C-Bi2O3-CuO-ZnO adsorbing material and preparation method and application thereof

A c-bi2o3-cuo-zno, adsorption material technology, applied in chemical instruments and methods, adsorption water/sewage treatment, water/sludge/sewage treatment, etc. and other problems, to achieve the effect of overcoming uneven heating, good adsorption and removal effect, and no temperature gradient

Active Publication Date: 2020-05-05
HEFEI UNIV
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adsorption and catalytic performance of a single porous activated carbon material is limited, and it cannot exert a good adsorption effect. Due to its unique properties, the composite porous activated carbon material has better adsorption and catalytic performance than a single porous carbon material. focus

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • C-Bi2O3-CuO-ZnO adsorbing material and preparation method and application thereof
  • C-Bi2O3-CuO-ZnO adsorbing material and preparation method and application thereof
  • C-Bi2O3-CuO-ZnO adsorbing material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A C-Bi 2 o 3 -The preparation method of CuO-ZnO adsorption material, comprises the following steps:

[0028] S1, adding bismuth nitrate, copper nitrate, zinc acetate and gac into 50mL concentration is in the dilute nitric acid solution of 0.15mol / L, makes bismuth nitrate, copper nitrate, zinc acetate dissolve, obtains mixed solution;

[0029] S2. Adjust the pH of the mixed solution in step S1 to 5-12 with an ammonia solution to obtain a reaction solution;

[0030] S3. Under stirring and microwave conditions, the reaction solution described in step S2 was hydrothermally reacted at 100°C for 20 minutes. The reaction vessel was the XH-800SP multifunctional microwave hydrothermal parallel synthesizer reactor produced by Beijing Xianghu Technology Co., Ltd., tank The body pressure is 3Mpa; then dry at 150°C for 3h to obtain C-Bi 2 o 3 -CuO-ZnO adsorption material, where the microwave power is 1000W.

[0031] According to the above preparation method, C-Bi 2 o 3 -CuO-Z...

Embodiment 2

[0033] A C-Bi 2 o 3 -The preparation method of CuO-ZnO adsorption material, comprises the following steps:

[0034] S1, adding bismuth nitrate, copper nitrate, zinc acetate and gac into 50mL concentration is in the dilute nitric acid solution of 0.15mol / L, makes bismuth nitrate, copper nitrate, zinc acetate dissolve, obtains mixed solution;

[0035] S2. Adjust the pH of the mixed solution in step S1 to 5-12 with an ammonia solution to obtain a reaction solution;

[0036] S3. Under stirring and microwave conditions, the reaction solution described in step S2 was hydrothermally reacted at 100°C for 20 minutes. The reaction vessel was the XH-800SP multifunctional microwave hydrothermal parallel synthesizer reactor produced by Beijing Xianghu Technology Co., Ltd., tank The body pressure is 3Mpa; then dry at 150°C for 3h to obtain C-Bi 2 o 3 -CuO-ZnO adsorption material, where the microwave power is 1000W.

[0037] According to the above preparation method, C-Bi 2 o 3 -CuO-Z...

Embodiment 3

[0039] A C-Bi 2 o 3 -The preparation method of CuO-ZnO adsorption material, comprises the following steps:

[0040] S1, adding bismuth nitrate, copper nitrate, zinc acetate and gac into 50mL concentration is in the dilute nitric acid solution of 0.15mol / L, makes bismuth nitrate, copper nitrate, zinc acetate dissolve, obtains mixed solution;

[0041] S2. Adjust the pH of the mixed solution in step S1 to 5-12 with an ammonia solution to obtain a reaction solution;

[0042] S3. Under stirring and microwave conditions, the reaction solution described in step S2 was hydrothermally reacted at 100°C for 20 minutes. The reaction vessel was the XH-800SP multifunctional microwave hydrothermal parallel synthesizer reactor produced by Beijing Xianghu Technology Co., Ltd., tank The body pressure is 3Mpa; then dry at 150°C for 3h to obtain C-Bi 2 o 3 -CuO-ZnO adsorption material, where the microwave power is 1000W.

[0043] According to the above preparation method, C-Bi 2 o 3 -CuO-Z...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a C-Bi2O3-CuO-ZnO adsorbing material and a preparation method and application thereof. The preparation method comprises the following steps of S1, adding copper salt, bismuth salt, zinc salt and activated carbon into a dilute nitric acid solution, dissolving the copper salt, the bismuth salt and the zinc salt, and obtaining a mixed solution; S2, adjusting the pH value of the mixed solution obtained in the step S1 to 5-12 to obtain a reaction solution; and S3, carrying out hydrothermal reaction on the reaction solution obtained in the step S2 under the conditions of stirring and microwaves to obtain the C-Bi2O3-CuO-ZnO adsorbing material. The C-Bi2O3-CuO-ZnO adsorbing material provided by the invention has a good adsorption and removal effect on heavy metal ions, andcan be applied to environmental treatment of industrial sewage and wastewater containing heavy metals.

Description

technical field [0001] The invention relates to the technical field of adsorption materials, in particular to a C-Bi 2 o 3 -CuO-ZnO adsorption material and its preparation method and application. Background technique [0002] Porous activated carbon material has a unique skeleton structure, high surface area, directional pore distribution, and high chemical stability. It is a pollution-free and environmentally friendly adsorbent material. and other fields have been widely used. However, the adsorption and catalytic performance of a single porous activated carbon material is limited, and it cannot exert a good adsorption effect. Due to its unique properties, the composite porous activated carbon material has better adsorption and catalytic performance than a single porous carbon material. focus. [0003] With the development of industry, wastewater containing heavy metals has become a major problem for people. Heavy metals have significant toxicity to humans, animals and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/20B01J20/28B01J20/30C02F1/28C02F101/20C02F101/22
CPCB01J20/06B01J20/20B01J20/28019B01J20/28033C02F1/288C02F2101/20C02F2101/22
Inventor 阳杰姚李胡坤宏司靖宇陆井李东范苏皖陈新宇
Owner HEFEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap