nano-airgel, graphene, White high-temperature ceramic glaze, Euc...

Embodiment 3

[0041] A method for preparing a sound-insulating type A-class fireproof polystyrene board, comprising the following synthesis steps:

[0042] S1. Raw material mixing: 55 parts of polystyrene raw material, 52 parts of fumed silica, 6 parts of nano-aerogel, 6 parts of graphene, 15 parts of white high-temperature ceramic glaze, and 16 parts of Eucommia gum, based on the mass fraction. 2 parts, 2 parts of antioxidant AW and 9 parts of modified sepiolite for material premixing;

[0043] S2, heating and stirring: the premixed material obtained in step S1 is placed in a stirring device with electric heating function, and the temperature is raised to 70° C. and stirred for 20 minutes, so that the materials are fully mixed;

[0044] S3. Baking and bonding: put the evenly stirred mixture in step S2 in an oven and continue to bake at 90°C for 40 minutes to make polystyrene powder and Eucommia gum viscous. Fumed silica, nano-airgel, graphene, White high-temperature ceramic glaze, Eucommi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a sound insulation type A-grade fireproof polystyrene board and a preparation method thereof. The sound insulation type A-grade fireproof polystyrene board comprises the following components in parts by mass: 38 to 55 parts of a polystyrene raw material, 38 to 52 parts of fumed silica, 1 to 6 parts of nano-aerogel, 1 to 6 parts of graphene, 1 to 15 parts of white high-temperature ceramic glaze, 5 to 16 parts of gutta-percha, 0.5 to 2 parts of an anti-aging agent AW and 3 to 9 parts of modified sepiolite. Through formula adjustment, the modified polystyrene board which has a heat insulation function, achieves A-grade fire resistance and has an extremely strong sound insulation effect is produced; the compression resistance and tensile strength of the polystyrene board are enhanced, fire safety is improved, and energy conservation and emission reduction are realized; and the sound insulation type A-grade fireproof polystyrene board is low in cost, high in safety coefficient and wide in application range, and has good economic benefits and social benefits.

Description

technical field [0001] The invention relates to the technical field of building boards, in particular to a sound-insulating A-grade fireproof polystyrene board and a preparation method thereof. Background technique [0002] Polystyrene foam board (referred to as polystyrene board) is widely used in construction and packaging fields due to its low price, excellent thermal insulation performance, and easy processing. However, due to the poor fire performance of polystyrene board, it will produce deadly poisonous gas when it is burned. It has been banned by the relevant state departments, and glass rock wool is used instead of polystyrene board. Although glass rock wool has heat insulation function and A-level fire protection function , but belongs to the high energy consumption, high emission, high pollution industry, wastes resources, affects the environment, and cannot effectively soundproof, is not strong enough, damages human health, and has poor safety factor and limited ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L25/06C08L7/00C08K13/06C08K3/36C08K3/04C08K9/06C08K9/02C08K3/34C08K5/3437C08J9/00
CPCC08J9/0028C08J9/0061C08J9/0066C08J9/009C08J9/0095C08J2325/06C08J2407/00C08K3/34C08K3/36C08K5/3437C08K9/02C08K9/06C08K13/06C08K3/042Y02P20/10
Inventor 李金良
Owner 徐州飞云泡沫制品有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products