Preparing process of welding wire suitable for fusion welding of spray-formed ultrahigh-strength aluminum alloy plate

An aluminum alloy plate, spray forming technology, applied in the direction of manufacturing tools, welding equipment, metal processing equipment, etc., can solve the problems of low weld metal strength, low yield rate, etc., to reduce wire breakage during drawing, improve yield rate, small size effect

Inactive Publication Date: 2020-04-28
JIANGSU HAORAN SPRAY FORMING ALLOY
View PDF8 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a welding wire preparation process suitable for fusion welding of spray-formed ultra-high-strength aluminum alloy plates, and to solve the technical problems of low yield and low weld metal strength in the prior art when welding ultra-high-strength aluminum alloy plates with welding wires

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing process of welding wire suitable for fusion welding of spray-formed ultrahigh-strength aluminum alloy plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The technical solutions of the present invention will be clearly and completely described below in conjunction with the accompanying drawings of the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0030] Spray forming technology is developed from the traditional rapid solidification powder metallurgy process. It is a rapid solidification and near net forming material billet technology. Compared with the traditional casting process, spray forming, as a new generation of solidification technology, improves the solidification unit from centimeter level (semi / continuous casting) to micron level, which can greatly increase the solidification rate, and is a disruptive technology for the pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparing process of a welding wire suitable for fusion welding of a spray-formed ultrahigh-strength aluminum alloy plate. The process includes the steps of material preparing, vacuum smelting, powder atomizing, powder screening, ball-milling and powder mixing, vacuum canning, hot isostatic pressing, lathing, hot extruding and the like. The welding wire produced through the method does not need to be homogenized, saves energy and shortens the welding wire production process. Surplus crystal-phase particles in the prepared welding wire are small in size and are evenly dispersed and distributed, drawing breakage of the wire is reduced, the yield of the welding wire is increased, production cost is reduced, the welding performance of the welding wire and the metal strength of a weld joint can be improved, and the welding wire is particularly suitable for fusion welding of the spray-formed ultrahigh-strength aluminum alloy plate.

Description

technical field [0001] The invention relates to the technical field of welding wire production and preparation, in particular to a welding wire preparation process suitable for fusion welding of spray-formed ultra-high-strength aluminum alloy plates. Background technique [0002] Ultra-high-strength aluminum alloy is an Al-Zn-Mg-Cu high-strength aluminum alloy with Zn as the main strengthening element. It has the advantages of low density, good toughness, high specific strength, high specific stiffness, and excellent stress corrosion resistance. Ultra-high strength is the high-strength aluminum alloy with the best comprehensive performance at present, and has been widely used in aerospace, transportation, shipbuilding, nuclear industry and other fields for a long time. Ultra-high-strength aluminum alloy is a typical structural material, and its weldability is an important process performance index of ultra-high-strength aluminum alloy. Its large-scale use is limited due to i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F5/12C22C21/10B22F9/08B22F3/15B22F3/20B23K35/28B23K35/40
CPCC22C21/10B22F5/12B22F9/082B22F3/15B22F3/20B23K35/288B23K35/40B22F2998/10B22F2003/208B22F2009/043
Inventor 周建党胡余生叶庆丰范曦张豪
Owner JIANGSU HAORAN SPRAY FORMING ALLOY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com