Preparation method of anti-mildew and anti-corrosion fabric

A fabric and anti-mildew technology, applied in the manufacture of rayon, conjugated rayon, chemical characteristics of fibers, etc., can solve the problems of high cost, poor anti-mildew and anti-corrosion effect, complex production process, etc. Anti-corrosion effect, the effect of simple production process

Inactive Publication Date: 2020-05-05
宁波太平鸟潮服饰营销有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problems of poor anti-mildew and anti-corrosion effect, complex production process and high cost in the prior art, and propose a method for preparing anti-mildew and anti-corrosion fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing an anti-mold and anti-corrosion fabric, mainly comprising the following steps: S1, preparing modified anti-mold fiber; mainly including the following steps: the first step, preparing a modified anti-mold fiber raw material, the raw material includes 40 parts of kapok fiber, carbonized cotton 20 parts of fiber, 5 parts of bamboo fiber, 10 parts of water, 20 parts of chitosan polysaccharide, 2 parts of eucalyptus oil, 2 parts of agar oligosaccharide, 0.5 part of perilla, 1 part of licorice, 3 parts of brocade , 5 parts of starch, 1 part of aloe vera oil, 0.5 part of dispersant, pulverize kapok fiber, carbonized cotton fiber, bamboo fiber, perilla, licorice and S. , chitosan polysaccharides, agar oligosaccharides and starch are poured into a stirring container for stirring, the stirring time is 1h, the rotating speed is 800 rpm, and the modified powder is obtained by spray drying; the third step is to mix the fiber particles, Modified powder, Chinese...

Embodiment 2

[0022] A method for preparing an anti-mold and anti-corrosion fabric, mainly comprising the following steps: S1, preparing modified anti-mold fiber; mainly including the following steps: the first step, preparing raw materials for modified anti-mold fibers, the raw materials include 55 parts of kapok fiber, carbonized cotton 35 parts of fiber, 10 parts of bamboo fiber, 15 parts of water, 25 parts of chitosan polysaccharide, 5 parts of eucalyptus oil, 4 parts of agar oligosaccharide, 2 parts of perilla, 3 parts of licorice, 6 parts of brocade brocade , 8 parts of starch, 3 parts of aloe vera oil, 2.5 parts of dispersant, pulverize kapok fiber, carbonized cotton fiber, bamboo fiber, perilla, licorice and S. , chitosan polysaccharides, agar oligosaccharides and starch are poured into a stirring container for stirring, the stirring time is 2 hours, the rotating speed is 1000 rpm, and the modified powder is obtained by spray drying; the third step is to mix the fiber particles, The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of fabric, in particular to a preparation method of anti-mildew and anti-corrosion fabric. The preparation method mainly comprises the steps of S1, preparing modified anti-mildew fibers; S2, weaving the modified anti-mildew fibers into modified fabric; S3, pretreating the modified fabric; S4, preparing an anti-corrosion solution; S5, coating the surfaceof the pretreated modified fabric with the anti-corrosion solution; and S6, drying and shaping the modified fabric coated with the anti-corrosion solution to obtain the anti-corrosion and anti-corrosion fabric. A fabric base body is made of the modified anti-mildew fibers prepared from natural antibacterial materials, so that the fabric has sterilization, mildew prevention and bacteriostasis performances, the health care effect of the fabric is achieved, the softness, moisture permeability and comfort of the fabric base body are improved, the fabric base body is coated with the anti-corrosionsolution, the service life of the fabric is prolonged, and the fabric has high acid and alkali resistance, worm damage resistance and weather resistance, the anti-corrosion effect is improved, and the fabric is suitable for wide popularization.

Description

technical field [0001] The invention relates to the technical field of fabrics, in particular to a method for preparing mildew-resistant and anti-corrosion fabrics. Background technique [0002] As a necessity of life, home textile products not only bring physical comfort to people through its softness, but also affect people's emotional and physical activities through their styles and cultural connotations. With the improvement of people's consumption level 1. Changes in consumption awareness concepts. Fashionable home textile consumption concepts have been implanted into consumers' home textile product consumption concepts. Personalized and fashionable products are becoming more and more popular. Various cross-border popular cultures and increasingly mature new Elements have been successfully added to the R&D and design of home textile products; [0003] Antibacterial fabric has a good antibacterial effect, can eliminate the peculiar smell caused by bacteria, keep the fab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D01F1/10D01F8/02D01F8/18
CPCD01F1/103D01F8/02D01F8/18D06N3/00D06N3/0006D06N3/0015D06N2201/10D06N2209/143D06N2209/1671D06N2209/1692
Inventor 申亚欣窦倩王冻洋邵新平
Owner 宁波太平鸟潮服饰营销有限公司