Aluminum-wood heterogeneous composite engineered wood

A kind of technological wood and heterogeneous technology, applied in the field of technological wood, can solve the problems of lack of research on heterogeneous composite technological wood system, failure to meet aesthetic requirements, low-end technological wood, etc., to improve rigidity, toughness, not easy to crack, and improve water resistance Effect of Adhesive Properties

Active Publication Date: 2020-03-06
DEHUA TB NEW DECORATION MATERIAL CO LTD
View PDF13 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the younger consumers of interior decoration and the continuous improvement of consumption levels and individual needs, the above-mentioned traditional technological wood products can no longer meet the current aesthetic requirements.
[0003] my country's research on technological wood began in Shanghai in the 1980s, and it started relatively late. At present, there is no systematic research on heterogeneous composite technological wood in China, which makes my country's technological wood at the low end of the industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum-wood heterogeneous composite engineered wood
  • Aluminum-wood heterogeneous composite engineered wood
  • Aluminum-wood heterogeneous composite engineered wood

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0080] The preparation method of the prepressed formaldehyde-free soybean protein adhesive comprises the following steps:

[0081] S1, proportioned according to the low-temperature pre-cured pre-pressed soybean protein adhesive formula 1;

[0082] S2, adding the polyamide-based epoxy compound into water, ultrasonicating for 3 minutes, adding 20% ​​soybean meal powder, and emulsifying homogeneously for 15 minutes at 40 MPa to obtain the first mixture;

[0083] S3, adding the remaining soybean meal powder into the first mixture, mixing evenly, adding 40% triazine ring-based high-reactivity multifunctional epoxy compound, and reacting at 40°C for 25 minutes to obtain the second mixture;

[0084] S4, adding the remaining triazine ring-based high-reactivity multifunctional epoxy compound into the second mixture, reacting at 70°C for 8 minutes, and cooling down to room temperature to obtain a pre-pressed formaldehyde-free soybean protein adhesive.

[0085] Prepressed formaldehyde-f...

Embodiment 1

[0156] According to the pattern design requirements, first recombine the 3-layer Ayousi veneer with a water-based API adhesive with a solid content of 54% and a viscosity of 600mPa·s to obtain the first blank layer, and then coat the two layers of the first blank layer on one side The high-elastic polyurethane adhesive with a viscosity of 250mPa·s (the amount of glue applied is 180g / ㎡) is compounded and pressure-bonded with the aluminum plate after the surface lye degreasing and acid solution neutralization to obtain the second base plate layer, and further The second base layer and the Ayousi veneer coated with urea-formaldehyde resin adhesive on both sides were recombined and recombined. The pressing time was 120 hours, the pressure was 0.6MPa, and the health was cured for 40 days. Finally, the Ayousi veneer and aluminum veneer were produced. Heterogeneous composite technology wood. High-elastic polyurethane adhesive is used for aluminum-wood composites, and high-strength ti...

Embodiment 2

[0158] According to the pattern design requirements, first recombine the 4-layer Ayousi veneer with a water-based API adhesive with a solid content of 50% and a viscosity of 550mPa·s to obtain the first blank layer, and then coat the two layers of the first blank layer on one side The high-elastic polyurethane adhesive with a viscosity of 350mPa·s (the amount of glue applied is 150g / ㎡) is compounded and pressure-bonded with the aluminum plate after the surface lye degreasing and the acid solution neutralization treatment to obtain the second base plate layer. The second base layer and the Ayousi veneer coated with urea-formaldehyde resin adhesive on both sides were recombined and recombined. The pressing time was 240 hours, the pressure was 0.8MPa, and the health was cured for 20 days. Finally, the Ayousi veneer and aluminum veneer were produced. Heterogeneous composite technology wood. High-elastic polyurethane adhesive is used for aluminum-wood composites, and high-strength ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to engineered wood, and in particular, relates to aluminum-wood heterogeneous composite engineered wood. The aluminum-wood heterogeneous composite engineered wood sequentially comprises an Ayous veneer layer, more than one group of second blank plate layers and an Ayous veneer layer; the second blank plate layers are each formed by compounding, pressurizing and gluing a firstblank plate layer, an aluminum plate and a second blank plate layer, and the first blank plate layer is formed by recombining more than one Ayous veneer. A preparation method comprises the followingsteps: (1) recombining more than one Ayous veneer by coating a first adhesive to prepare the first blank plate layer; (2) coating the single surface of each of two blank plates A with a second adhesive, and compounding, pressurizing and gluing with a pretreated aluminum plate to obtain the second blank plate layer; (3) compounding, recombining, pressurizing and curing the second blank plate layersand the Ayous veneer coated with a third adhesive, and thus obtaining the aluminum-wood heterogeneous composite engineered wood batten; and (4) slicing. The aluminum-wood heterogeneous composite engineered wood is not prone to cracking and good in stability and has the metallic luster decoration effect.

Description

technical field [0001] The invention relates to a technical wood, in particular to an aluminum-wood heterogeneous composite technical wood. Background technique [0002] With the rapid shrinking of virgin forests in the world, traditional timber exporting countries have raised the export threshold of logs, and my country has also implemented natural forest protection projects. The contradiction between supply and demand of natural precious timber has become increasingly prominent, seriously restricting the construction and decoration, furniture veneer and other industries. healthy growth. Under the above background, scientific and technological wood has developed rapidly. Scientific and technological wood (scientific name: recombined decorative wood) is made of veneer of common tree species as the main raw material, and is manufactured by veneer coloring, lamination, molding and gluing. A wooden decorative material with the texture, pattern, color and other characteristics o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B21/04B32B21/14B32B15/10B32B15/20B32B7/12B32B37/06B32B37/12B32B37/10C09J189/00C09J11/06C09J11/08B27D1/00
CPCB32B21/042B32B21/14B32B15/10B32B15/20B32B7/12B32B37/1284B32B37/06B32B37/10C09J189/00C09J11/06C09J11/08B27D1/00B32B2307/406B32B2307/558B32B2601/00C08L2205/03C08L77/00C08K5/3492C08L25/18C08K5/19C08L53/02C08L33/00C08L25/14
Inventor 卓艳卓凯程明娟杨楠陈凯沈煜燕徐应林吴云刚李国忠
Owner DEHUA TB NEW DECORATION MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap